An investigation into the effect of alloying elements on corrosion behavior of severely deformed Cu-Sn alloys by equal channel angular pressing

Ebrahimi M., Attarilar Sh., Shaeri M. H., Gode C., Armoon H., Djavanroodi F.

Archives of Civil and Mechanical Engineering

|

2019

|

Vol. 19, no. 3

842--850

EN

To overcome some possible deficiencies of pure copper, dilute alloying and employment of equal channel angular pressing seem the cost-effective solutions. In this work, dilute copper alloys with the tin amount of 0.18, 0.3, and 0.5 wt.% were obtained with continuous casting and subsequently, they were subjected to ECAP process up to four passes. It was shown that integrated treatment by dilute alloying and ECAP lead to 182% improvement of the corrosion resistance as compared to the as-received condition due to the grain refinement. Meanwhile, the alloying impact on current density is decreased with the ECAP process which may result from the changes at the distribution of Sn atoms in Cu. The difference in measured corrosion current density of unprocessed and ECAPed samples for the alloys Cu-0.3%Sn and Cu-0.5%Sn are 15% and 2%, respectively. The corrosion improvement by means of current density reduction due to the alloying before the ECAP process is about 45% while this value after the ECAP diminishes to 35%. Microstructure analysis showed that four passes of ECAP process cause the average grain size of the pure copper to less than 700 nm and the Cu-0.5%Sn to about 550 nm. Also, the HAGBs fraction of the ECAPed pure Cu is 74%, while the correspond-ing magnitude for the Cu-0.5%Sn is 78%.

2

Wybrane aspekty prognozowania poziomu korozji stali zbrojeniowej w betonie metodą elektrochemiczną

Raczkiewicz W., Wójcicki A.

Przegląd Spawalnictwa

|

2017

|

R. 89, nr 11

28--33

PL

Korozja stali zbrojeniowej w betonie jest często trudna do wykrycia ze względu na brak widocznych zmian na powierzchni elementów. Pomocne są w tym przypadku nieniszczące metody diagnostyczne. Jedną z nich jest metoda impulsu galwanostatycznego. Metoda ta pozwala ustalić obszary występowania korozji oraz oszacować aktywność korozyjną zbrojenia. W artykule opisano sposób badań przy użyciu zestawu GP-5000 GalvaPulseTM. Zestaw ten umożliwia jednoczesny pomiar trzech wielkości: potencjału stacjonarnego zbrojenia, rezystywności otuliny betonowej oraz gęstości prądu korozyjnego, które odniesione do pewnych wartości granicznych pozwalają ocenić zagrożenie korozyjne zbrojenia. W artykule przedstawiono metodykę prowadzenia pomiarów, zaprezentowano przykładowe wyniki badań, przedstawiono sposób ich analizy i wnioski dotyczące możliwości wykorzystania metody w praktyce.

EN

Steel reinforcement corrosion in concrete is sometimes difficult to detect because of the lack of visible changes on the element surface. Therefore some non-destructive methods are used. One of them is the galvanostatic pulse method. This electrochemical method allows to determine the corrosion areas and estimate the steel bars corrosion activity. This article presents a test method by using the GP- 5000 GalvaPulseTM set. Using this apparatus it is possible to measure three parameters simultaneously: reinforcement stationary potential, concrete cover resistivity and corrosion current density that referred to the appropriate criteria allow to evaluate the reinforcement corrosion risk. The paper presents the methodology of measurements as well as the experimental test results, the analysis method of them and the conclusions about possibilities of using this method in practice.

3

Laboratory tool for electrochemical study of sulphide minerals

Galfi I., Aromaa J., Forsen O.

Physicochemical Problems of Mineral Processing

|

2007

|

Vol. 41

301-312

EN

Sulphide mineral dissolution in aqueous media occurs by different mechanisms. The rate of the overall reaction is controlled by the rate of the slowest reaction step. Most important factor in the anodic dissolution of mineral sulphides is the formation of a reaction product layer, which affects the mass transfer rate, often the rate determining step of the overall reaction. In this work we have used electrochemical tests for evaluating factors affecting sulphide mineral dissolution. As an essential tool, an electrochemical measurement method for leaching behaviour of sulphide minerals has been developed. Development of a graphite paste electrode (GPE) for the electrochemical measurements has made it possible to investigate powdered sulphide mineral samples. This ensures that the measurement conditions are as close as possible to the real leaching conditions. The graphite paste electrode makes it possible to run electrochemical measurements reproducibly and reliably.

PL

Roztwarzanie minerału siarczkowego w roztworach wodnych zachodzi na drodze różnych mechanizmów. Szybkość całkowitej reakcji jest kontrolowana przez szybkość najwolniejszego etapu reakcji. Najważniejszym czynnikiem w anodowym rozkładzie minerałów siarczkowych jest tworzenie warstwy produktu reakcji, która wpływa na szybkość wymiany masy na granicy faza stała – roztwór, która jest często etapem kontrolującym proces roztwarzania minerału. W tej pracy użyliśmy elektrochemicznej metody oceny podatności surowców siarczkowych na proces ługowania. Jako podstawowe narzędzie tej metody zastosowaliśmy pomiary elektrochemiczne na elektrodach wykonanych z badanego surowca. Elektrody użyte w pomiarach są wykonane w postaci pasty z udziałem grafitu i drobnoziarnistego materiału siarczkowego. Taka konstrukcja elektrody zapewnia warunki bliskie tym, jakie występują w rzeczywistym procesie ługowania. Grafitowa elektroda w formie pasty zawierającej siarczki metali gwarantuje dużą powtarzalność i niezawodność.