A series of PLGA (poly L-lactide-co-glycolide) based composites modified with gel-derived glasses in the form of foils were obtained by solvent casting procedure. As a modifier, glass particles with different chemical compositions from the CaO–SiO2, CaO–P2O5–SiO2,and Al2O3–SiO2 systems were used. All glasses were synthesized by the sol-gel process. Evaluation of bioactive properties of obtained composites was made on the basis of surface changes occurring during contact with simulated body fluid. The changes of Ca, P and Si ions concentration in SBF after incubation of composites were also measured. The result showed that all composites with bioglasses (CaO–SiO2, CaO–P2O5–SiO2) exhibit formation of calcium phosphates layer after SBF test, however, kinetics of Ca, Si ion release and P uptake from SBF was dependent on bioglass chemical composition. The higher solubility, as well as faster consumption of phosphorus from SBF, was observed for materials from CaO–SiO2 (T1/PLGA, S1/PLGA) compared to composites with respective bioglass particles from the CaO–P2O5–SiO2(T2/PLGA, S2/PLGA). Our results showed that rate of Si and Ca release from the gel-derived glasses and P uptake from SBF are dependent on both: the concentration of respective ions in the materials and the presence of phosphates in their structure. For materials modified with gel-derived glasses from Al2O3–SiO2 system no significant surface changes during contact with SBF were observed, and it seems that their behavior in physiological solution indicate that they are bio-inert materials.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Kompozyty polimerowo-ceramiczne o strukturze infiltrowanej charakteryzują się unikatową przestrzenną strukturą wzajemnie przenikających się szkieletów fazy polimerowej i ceramicznej. Jednym ze sposobów wytwarzania tego typu kompozytów jest infiltracja ciekłego polimeru do porowatej kształtki ceramicznej. W niniejszej pracy zastosowano kształtki z ceramiki korundowej o budowie pianki, wytworzone metodą żelowania spienionej zawiesiny (ang. gelcasting of foams). Zaletą tej ceramiki jest wyższa wytrzymałość mechaniczna w porównaniu z wytrzymałością wysokoporowatej ceramiki otrzymywanej dotychczas najbardziej popularną techniką, którą jest osadzenie ceramicznej masy lejnej na spienionym podłożu polimerowym (ang. polymeric sponge method). Przed procesem infiltracji wyznaczono porowatość całkowitą i otwartą pianek, a także rozmiar makroporów i połączeń pomiędzy makroporami. Wyznaczono także wytrzymałość na ściskanie, a także przepuszczalność pianek korundowych. Pianki ceramiczne infiltrowano trójfunkcyjną żywicą epoksydową, aby otrzymać materiały kompozytowe charakteryzujące się zwiększoną wytrzymałością mechaniczną oraz zmniejszoną palnością, przy jednocześnie małej gęstości – mogące mieć potencjalne zastosowanie w lotnictwie.
EN
Ceramic-polymer composites are characterized by the unique spatial structure of interpenetrating skeletons of polymer and ceramic phases. Infiltration of a liquid polymer into a porous ceramic material is the way of producing these type of composites. In this paper, alumina (α-Al2O3) samples of a foam structure produced by the gelcasting of foams process were used. The advantage of ceramic foams manufactured by the gelcasting method is higher mechanical strength when compared to those produced by the most popular technique known as the polymeric sponge method. Before the infiltration process, the alumina samples were characterized in terms of total and open porosity; sizes of macropores and interconnections between macropores were also determined. Compressive strength and permeability of the alumina foams were studied. The alumina foams were infiltrated by three-functional epoxy resins in order to obtain composite materials of low density having enhanced mechanical strengths and reduced flammability. These materials have potential application in aerospace industry.
Kompozyty polimerowo-ceramiczne są powszechnie stosowane jako opakowania elektroniczne. W artykule przedstawiono właściwości dielektryczne kompozytów złożonych z termoplastycznych polimerów PET i PPS i napełniacza w postaci cząstek ceramicznych tytanianu baru (BT). Określono wpływ stężenia napełniacza na przenikalność elektryczną oraz stratność dielektryczną tych kompozytów.
EN
Polymer/ceramic nanocomposites designed for electronic packaging. The dielectric properti of the composites made from polyethylene terephthalate (PET), polyphenylene sulphide (PPS) an barium titanate (BT) were studied as a function of BaTi03 fraction. Processing parameters ε optimized in order to obtain the composites with appropriate dielectric properties like dielectri permittivity e' and dielectric losses ε.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.