The role of ECAP in densification behaviour of PM aluminium alloy

Bidulska J., Kocisko R., Kovacova A., Dutkiewicz J.

Inżynieria Materiałowa

2011

Vol. 32, nr 2

82-85

The present paper focused on the role of ECAP process on the densification behaviour of PM aluminium alloys. An aluminium powder Al-Mg- Si-Cu-Fe was used as material to be investigated. After applying different compacting pressures in the range of 400 to 700 MPa, specimens were dewaxed at 400°C for 60 min. Sintering was carried out in a vacuum furnace at 610°C for 30 min. The specimens were ECAPed for 1 pass. Structural characterization was carried out on the minimum of 10 different image fields for pressed and sintered specimens as well ECAPed specimens. A decrease of porosity was revealed for all specimens.

Praca dotyczy zastosowania technologii przeciskania przez kanał kątowy ECAP dla zagęszczania proszków stopów aluminium. Badano proszek stopu aluminium Al-Mg-Si-Cu-Fe. Po zastosowaniu prasowania przy różnych ciśnieniach od 400÷700 MPa, próbki oczyszczano z substancji organicznych przez wyżarzanie w 400°C przez 60 min. Następnie próbki spiekano w temperaturze 610°C przez 30 min. Następnie poddano je przeciskaniu w kanale ECAP. Porównano struktury próbek spiekanych i przeciskanych w kilku miejscach i stwierdzono znaczny spadek porowatości.