Failure modes of coatings on steel substrate

Mróz K. P., Kucharski S., Doliński K., Bigos A., Mikułowski G., Beltowska-Lehman E., Nolbrzak P.

Bulletin of the Polish Academy of Sciences. Technical Sciences

2016

Vol. 64, nr 1

249--256

The critical monotonic strain of Ni-W and MoS2(Ti,W) coatings on steel substrates was studied. The idea of axisymmetric bending test (called here as coin bending test) limited to monitoring of the coating failure was used. Experiments revealed mechanism of the coating failure, as cracking initiated from coating surface defects and/or substrate was demonstrated using indentation technique. By pushing the center of the uncoated side of a circular plate, the axisymmetric stress state was generated in the coating. The stress components varied gradually from the greatest value in the center to the smallest value at the edge of the specimen. The changes of the sample surface as a result of loading were monitored step by step via optical microscopy.

Wpływ obróbki cieplnej na odporność korozyjną elektrolitycznych powłok Ni-W

Łosiewicz B., Popczyk M.

Ochrona przed Korozją

2012

nr 3

128-131

W pracy przedstawiono wyniki badań dotyczących oceny odporności korozyjnej powłok Ni-W, elektroosadzanych na podłożu ze stali węglowej metodą galwanostatyczną, przed i po obróbce cieplnej w powietrzu w temp. 900°C. Odporność na korozję elektrochemiczną badano w 5% roztworze NaCl przy zastosowaniu techniki polaryzacji potencjodynamicznej oraz elektrochemicznej spektroskopii impedancji. Powłoki poddano także ocenie jakościowej w badaniach odporności na działanie obojętnej mgły solnej zgodnie z normą PN-EN ISO 9227:2007. Charakterystykę materiału badań przed i po badaniach korozyjnych przeprowadzono za pomocą skaningowej mikroskopii elektronowej oraz dyfrakcji promieni rentgenowskich. Sugerowaną przyczyną poprawy właściwości ochronnych powłoki Ni-W po obróbce cieplnej jest modyfikacja jej struktury.

This work presents the results of investigations concerning an assessement of corrosion resistance of the Ni-W coatings electrodeposited on a carbon steel substrate using galvanostatic method, before and after heat treatment in air at temp. 900°C. Resistance to electrochemical corrosion was tested in 5% NaCl solution using potentiodynamic polarization technique and electrochemical impedance spectroscopy. The coatings were also subjected to a qualitative assessement in tests of resistance to neutral salt fog effect according to PN-EN ISO 9227:2007 standard. Characteristics of the material under investigation before and after corrosive tests was carried out using scanning electron micrsocopy and X-ray diffraction. Suggested reason for the improvement of protective properties of the Ni-W coating after heat treatment is the modification of its structure.

Optimization of galvanic bath and operating parameters for amorphous Ni-W electrodeposition

Indyka A., Bełtowska-Lehman E., Bigos A., Tarkowski L., Kot M., Morgiel J.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

377-381

The electroplating of Ni-W amorphous coatings from citrate aqueous solutions was studied with the aim of determination the optimal condition to obtain high tungsten content and good quality of the deposits. The influence of bath composition and the operating parameters on the tungsten content and the alloy properties were discussed. It was shown that the most important variable determining the alloy chemical composition and current efficiency is the concentration of tungstate ions in solution. As the WO4 2- concentration in the bath was increased, at a constant Ni(II) species content, the tungsten content in the alloy increased too, whereas the Faradaic efficiency decreased. No effect of mass transport limitation on Ni-W electrodeposition process was observed. The amorphous coatings are formed when the tungsten content is higher than about 40 wt. %. The obtained deposits containing considerable amount of tungsten (>60 wt. %) revealed a characteristic crack pattern, although they were well adherent to the steel substrate.

W celu określenia optymalnych warunków otrzymywania dobrej jakości amorficznych powłok Ni-W, zawierających dużą zawartość wolframu, badano proces elektroosadzania z wodnych, cytrynianowych roztworów. Określono wpływ składu kąpieli oraz parametrów operacyjnych na zawartość wolframu w stopie i jego właściwości. Wykazano, że stężenie jonów wolframianowych w roztworze jest najważniejszą zmienną determinującą skład chemiczny stopów i katodową wydajność prądową. Ze wzrostem stężenia jonów WO4 2- w kąpieli, przy stałej zawartości Ni(II), wzrasta zawartość wolframu w powłoce oraz maleje katodowa wydajność prądowa. Nie zaobserwowano wpływu szybkości transportu masy na proces elektroosadzania Ni-W. Stwierdzono, że powłoki amorficzne tworzą się przy zawartości wolframu większej od około 40% mas. Otrzymane powłoki o znacznej zawartości wolframu (>60% mas.) charakteryzują się siatką mikrospękań, pomimo dobrej adhezji do stalowego podłoża.