Roughness Influence on Macro- and Micro-Tribology of Multi-Layered Hard Coatings on Carbon Fibre Polymer Composite

Lackner J. M., Major B., Waldhauser W., Mzyk A., Major Ł., Kot M.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 3

2145--2151

Goal of this work is the investigation of roughness influences on the abrasive wear behaviour of magnetron sputtered multi- -layered, low-friction coatings on carbon-fibre reinforced polymers (CFRP). Higher coating roughness at similar CFRP quality was realized by higher deposition rates, leading to increased heat flux to the substrates during deposition. Thermal expansion of the epoxy matrix on the micro scale results in a wavy, wrinkled surface topography. Both in scratch and reciprocal sliding testing against alumina, the friction coefficients are lower for the smooth coatings, but their wear rate is higher due to low-cycle fatigue caused abrasion.

Celem pracy jest badanie wpływów szorstkości na zużycia abrazyjne osadzonych magnetronowo wielowarstwowych powłoki o niskim współczynniku tarcia na bazie wzmocnionych włóknami węglowych polimerów (CFRP). Większa szorstkość powłoki przy podobnej jakości (CFRP) została uzyskana przez wyższe szybkości osadzania, co prowadziło do zwiększonego strumienia ciepła do podłoża podczas osadzania. Rozszerzalność cieplna matrycy epoksydowej w skali mikro pozwalała na uzyskanie falistej, pofałdowanej topografii powierzchni. Zarówno w teście zarysowania jak i ścierania z przeciwpróbką korundową uzyskano niższe współczynniki tarcia dla gładkich powierzchni zaś ich szybkość zużycia była wyższa ze względu na nisko-cyklowe zmęczenie wywołujace przetarcie.