Effect of particle size on surface roughness and morphology of heat-treated electroless Ni-YSZ coating

Bahiyah Baba N., Ghazali A. S., Azinee S. N., Abdul Rahman A. H., Sharif S.

Journal of Achievements in Materials and Manufacturing Engineering

2022

Vol. 114, nr 1

5--14

Purpose: The paper discusses the surface characterisation of electroless nickel-yttria-stabilised zirconia (Ni-YSZ) coating with varying YSZ particle sizes and undergoes heat treatment at a temperature between 300-400°C for 1-2 hours for wear resistance purposes. This finding will be helpful to the application of Ni-YSZ as an alternative coating for cutting tools. Design/methodology/approach: The surface characterisation was analysed using JOEL Scanning Electron Microscope (SEM) coupled with Energy Dispersive X-ray (EDX) JSM 7800F. The crystallographic structure of materials was analysed by X-ray diffraction (XRD) Bruker D8 Advance instrument. The Ni-YSZ coating was deposited using electroless nickel co-deposition of 8YSZ ceramic particles with a nano, mixed and microparticle sizes onto a high-speed steel (HSS) substrate. The coatings were heat treated at temperature 300-400°C and time 1-2 hours. The surface roughness was measured using Mitutoyo surface roughness tester SJ-301. Findings: The electroless Ni-YSZ coating deposited has an average thickness of 30 μm. It is found that the coating morphology electroless coating without YSZ particle incorporation (EN) and Ni-YSZ nano (N) is smoother compared to the Ni-YSZ mixed (NM) and Ni-YSZ micro (M). The EDS composition analysis shows the YSZ content in the electroless Ni-YSZ coating for N samples is the lowest, whereas NM samples are the highest. This resulted in the surface roughness behaviour where the mixed-size YSZ particle gives the highest roughness at all temperatures. The XRD analysis shows that heating temperatures above 300°C caused the precipitation of Ni3P crystalline. Research limitations/implications: Previous studies in the surface characterisation of electroless nickel composite are scarce; thus, the study has limitations in finding supporting data. Originality/value: The surface characterisation especially related to the surface roughness of the electroless nickel, either the Ni-P or composites or alloys are rarely reported. Thus, this study enlightened the effect of particle size on surface roughness and morphology of heat-treated coatings.

Corrosion Resistance Of Electroless Ni-P/Cu/Ni-P Multilayer Coatings

Zhao G. L., Zou Y., Hao Y. L., Zou Z. D.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2A

1003--1008

Ni-P/Cu/Ni-P multilayer coatings were prepared by deposition of Cu layer between two Ni–P layers. The Cu layer was deposited by metal displacement reaction between Cu2+ and Fe atoms. Corrosion behavior of single-layer Ni-P coatings, double-layer Ni-P/Cu coatings, and three-layer Ni-P/Cu/Ni-P coatings were investigated by electrochemical tests in 3.5% NaCl solution. The three-layer coatings exhibited more positive Ecorr and decreased Icorr compared with conventional single-layer Ni-P coatings, which indicated an improved corrosion resistance. The polarization curves of the three-layer coatings were characterized by two passive regions. The improved corrosion resistance was not only attributed to the function of the blocked pores of Cu. The Cu interlayer also acted as a sacrificial layer instead of a barrier in the coatings, which altered the corrosion mechanism and further improved the corrosion resistance of the coatings.

Wielowarstwowe powłoki Ni-P/Cu/Ni-P wytworzono metodą osadzania miedzi pomiędzy dwoma warstwami Ni-P. Warstwę Cu otrzymano dzięki reakcji wypierania metalu przez metal (dla miedzi i żelaza). Aby określić właściwości korozyjne jednowarstwowej powłoki Ni-P, dwuwarstwowej Ni-P/Cu oraz trójwarstwowej Ni-P/Cu/Ni-P przeprowadzono pomiary elektrochemiczne w 3,5% roztworze NaCl. Powłoki trójwarstwowe w porównaniu do jednowarstwowych wykazały się większą wartością Ecorr, przy malejącej wartości Icorr. Wskazuje to na poprawę odporności na korozję. Krzywe polaryzacji dla powłok trójwarstwowych charakteryzują się występowaniem dwóch obszarów pasywacji. Poprawa odporności na korozję jest skutkiem nie tylko tzw. zjawiska blokowania porów w miedzi. Powłoka z Cu działała także jako warstwa protektorowa, modyfikując mechanizm korozji i poprawiając odporność korozyjną powłok.