Deposition of phosphate coatings on titanium within scaffold structure

Trybuś B., Zieliński A., Beutner R., Seramak T., Scharnweber D.

Acta of Bioengineering and Biomechanics

|

2017

|

Vol. 19, no. 2

65--72

EN

Purpose. Existing knowledge about the appearance, thickness, and chemical composition of 37 phosphate coatings on titanium inside porous structures is insufficient. Such knowledge is 38 important for the design and fabrication of porous implants. 39 Methods. Metallic scaffolds were fabricated by selective laser melting of 316L stainless steel 40 powder. Phosphate coatings were deposited on Ti sensors placed either outside the scaffolds 41 or in the holes in the scaffolds. The electrochemically-assisted cathodic deposition of 42 phosphate coatings was performed under galvanostatic conditions in an electrolyte containing 43 the calcium and phosphate ions. The phosphate deposits were microscopically investigated; 44 this included the performance of mass weight measurements and chemical analyses of the content of Ca2+ and PO4 2‒ 45 ions after the dissolution of deposits. 46 Results. The thicknesses of the calcium phosphate coatings were about 140 and 200 nm for 47 isolated titanium sensors and 170 and 300 nm for titanium sensors placed inside pores. 48 Deposition of calcium phosphate occurred inside the pores up to 150 mm below the scaffold 49 surface. The deposits were rich in Ca, with a Ca/P ratio ranging between 2 and 2.5. 50 Conclusions. Calcium phosphate coatings can be successfully deposited on a Ti surface 51 inside a model scaffold. An increase in cathodic current results in an increase in coating 52 thickness. Any decrease in the cathodic current inside the porous structure is slight. The 53 calcium phosphate inside the pores has a much higher Ca/P ratio than that of stoichiometric 54 HAp, likely due to a gradual increase in Ca fraction with distance from the surface.

2

Profilometry surface analysis of bonded magnets based on biencapsulated Nd-(Fe,Co)-B powder

Radomska K., Pawłowska G., Klimecka-Tatar D.

Ochrona przed Korozją

|

2014

|

nr 4

142--146

EN

In this paper the detailed evaluation of the bonded magnetic materials surface has been presented. Bonded magnets based on Nd-(Fe,Co)-B powder after biencapsulation with coating (phosphate/epoxy resin, Ni-P/epoxy resin). As a reference material, the bonded magnets based on powder encapsulated with epoxy resin was applied. The aim of this study was to analyze the surface of bonded magnetic materials based on Nd-(Fe,Co)-B subjected to different biencapsulation methods. In the work the measurements of roughness (2D) evaluated with contact profilometer (Taylor Hobson) as well as the surface analysis with SEM Phenom microscope (Labsoft) were performed. It was found that the used biencapsulation methods (especially phosphate/epoxy resin coating) have a positive impact on the surface of the bonded magnetic materials.

PL

W niniejszej pracy dokonano szczegółowej oceny powierzchni wiązanych materiałów magnetycznych Nd-(Fe,Co)-B wytworzonych z proszków po procesie bienkapsulacji powłokami ochronnymi (fosforan/żywica epoksydowa oraz Ni-P/żywica epoksydowa). Jako odnośnik zastosowano materiał po enkapsulacji żywicą epoksydową. Celem niniejszej pracy było dokonanie analizy warstwy wierzchniej wiązanych materiałów magnetycznych na bazie Nd-(Fe,Co)-B poddanych różnym procesom bienkapsulacji. W pracy dokonano pomiaru chropowatości (2D) z użyciem profilometru stykowego (Taylor Hobson) oraz analizę powierzchni na mikroskopie SEM Phenom firmy Labsoft. Stwierdzono, że zastosowane metody bienkapsulacji (zwłaszcza powłoka fosforan/żywica epoksydowa) mają korzystny wpływ na stan powierzchni wiązanych materiałów magnetycznych.

3

The disbonding of powder polyester coating on steel pretreated by zinc-phosphate and iron-phosphate coatings

Jegdic B. V., Popic J. P., Bajat J. B., Miskovic-Stankovic V. B

Ochrona przed Korozją

|

2013

|

nr 10

423--429

EN

The influence of different types of conversion phosphate coatings on the corrosion stability of top powder polyester coating on steel was investigated. The morphology of phosphate coatings was investigated using scanning electron microscopy (SEM), composition by energy dispersive X-ray spectroscopy (EDS) and surface coverage by voltametric anodic dissolution (VAD) technique. The corrosion stability of polyester coating on steel pretreated by phosphate coatings was investigated by electrochemical impedance spectroscopy (EIS). It was shown that small crystal nuclei of iron-phosphate coating have sporadically emerged on the steel substrate while zinc-phosphate coating had more compact structure with better surface coverage. After prolonged exposure, there was a significant decrease in Rp values for polyester/zinc-phosphate protective system, as a result of the disbondment of polyester coating, while Rp values for polyester coating on steel pretreated with iron-phosphate coating remained almost unchanged, pointing to a greater stability of this protective system.

PL

Zbadano wpływ różnych typów powłok fosforanowych na odporność na korozję stali pokrytej nawierzchniową powłoką poliestrową. Morfologię powłok fosforanowych badano za pomocą skaningowego mikroskopu elektronowego (SEM), skład za pomocą dyspersyjnej spektroskopii rentgenowskiej (EDS), a pokrycie powierzchni metodą woltamperometrycznego roztwarzania anodowego (VAD).Odporność na korozję powłoki poliestrowej nałożonej na stal fosforanowaną badano za pomocą elektrochemicznej spektroskopii impedancyjnej (EIS). Stwierdzono, że na podłożu stalowym pojawiły się sporadycznie niewielkie zarodki krystalizacji fosforanu żelaza, podczas gdy powłoka fosforanu cynku miała bardziej zwartą strukturę i wykazała lepsze pokrycie powierzchni. Po dłuższej ekspozycji nastąpił znaczący spadek wartości Rp dla układu powłoka poliestrowa / fosforan cynku, w wyniku odwarstwiania powłoki poliestrowej, podczas gdy wartości Rp powłok poliestrowych na stali z powłoką z fosforanu żelaza pozostały prawie niezmienione, wskazując na większą stabilność tego systemu ochronnego.

4

Właściwości ochronne powłok antykorozyjnych - porównanie wyników badań terenowych i przyspieszonych

Zubielewicz M., Kamińska-Tarnawska E.

Ochrona przed Korozją

|

2006

|

nr 5

155-159

PL

W 2004 roku przeprowadzono badania laboratoryjne właściwości powłok pigmentowanych fosforanem cynku i modyfi kowanym zasadowym fosforanem cynku, nałożonych na podłoża fosforanowane amorfi cznie i krystalicznieW celach porównawczych przebadano powłoki bez pigmentu antykorozyjnego oraz powłoki nałożone na podłoże niefosforanowane. Badania przyspieszone obejmowały oznaczanie nasiąkliwości, przepuszczalności pary wodnej, adhezji oraz właściwości antykorozyjnych, w komorze solnej i metodą elektrochemicznej spektroskopii impedancyjnej (EIS). W niniejszej publikacji omówiono wyniki 2-letnich badań powłok na stacji terenowej w Gliwicach i porównano je z wynikami badań przyspieszonych w komorze solnej. Stwierdzono dobrą korelację między wynikami uzyskanymi w warunkach naturalnych i przyspieszonych oraz synergicznie oddziaływanie pigmentów fosforanowych z powłoką konwersyjną.

EN

In 2004 laboratory investigations were carried out on the properties of coatings pigmented with zinc phosphate and modified basic zinc phosphate, applied on amorphous and crystalline phosphated steel surfaces. Both coatings without anticorrosive pigments and coatings applied on non-phosphated substrate were tested and compared. The accelerated tests were performed to determine the water absorption, water permeability, adhesion and anti-corrosive properties of the coatings in a salt spray test and EIS. The results of 2 year long studies of the coatings at a fi eld station in Gliwice have been presented in this publication. These results were afterwards compared with the results obtained in the accelerated tests in a salt spray chamber. A good correlation between the obtained results in the natural weathering tests and those in the accelerated tests was observed. Correspondingly, the synergism between the phosphate pigments and the conversion coating was also noted.