Kondratowicz - Fibre-grade copoly(oxyethylene-b-ethylene terephthalate)s with improved optical properties

Ukielski R., Kondratowicz F. Ł.

Polimery

2008

T. 53, nr 3

224-227

The conditions of synthesis of block copoly(oxyethylene-b-ethylene terephthalate)s (PEG-b-PET) with good optical parameters and designed for the production of hydrophilic fibers are presented. For polycondensation the catalysts: antimony trioxide (Sb2O3) and titanium tetraisopropoxide [Ti(OiPr)4] were used. The best optical properties of the polymers were achieved by using the mixture of Sb2O3/Ti(OiPr)4 catalysts. The system which thermally stabilize the PEG-b-PET copolymers was selected. It was stated that the melting temperature (Tm) of the copolymer was insignificantly lower than that of the PET homopolymer (...T=11K) when the content of PEG 4000 comonomer amounts 30 wt. %. When the weight fraction of PEG 4000 in the copolymer does not exceed 20 wt. % a cold crystallization is observed.

Przedstawiono warunki syntezy blokowych kopoli(oksyetyleno-b-etylenotereftalanów) (PEG-b-PET) o dobrych parametrach barwy, przeznaczonych do produkcji włókien hydrofilowych. Do polikondensacji zastosowano katalizatory tritlenek antymonu (Sb2O3) oraz tetraizopropoksytytan [Ti(OiPr)4]. Najlepsze parametry barwy uzyskano stosując mieszaninę katalizatorów Sb2O3/Ti(OiPr)4. Wytypowano układ stabilizujący termicznie kopolimery PEG-b-PET. Stwierdzono, że przy zawartości 30% mas. komonomeru PEG 4000 temperatura topnienia PEG 4000-b-PET jest nieznacznie niższa od homopolimeru PET (?T=11K). Zauważono występowanie zimnej krystalizacji w kopolimerach PEG-b-PET o zawartości nie większej niż 20% mas. komonomeru.