Influence of plasma spraying conditions on the microstructure and functional properties of WC-Cr-Ni metaloceramic layers

Kubaszek Tadeusz, Góral Marek, Różański Radosław, Szczepański Łukasz

Journal of Metallic Materials

|

2019

|

Vol. 71, no. 2

3--7

EN

The article presents the results of research on the impact of the conditions of plasma spraying on thickness and porosity, as well as the erosion resistance of WC-Cr-Ni metaloceramic coatings. It was shown that the selection of current intensity - 450 A and flow rate H2 = 5 dm3 /min and Ar = 68 dm3 /min allows obtaining a coating with a thickness of approx. 177 μm and low porosity < 6%. At the same time, this coating is characterised by the greatest hardness - 758 HV0.5, and the best erosion resistance at room and elevated temperature. The analysis of test results indicates that lower current and hydrogen content in the plasma stream do not ensure sufficient melting of the metallic matrix of the powder - Ni and Cr, and thus greater brittleness of the coating and its lower erosion resistance. It was also found that an increase in plasma stream energy due to an increase in torch current or hydrogen flow rate may cause tungsten carbide to decompose in the plasma stream - the phase affecting hardness and abrasion resistance.

PL

W artykule przedstawiono wyniki badań wpływu warunków natryskiwania plazmowego na grubość i porowatość, a także odporność erozyjną powłok metaloceramicznych typu WC-Cr-Ni. Wykazano, że dobór natężenia prądu - 450 A oraz natężenia przepływu H2 = 5 dm3 /min i Ar = 68 dm3 /min, umożliwia uzyskanie powłoki o grubości ok. 177 μm i małej porowatości < 6%. Jednocześnie powłoka ta charakteryzuje się największą twardością - 758 HV0.5, i najlepszą odpornością erozyjną w temperaturze pokojowej oraz podwyższonej. Analiza wyników badań wskazuje, że mniejsze natężenie prądu i zawartość wodoru w strumieniu plazmy nie zapewnia wystarczającego stopienia metalicznej osnowy proszku - Ni i Cr, a przez to większą kruchością powłoki i jej mniejszą odpornością erozyjną. Ustalono również, że zwiększenie energii strumienia plazmy na skutek wzrostu natężenia prądu palnika lub natężenia przepływu wodoru może powodować rozkład węglika wolframu w strumieniu plazmy - fazy decydującej o twardości i odporności na ścieranie.

2

Właściwości powłok metaloceramicznych stosowanych na elementy sprężarki silnika lotniczego

Mendala B., Swadźba L.

Ochrona przed Korozją

|

2011

|

nr 4-5

136-141

PL

W artykule przedstawiono wyniki badań przeprowadzonych dla metaloceramicznych powłok antykorozyjnych wytwarzanych z zawiesin nieorganicznych zawierających drobny proszek aluminium. Do badań wybrano zawiesinę wodorozcieńczalną, o obniżonej zawartości chromu sześciowartościowego. Właściwości wykonanych powłok zbadano na próbkach ze stali 10 oraz łopatkach sprężarki silnika lotniczego wykonanych ze stali martenzytycznej typu EI961. Dokonano oceny wyglądu wytworzonych powłok oraz zbadano ich grubość. Określono wpływ obróbek wykańczających na strukturę i właściwości wytworzonych powłok ochronnych. Przeprowadzono badania elastyczności powłok i oceniono ich adhezję do stalowego podłoża. Zbadano odporność powłok na uderzenia drobnymi kamieniami oraz ich odporność korozyjną w obojętnej mgle solnej. Stwierdzono bardzo dobre właściwości antykorozyjne badanych powłok oraz ich zdolności do protektorowania stalowego podłoża.

EN

In this paper the results of investigation of corrosion resistant metallo-ceramic inorganic slurry coatings, contained super fine powder of aluminium have been presented. The research were conducted with using water diluted slurry, with lowered content of hexavalent chromium. The properties of the coatings produced on the samples made of 10 steel and the compressor blades of aircraft engine made of martensitic EI961 steel were determined. View of obtained coatings was described and their thickness were measured. The influence of coatings treatment on their microstructure and properties were described. The bend test of coatings was made and their adhesion to steel was determined. The resistance to impact by small stones as well as corrosion resistance in neutral salt spray were tested. The very good corrosion resistant properties of the metallo-ceramic coatings and their ability to protection of steel were found.

3

Metaloceramiczne powłoki ochronne na wybranych elementach silników lotniczych

Mendala B., Swadźba L., Hetmańczyk M.

Ochrona przed Korozją

|

2008

|

nr 4-5

166-170

PL

W artykule przedstawiono wyniki badań metaloceramicznych powłok antykorozyjnych otrzymywanych z wodorozcieńczalnych zawiesin nieorganicznych. Badania prowadzono na próbkach ze stali 10 oraz łopatkach sprężarki silnika lotniczego ze stali martenzytycznej typu EI961. Powłoki wytwarzano przy zastosowaniu zawiesiny typu Ceral 114, o obniżonej zawartości Cr+6. Dokonano oceny wyglądu wytworzonych powłok oraz zbadano ich grubość i strukturę. Przeprowadzono badania oporności elektrycznej, chropowatości oraz adhezji powłok metaloceramicznych poddanych obróbce wykańczającej. Zbadano odporność korozyjną powłok w obojętnej mgle solnej. Stwierdzono bardzo dobre właściwości antykorozyjne badanych powłok oraz ich zdolności do ochrony protektorowe stalowego podłoża.

EN

This paper presents results of investigation of corrosion resistant metallo-ceramic inorganic slurry coatings. Samples of steel type 10 and compressor blade of aircraft engine made of martensitic EI961 steel were tested. Coatings were deposited using Ceral 114 slurry, with lowered content of Cr+6. Appearance of obtained coatings was evaluated and their thickness and structure were determined. Tests of electrical resistance, roughness and adhesion to steel of coatings subjected to finishing were made. Corrosion resistance of coatings was investigated in neutral salt spray conditions. Very good anticorrosive properties of metallo-ceramic coatings and their ability of sacrificial protection of steel were found.