EN
In this paper the results of accelerated aging tests of two grades of polybutylene terephthalate (PBT) are presented. The degradation process of the mechanical properties was monitored with the help of 3-point bending test, supported with the results of gel permeation chromatography (GPC) measurements. Based on performed experiments, it can be concluded that the hydrolysis resistant (HR) PBT ages approximately 3 times slower as compared to standard grade. To predict the long-term behaviour of studied materials, the time-temperature superposition concept was applied. The respective shift factors, describing degradation of material properties as a function of time, were derived. It was found that the temperature increases by 10°C and relative humidity (RH) increase by 10% decrease the expected material life time by a factor of 2.5 and 1.3, respectively.
PL
W artykule przedstawiono wyniki przyspieszonych testów starzenia dwóch rodzajów poli(tereftalanu butylenu) (PBT). Proces degradacji właściwości mechanicznych monitorowano za pomocą 3-punktowego testu zginania, popartego wynikami pomiarów chromatografii żelowej (GPC). Na podstawie uzyskanych wyników stwierdzono, że PBT odporny na hydrolizę (HR) starzeje się ok. 3 razy wolniej w porównaniu ze standardową wersją. Aby przewidzieć długoterminowe zachowanie badanych materiałów, zastosowano koncepcję superpozycji czasowo-temperaturowej. Wyprowadzono odpowiednie czynniki przesunięcia opisujące degradację właściwości materiału w funkcji czasu. Stwierdzono, że wzrost temperatury o 10°C i wzrost wilgotności względnej (RH) o 10% zmniejszają przewidywany czas życia materiału o odpowiednio 2,5 i 1,3.
EN
The paper discusses the results of examinations of mechanical properties and examinations of the structure of composite polybutylene terephthalate with montmorillonite. The aim of the material examinations presented in this paper was to determine the effect of the content of the fillers on the structure and properties of the polymer composite. For this purpose, the examinations of tensile strength, hardness and topography of sample surface were performed for the surface of the specimens of the composite obtained using atomic-force microscope. The specimens of composites were obtained using the injection moulding method with processing parameters for which the best properties were obtained. The study revealed an insignificant increase in tensile strength for the specimens with addition of montmorillonite of 3 and 7% from 51 MPa for butylene polyterephthalate to 53 and 54 MPa, respectively. An increase in material Shore hardness was also found. All the composite specimens were characterized by hardness at similar level of 95 to 96 degrees on the Shore scale. An increase in hardness of the composites measured by means of the ball indentation test was observed compared to polybutylene terephthalate. Addition of montmorillonite of 3 and 7% leads to the increase in hardness from 130 MPa for polybutylene terephthalate to 143 and 148 MPa, respectively. Structural changes caused by the use of montmorillonite as a filler were observed in the examinations of surface topography. Several structural drawbacks linked to the adhesion between the matrix and the filler were also found.
PL
W artykule omówiono wyniki badań właściwości mechanicznych oraz badań struktury kompozytu politereftalanu butylenu z montmorylonitem. Celem badań materiałoznawczych było określenie wpływu zawartości zastosowanego napełniacza na strukturę i właściwości wytworzonego kompozytu polimerowego. W tym celu przeprowadzono badania: wytrzymałości na rozciąganie, twardości i topografii powierzchni próbek z wytworzonego kompozytu na mikroskopie sił atomowych. Badania przeprowadzono na próbkach kompozytów wytworzonych metodą wtryskiwania przy parametrach przetwórstwa, dla których uzyskano najkorzystniejsze właściwości. Badania wykazały nieznaczny wzrost wartości wytrzymałości na rozciąganie w próbkach z dodatkiem montmorylonitu 3 i 7% z 51 MPa dla politereftalanu butylenu do odpowiednio 53 i 54 MPa. Stwierdzono wzrost twardości wytworzonego materiału, stosując w badaniach metodę Shore’a. Wszystkie badane próbki kompozytów charakteryzowały się twardością na zbliżonym poziomie wynoszącą 95-96 stopni Shore’a. Zarejestrowano wzrost wartości twardości badanych kompozytów zmierzoną metodą wciskania kulki w porównaniu do politereftalanu butylenu. Dodatek montmorylonitu 3 i 7% powoduje wzrost twardości ze 130 MPa dla politereftalanu butylenu do odpowiednio 143 i 148 MPa. W badaniach topografii powierzchni zarejestrowano zmiany strukturalne spowodowane zastosowaniem montmorylonitu jako napełniacza. Stwierdzono pewne wady strukturalne związane z adhezją pomiędzy osnową a użytym napełniaczem.