Wyniki wyszukiwania - BazTech

1

Impact of Impurities of Polypropylene and Silicone Inclusions on the Properties of Polyamide 6.6 Regranulates Derived from the Re-Processing of Airbags

Stachowiak Tomasz

Archives of Metallurgy and Materials

|

2022

|

Vol. 67, iss. 2

455--463

EN

The following article presents the results of selected properties of regranulates of polyamide 6.6, regranules of polyamide contaminated with polypropylene and regranules of polyamide contaminated with silicone. The tested materials came from the reprocessing of polyamides 6.6 originally derived from production of airbags from renowned world producers (material for the research came from production waste). The results of examination were referred to regranulates of uncontaminated polyamide but also obtained from waste from the production of these airbags. The influence of impurities on properties of regranulates such as their density and melt flow index was assessed. The tests allowed to show a significant impact of impurities on the density but above all on the mass and volume flow rate index which ranged from 47 to 116 g/10 min. In the case of standardized test specimens selected thermal and mechanical properties were analyzed. Differential scanning calorimetry was used to assess the impact of impurities on the thermal properties of polyamides, allowing primarily identification of materials and impurities (especially polypropylene) as well as characteristic temperatures and the enthalpy of melting of the materials being analyzed. The mechanical properties were assessed using a DMA device. DMA research allowed to determine changes in mechanical properties in a wide temperature range of tested materials. It allowed to obtain full characteristics of changes in material stiffness under the influence of two factors, i.e. temperature and content of impurities, like polypropylene or silicone.

2

Właściwości mechaniczne mieszanin PC/PA 6.6 otrzymanych z recyklatów

Bednarek W. H., Gireń A., Szostak M., Paukszta D.

Przetwórstwo Tworzyw

|

2017

|

T. 23, Nr 4 (178)

261--265

PL

W związku z powszechnym zastosowaniem poliwęglanu oraz poliamidu 6.6 zasadne jest rozwijanie technologii recyklingu tych tworzyw. W ramach niniejszej pracy otrzymano mieszaniny polimerowe PC/PA 6.6 o różnej zawartości każdego z polimerów; z granulatów handlowych oraz recyklatów. Porównano właściwości mechaniczne mieszanin. Właściwości wytrzymałościowe mieszaniny PC/PA 6.6 poddanej recyklingowi są zbliżone do właściwości mieszaniny PC/PA 6.6 otrzymanej z granulatów handlowych. Materiały wytworzone z poliamidu oraz poliwęglanu poddanemu recyklingowi mogą być stosowane zamiennie z materiałami wytworzonymi z poliamidu oraz poliwęglanu niepoddanych powtórnemu przetworzeniu. Najmniej zadowalające właściwości użytkowe wykazała mieszanina zawierająca 50% wag. PC oraz 50% wag. PA 6.6.

EN

In view of the extensive use of PC and PA 6.6, it is reasonable to develop recycling technologies for these materials. The main aim of this study was to compare mechanical properties of PC/PA 6.6 blends with different content of each polymer. Moreover, the comparison between mechanical properties of blends made from commercial granules and recyclates was done. The strength properties of PC PA 6.6, made with use of recyclates are similar to those of the PC/PA 6.6 blends, obtained from commercial polymers. The least satisfactory mechanical properties presented the blend contained 50 wt% PA 6.6 and PC.

3

Badania wpływu starzenia UV na właściwości i strukturę kompozytów PA 6.6 z włóknem szklanym

Gnatowski A., Kwiatkowski D., Nabiałek J.

Kompozyty

|

2010

|

R. 10, nr 3

240-243

PL

W artykule omówiono wyniki badań wpływu procesu starzenia promieniowaniem UV na strukturę i właściwości próbek wykonanych z kompozytu poliamid 6.6/włókno szklane. Badania obejmowały: właściwości dynamiczne, analizę termiczną oraz strukturę nadcząsteczkową. Badania właściwości dynamicznych przeprowadzono metodą DMTA. Wyznaczono przebiegi zmian wartości modułu zachowawczego E' oraz tangensa kąta stratności mechanicznej tg[delta] w zależności od temperatury i częstotliwości drgań. Zbadano stopień krystaliczności metodą DSC oraz strukturę za pomocą mikroskopu optycznego w świetle przechodzącym. Badania przeprowadzono dla kompozytu poliamidu 6.6 z 25% zawartością włókna szklanego o nazwie firmowej Vampamid 66 2526 V0 Naturale 30, zarówno przed, jak i po procesie starzenia UV. Zaobserwowano zmiany wartości modułu zachowawczego i tangensa strat mechanicznych w funkcji temperatury oraz częstotliwości drgań dla próbek po procesie starzenia. W przeprowadzonych badaniach zarejestrowano najwyższe wartości modułu zachowawczego i tangensa strat mechanicznych dla kompozytów po starzeniu UV. Charakter zmian wartości modułu zachowawczego w funkcji temperatury jest jednakowy dla badanych częstotliwości drgań 1 i 10 Hz. Stwierdzono wpływ procesu starzenia na stopień krystaliczności, którego wartość zwiększa się w nieznacznym stopniu dla próbek badanego kompozytu po promieniowaniu UV.

EN

In this article the results of investigations of dynamical, thermal properties and structure of PA 6.6/glass fibre composite were presented. Determination of the influence of ultraviolet radiation ageing and frequency on dynamical properties of polyamide 6.6 composite is the aim of this work. DMTA method was used to determine the influence of a ultraviolet radiation ageing on dynamical properties of polyamide 6.6 composite. Using this equipment, dynamical properties of polyamide 6.6 composite in relation to the temperature and frequency were determined. Analysis of the influence of temperature and frequency on the storage modulus and loss tangent has been performed. The samples were bended with a frequency 1 Hz and 10 Hz in a temperature range from - 50 to 160°C and a heating rate 2 K/min. The increase of the value storage modulus for PA 6.6 with content of 25% of glass fibre addiction after ultraviolet radiation ageing was observed. The highest value of the storage modulus for PA 6.6/glass fibre composite was obtained 7341 MPa. For the sample of PA 6.6/glass fibre composite after ultraviolet radiation ageing the highest value of the storage modulus was obtained 8130 MPa. The similar dependence was obtained for a frequency 1 Hz and 10 Hz. With the increase of the temperature, the storage modulus decreases. It was found, that after ultraviolet radiation ageing increase value of tg[delta]. Investigations of crystallization degree by means of DSC method as well as investigations of the structure using optical microscope have been conducted. The DSC investigations prove the increase in the crystallization degree of PA 6.6/glass fibre composite for the samples after ultraviolet radiation ageing.

4

Wpływ przetwórstwa oraz wygrzewania na właściwości dynamiczne kompozytu poliamidu 6,6 z włóknem szklanym

Gnatowski A., Kwiatkowski D., Nabiałek J.

Kompozyty

|

2009

|

R. 9, nr 2

128-132

PL

Przedstawiono wyniki badań metodą DMTA modułu zachowawczego i tangensa strat mechanicznych kompozytu poliamidu 6,6 z włóknem szklanym. Badania kompozytu przeprowadzono przed i po wygrzewaniu. Do badań użyto kompozytu poliamidu 6,6 z 25% dodatkiem włókna szklanego o nazwie firmowej Vampamid 66 2526 V0 Naturale 30. Badania wykonano dla próbek z kompozytu wytworzonych metodą wtryskiwania przy różnych parametrach przetwórczych. Uzyskano istotne zmiany wartości modułu zachowawczego i tangensa strat mechanicznych w funkcji temperatury oraz częstotliwości drgań w zależności od temperatury wtryskiwania oraz temperatury formy. Również istotny wpływ na przebieg zmian wartości modułu zachowawczego i tangensa strat mechanicznych w funkcji temperatury zarejestrowano dla kompozytów poddanych wygrzewaniu. W przeprowadzonych badaniach zarejestrowano najwyższe wartości właściwości modułu zachowawczego dla kompozytów uzyskanych przy temperaturze wtryskiwania 280°C i temperaturze formy 80°C. Obniżając wartość temperatury przetwórstwa do 265°C, uzyskano niższe wartości modułu zachowawczego. Odwrotną zależność otrzymano dla próbek pod-danych wygrzewaniu. W tym przypadku zarejestrowano znaczny wzrost wartości modułu zachowawczego dla kompozytów poddanych wygrzewaniu, ale uzyskanych przy niższej temperaturze przetwórstwa.

EN

In this work the results of investigations of conservative modulus value and mechanical loss coefficient polyamide 6,6 with addition of glass fibre were presented. The main purpose of polymeric composites manufacturing is wish to eliminate or reduce drawbacks which polymers are characterised with and also to strive for reduction of the price of expensive polymers with particular, very precious properties by mixing them with fillers but without significant deterioration of their properties. Next purpose is to combine certain important properties of polymers with reduction their individual disadvantages. The properties of the polymer composites depend significantly on the type of the components and conditions of the injection moulding. That kind of influence manifests especially in the change of the dynamical properties. The investigations for the influence of conditions of the injection moulding on the properties of PA 6.6 composite with glass fibre commercial name of Vampamid 66 2526 V0 Naturale 30 have been conducted. Investigation have been conducted for the composite before as well as after soaking. Mechanical received characterizations as the result of research at the static load measured in the room temperature are inadequate to forecasting of the comportment of the material in given conditions of the use and longs. Fully to characterize properties of investigated composites and to rate material will keep in provided for conditions of the usage, was qualified temperature dependences of the value of dynamic Young modulus and the tangent of mechanical losses and was qualified the influence of the change of the frequency. It the influence of soaking and conditions of the injection moulding was established was, in this and glass fibre on conservative modulus value and mechanical loss coefficient. The highest value of the conservative module for PA 6.6 composite with glass fiber was obtained at injection temperature of 280°C and form temperature of 80°C. At the temperature of the processing 265°C lower values of the conservative module were registered. The inverse dependence was obtained for samples after soaking. In this case, the significant increase of the conservative module was registered for composites after soaking, but obtained at a lower temperature processing.

5

Charakterystyki tarciowe kompozytów poliamidowych współpracujących ślizgowo ze zmodyfikowanym elementem stalowym

Osuch-Słomka E., Piekoszewski W., Szczerek M.

Tribologia

|

2005

|

nr 3

267-274

PL

W pracy przedstawiono wyniki wpływu zawartości dwusiarczku molibdenu na charakterystyki tribologiczne kompozycji PA 6.6 w skojarzeniu tarciowym ze stalą ŁH15 i z nałożonymi na nią powłokami WC/C i CrN. W przypadku współpracy stosowanych układów materiałowych polimerowo-metalowych węzłów tarcia, czyli elementu stalowego z polimerem modyfikowanym dwusiarczkiem molibdenu otrzymano wyniki potwierdzające redukcję zużycia kompozytu oraz siły tarcia. Współpraca poliamidu PA 6.6 z elementem stalowym, którego powierzchnia została zmodyfikowana poprzez nałożenie powłoki WC/C i CrN wykazała zmniejszenie wartości współczynnika tarcia i intensywności zużycia w porównaniu ze współpracą z przeciwpróbką stalową niezmodyfikowaną.

EN

In this work was finding an effect of the content of disulphide of molybdenum (M0S2) on sliding properties of PA 6.6 composites in the contact with tool steel covered WC/C and CrN layers. Sliding properties were characterised by friction force and wear. Friction coefficient values and wear were plotted and analysed along sliding distance. Experiments were conducted under conditions of dry friction of ring-on-disk type, where disks were made of modified polyamide 6.6 composites and rings were made of steel modified wear resistant layers: WC/C and CrN. It was observed that an influence of filler on the sliding properties of PA 6.6 composites is easy to assess. For example, a decrease in friction with decreasing wear was shown (Fig. 5, 6). Movement resistances, linear abrasion and temperature as a function sliding distance shown in Fig. 1-4 for polymer - coating obtained on the steel.