Effect of ZDDP and Fullerenes Added to PAO 8 Lubricant on Tribological Properties of the Surface Layer of Steel Bare Steel and W-DLC Coating

Kowalczyk Joanna, Kulczycki Andrzej, Madej Monika, Ozimina Dariusz

Tribologia

2022

nr 1

19--32

The paper presents the effect of adding zinc dialkyldithiophosphate (ZDDP) and/or fullerenes on the properties of tribological systems coated with diamond-like carbon coatings doped with tungsten (W-DLC) and 100Cr6 steel without coating. The tribological tests were performed using a ball-on-disc tribometer. Discs made of bare 100Cr6 steel and discs with W-DLC coating were used as samples. Balls made of 100Cr6 steel were used as counter samples. The lubricants used:poly (α) olefin oil PAO 8, PAO 8 + 1.5% of ZDDP, PAO 8+ 0.005% of C60 fullerenes and PAO 8 + 1.5% of ZDDP + 0.005% of C60 fullerenes. Observations of the W-DLC coating were carried out using a scanning microscope, and the EDS analysis enabled the identification of the chemical composition along the cross-sections of the coating. A confocal microscope operating in the interferometric mode was used to analyse the geometrical structure of the samples before and after the friction tests. Observations of the wear marks on the samples and counter-samples were also carried out using a scanning microscope, and the chemical composition on the surfaces of the friction pairs was determined. The obtained test results indicated that the PAO 8 + ZDDP + C60 lubricant caused a reduction in the coefficient of friction and the linear wear in the tested steel friction pairs. In the case of W-DLC coating, however, the ZDDP added to PAO 8 increased the resistance to motion with a simultaneous improvement in anti-wear properties.

W artykule zbadano wpływ dodatku w postaci dialkiloditiofosforanu cynku ZDDP i/lub fulerenów na właściwości systemów tribologicznych pokrytych diamentopodobnymi powłokami domieszkowanymi wolframem W-DLC oraz stali 100Cr6 bez pokrycia. Testy tribologiczne wykonano na testerze tribologicznym pracującym w skojarzeniu trącym kula-tarcza. Do badań jako próbek użyto tarcz ze stali 100Cr6 bez powłoki i z naniesioną powłoką W-DLC, a jako przeciwpróbek użyto kul ze stali 100Cr6. Badania przeprowadzono w warunkach smarowania olejem poli(α)olefinowym PAO 8, PAO 8 i 1,5% ZDDP, PAO 8 i 0,005% fulerenów C60 oraz PAO 8 i 1,5% ZDDP oraz 0,005% fulerenów C60. Za pomocą mikroskopu skaningowego wykonano obserwacje powłoki W-DLC, a analiza EDS umożliwiła identyfikację składu chemicznego na przekrojach poprzecznych powłoki. Mikroskop konfokalny z trybem interferometrycznym posłużył do analizy struktury geometrycznej próbek przed i po testach tarciowych. Przeprowadzono także obserwacje śladów wytarcia próbek i przeciwpróbek na mikroskopie skaningowym oraz określono skład chemiczny na powierzchniach par trących. Uzyskane wyniki badań wskazały, że substancja smarowa PAO 8 + ZDDP + C60 spowodowała zmniejszenie współczynnika tarcia i zużycia liniowego w badanych stalowych węzłach tarcia. Natomiast oddziaływanie ZDDP w przypadku powłoki W-DLC i PAO 8 wpłynęło na zwiększenie oporów ruchu z jednoczesną poprawą właściwości przeciwzużyciowych.

Optimisation of test parameters influencing the dry friction of W-DLC coated elements

Kalbarczyk M., Michalczewski R., Szczerek M., Trzos M., Wulczyński J.

Tribologia

2013

nr 6

35--46

The application of thin hard coatings, such as the DLC type, acquires growing importance in the area of machine elements working under conditions of friction. Due to mechanical properties, the thin hard coatings provide the increase in the durability of coated elements, the resistance to abrasion, and protection against corrosion. The structure of the coatings influences the tribological properties of friction joints by lowering the motion resistance. The extension of the area of coating application is connected with the development in the field of tribological research. One of the main issues of research quality is the spread of results, especially important while considering the friction coefficient and wear resistance of friction joints with coated elements. This paper presents the application of an optimization method for the selection of test parameters for the tribological research by means of a nanotribometer. The tested friction joint consisted of steel ball rubbing against a rotating steel disc with WC/C coating under conditions of low loads. The determination of optimal test parameters for the lowest possible results spreads were conducted according to the Taguchi approach. As a result of the performed research, the differentiation of analysed test parameters in the manner of influence on results spreads was determined. The optimal test parameter values are indicated in the study. The general effects of the conducted investigation are the recommendations for tests conduction by means of nanotribometer.

Twarde, cienkie powłoki przeciwzużyciowe, w tym DLC, są coraz częściej stosowane na elementy maszyn. Powłoki tego rodzaju charakteryzują się dobrymi właściwościami mechanicznymi, zapewniają bardzo dobrą odporność na utlenianie i mają bardzo dobre właściwości tribologiczne. Dalszy rozwój w tym obszarze wymaga zastosowania odpowiednich metod badawczych, zapewniających możliwie wysoką jakość wyznaczanych wartości wskaźników charakteryzujących właściwości tribologiczne. Istotny problem stanowią rozrzuty wyników badań tribologicznych, szczególnie współczynnika tarcia oraz zużycia. W artykule przedstawiono zastosowanie metody optymalizacji parametrów procesu tarcia w badaniach właściwości tribologicznych prowadzonych z wykorzystaniem nanotribometru. Badaniom poddano skojarzenie materiałowe powłoka W-DLC-stal. Wyznaczenie parametrów procesu optymalnych ze względu na rozrzut wyników przeprowadzono metodą optymalizacji zgodną z podejściem Taguchiego. W wyniku przeprowadzonych badań wykazano zróżnicowanie wpływu analizowanych parametrów na rozrzuty wyników pomiaru oraz wyznaczono wartości optymalne parametrów. Rezultatem przeprowadzonych analiz są zalecenia prowadzenia pomiarów wartości wskaźników tribologicznych z zastosowaniem nanotribometru.