1

Laboratory studies of the influence of thermal cycling on anti-wear properties of composites used in biotribological friction PAIRS

Walczak A., Pieniak D., Niewczas A. M., Gil L.

Tribologia

|

2018

|

nr 4

143--149

EN

This paper presents the problems associated with changes in resistance to the tribological wear of light-cured polymer matrix ceramic composites (LC PMCCs) used in conservative dentistry and in dental prosthetics (fillings of carious cavities, dental bridges, structural reinforcements of the dental arch). Wear resistance of the surface layer of PMCCs depends on the time of exposure to the conditions of the oral environment, such as alternating temperatures and the exposure to liquids. The aim of the study was to assess changes in the mechanical properties of the surface layer under thermal cycling in liquid. Indentation hardness tests and scratch tests were performed before and after conditioning. Conditioning included 10,000 cycles of step temperature changes (10–70°C). The results of the scratch tests showed that universal composites that had relatively high filler contents were more resistant to scratching than flow type composites with lower filler contents. It was found that cyclic changes in ambient temperature reduced the wear resistance of universal composites but improved the resistance of flow type composites. In addition, in the case of flow type composites, the hardness of the surface layer was also increased.

PL

W pracy zaprezentowano problematykę zmian odporności na zużycie tribologiczne światłoutwardzalnych kompozytów polimerowo-ceramicznych (LC PMCCs–light-cured polymer matrix ceramic composites) stosowanych w stomatologii zachowawczej oraz w protetyce stomatologicznej (wypełnienia ubytków próchnicowych w zębach, mosty stomatologiczne, wzmocnienia konstrukcyjne łuku zębowego). Odporność na zużycie warstwy wierzchniej PMCCs jest cechą zależną od czasu oddziaływania środowiska jamy ustnej, między innymi zmiennej temperatury i obecności płynów. Celem pracy była ocena zmian właściwości mechanicznych warstwy wierzchniej ze względu na cykliczne oddziaływanie płynów o zmiennej temperaturze. Badano twardość indentacyjną i ślad zarysowania przed i po kondycjonowaniu. Kondycjonowanie obejmowało 10 tys. cykli skokowej zmiany temperatury (10–70°C). Wyniki testu zarysowania wykazały, że materiały typu uniwersalnego o względnie dużej zawartości wypełniacza są bardziej odporne na zarysowania niż materiały typu flow o mniejszej zawartości wypełniacza. Stwierdzono, że cykliczne zmiany temperatury otoczenia zmniejszają odporność na zużycie kompozytów uniwersalnych, natomiast poprawiają odporność kompozytów typu flow. Ponadto w przypadku kompozytów typu flow obserwowano umocnienie warstwy wierzchniej polegające na wzroście twardości.

2

Propozycja oceny skurczu odlewniczego hybrydowych kompozytów epoksydowych stosowanych w transporcie morskim i lądowym

Bryll K., Deja A., Kaszycki L.

Autobusy : technika, eksploatacja, systemy transportowe

|

2018

|

R. 19, nr 12

62--65

PL

W niniejszej pracy określano wpływ połączenia dwóch materiałów fazy umocnienia, o skrajnych właściwościach mechanicznych, na skurcz objętościowy kompozytów hybrydowych o osnowie epoksydowej. Do badań zastosowano jako materiał umocnienia tworzywo pochodzące z recyklingu materiałowego ze względu na rozwijający się przemysł stoczniowy, który dąży do poszukiwań nowoczesnych sposobów zagospodarowania odpadów, powstających przy demontażu małych jednostek pływających. Materiał badawczy wytworzono w wyniku odlewania grawitacyjnego do formy półotwartej. Powstały kompozyt to: osnowa - żywica epoksydowa oraz umocnienie - włókna szklanego w udziale masowym 1%, jak również pianka poliuretanowa w udziale 1% do 10% masowym.

EN

This work determines the effect of combining two reinforcement phase materials, with extreme mechanical properties, on volume shrinkage of hybrid epoxy based composites. The strenghtening material used for the research was material recycled due to the developing shipbuilding industry, which seeks to search for modern ways of waste management, arising during the dismantling of small vessels. The research material was created as a result of gravity casting into a semi-open form of epoxy resin matrix and reinforcement of fiber glass (in mass fraction of 1%), as well as polyurethane foam (in the proportion of 1% to 10% by mass).

3

Influence of photopolymerization parameters on the mechanical properties of polymer : ceramic composites applied in the conservative dentistry

Pieniak D., Niewczas A. M., Walczak M., Zamościńska J.

Acta of Bioengineering and Biomechanics

|

2014

|

Vol. 16, no. 3

29--35

EN

In this paper the results of study of mechanical properties for four commercial polymer-ceramic composites applied in the conservative dentistry are presented, including one new silorane based composite and three standard composites based on methacrylate compounds. Influence of the type of light of diode and halogen polymerization lamps on the microhardness, flexural strength and elasticity were studied. Both exposed and unexposed specimens were taken into account. An exposure time was also differentiated (40 sec and 60 sec). Basic statistics of the analysed material parameters were determined. A post hoc test (Newman-Keuls) was performed in order to evaluate differences between microhardness of the studied materials, as well as Kruskal-Wallis test to evaluate differences in flexural strength and elasticity modulus of the material. It has been indicated that there is an impact of the type of lamp on the microhardness and flexural strength of composites with methacrylate matrix and lack of such impact in case of composites containing siloranes. Additionally, it has been found that an increase of photopolymerization time has a significantly different impact on the mechanical properties depending on the type of irradiated material.

4

Pianki korundowe do infiltracji metalami i polimerami

Potoczek M., Śliwa R. E., Ligoda J.

Rudy i Metale Nieżelazne

|

2013

|

R. 58, nr 11

704--708

PL

Kompozyty metalowo-ceramiczne, a także polimerowo-ceramiczne o strukturze infiltrowanej charakteryzują się unikalną przestrzenną strukturą wzajemnie przenikających się szkieletów fazy metalowej lub polimerowej i fazy ceramicznej. Najczęstszym sposobem wytwarzania tego typu kompozytów jest infiltracja ciekłego metalu lub polimeru do porowatej kształtki ceramicznej. Do infiltracji ciekłymi metalami lub polimerami zastosowano piankowe kształtki korundowe (α-Al2O3), wytworzone metodą żelowania spienionej zawiesiny (ang. gelcasting of foams). W procesie infiltracji ciśnieniowej stopu AlMg5 do pianki korundowej uzyskano kompozyt metalowo-ceramiczny (AlMg5/Al2O3) o strukturze infiltrowanej charakteryzujący się pełnym wypełnieniem komórek pianki przez metal i dobrym przyleganiem na granicy faz ceramika/metal. Stwierdzono, że kompozyt AlMg5/Al2O3 w porównaniu do stopu AlMg5 może osiągać wyższe wartości naprężeń ściskających. Wytworzono także kompozyty korundowo-polimerowe o osnowie z pianki ceramicznej, stosując jako wypełnienie elastyczny poliuretan oraz żywicę epoksydową. Stwierdzono, że kompozyt żywica epoksydowa/pianka korundowa w porównaniu do pianki korundowej może osiągać wyższe wartości naprężeń ściskających, a kompozyt poliuretan/pianka korundowa większe odkształcenia nie powodujące zniszczeń.

EN

Metal-ceramic composites or polymer-ceramic composites are characterized by a unique spatial structure of interpenetrating phase being metal or polymer and ceramic phase. The most common method for manufacturing such composites is the infiltration of molten metal, or polymer into porous ceramics. In this paper the alumnia foams (α-Al2O3) manufactured by gelcasting of foams method were used as proforms for metal or polymer infiltration. A direct pressure infiltration process was used to infiltrate the alumina foams with an AlMg5 alloy resulting in an interpenetrating microstructure. Due to the open cell structure of the Al2O3 foams, macropores in alumina preform were completely filled by metal. Microstructural characterization of the composites revealed a special topology of skeleton and good integrity of metal/ceramic interface. It was found that AlMg5/Al2O3 composites were characterized high compression strength, better than an AlMg5 alloy. Polymer- ceramics composites were also manufactured in the process of infiltration of a polyurethane or epoxy resin into alumina foams. It was found that epoxy/alumina foams composites were characterized high compression strength, better than the alumina foam as well as the polyurethane/alumina foams composites were characterized by ability to achieve large deformation.

5

Zastosowanie kompozytów ceramika - polimer o osnowie z ceramicznego tworzywa porowatego z fosforanów wapniowych w inżynierii tkankowej

Szafran M., Bobryk E., Rzeszutek R., Chróścicka A., Lewandowska-Szumieł M.

Inżynieria Biomateriałów

|

2005

|

R. 8, nr 47-53

92--96

PL

W artykule przedstawione zostały wyniki badań nad otrzymaniem materiału kompozytowego ceramiczno-polimerowego o osnowie z ceramicznego tworzywa porowatego. W opracowanym kompozycie fazę ceramiczną stanowi porowaty spiek z mieszaniny hydroksyapatytu i fosforanu wapnia, a fazą polimerową wypełniającą pory ceramicznego tworzywa ceramicznego jest biodegradowalny makromonomer laktydowo-węglanowy, w różnym stopniu wypełniający pory ceramicznej osnowy. Opracowane materiały zostały poddane wstępnym badaniom pozwalającym zakwalifikować kompozyt jako nośnik dla żywych komórek a także sprawdzić możliwość stosowania tej grupy materiałów w inżynierii tkankowej. Z pierwszych prób wynika, że zastosowane materiały z fosforanów wapnia są dobrze tolerowane przez ludzkie komórki osteogenne w hodowli in vitro.

EN

The paper presents the results of studies on obtaining polymer-ceramic composites based on a porous ceramic material. In the composite developed the ceramic phase consists of a porous ceramic sinter of a mixture of hydroxyapatite and calcium phosphate, and the polymer phase, filling the pores of the ceramic material, consists of a biodegradable lactide-carbonate macromonomer which fills, to a variable degree, the pores of the ceramic base. The obtained materials were subjected to preliminary investigations enabling to qualify the composite as a carrier for living cells an to check the possibility of using this group of materials in the tissue engineering. Preliminary tests have shown that the calcium phosphate materials used are well tolerated by osteogenic human cells in in vitro cultures.