This short review addresses the synthesis of thermoresponsive polymer surfaces and their application for cell tissue engineering. Four classes of synthetic thermoresponsive polymers are discussed: poly(N-isopropylacrylamide)s, poly[oligo(ethylene glycol)methacrylate]s, polyoxazolines and polyethers, most notably, polyglycidol. Synthetic routes leading to thermoresponsive layers on solid support are described. Relationships between structures of the layers and their interactions with cells are analyzed. Chemical (copolymerization or the inclusion of biologically active species) and physical (patterning or themorphology of the surfaces) modifications of macromolecular surfaces are described and their relations to the growth and detachment of cell sheets are reviewed. The application of cell sheets grown and detached from thermoresponsive surfaces to treat diseases is also presented.
PL
Praca stanowi przegląd literatury dotyczącej syntezy termoczułych powierzchni polimerowych i ichzastosowania w inżynierii tkankowej. Omówionocztery klasy termoczułych polimerów: poli(N-izopropyloakryloamidy),poli(metakrylany glikoli oligoetylenowych), polioksazoliny i polietery, w tymprzede wszystkim poliglicydol. Opisano syntetyczne szlaki prowadzące do termoczułych warstw stabilnie i kowalencyjnie związanych ze stałym podłożem. Przeanalizowano zależności między strukturą warstw a ich oddziaływaniem z komórkami. Omówiono chemiczne(kopolimeryzacja, dołączenie do polimerubiologicznie aktywnego związku) i fizyczne (modelowanie, morfologia powierzchni) modyfikacje powierzchni polimerowych oraz ich związek ze wzrostem i odczepianiem komórek. Przedstawiono również zastosowanie wyhodowanychi odczepionych od termoczułych powierzchni komórek w postaci arkusza wleczeniu różnych chorób.
W niniejszej pracy otrzymano równowagowe linie bazowe stanu stałego i ciekłego poli(N-izopropyloakryloamidu) (PNIPA) wykorzystując metody analizy termicznej. Linia odniesienia stanu stałego PNIPA została obliczona na podstawie założenia, że w temperaturze poniżej temperatury przejścia szklistego, eksperymentalne ciepło właściwe polimerów wynika tylko z oscylacyjnych ruchów molekularnych. Ponadto obliczono również równowagową linię bazową stanu ciekłego PNIPA. Na podstawie tak wyznaczonych linii odniesienia obliczono zmianę ciepła właściwego w temperaturze przejścia szklistego.
EN
In this paper, solid and liquid reference lines of poly(N-isopropylacrylamide) (PNIPA) were received using thermal analysis methods. The baseline of solid PNIPA was calculated based on the assumption that at a temperature below the glass transition temperature, major contribution to the experimental heat capacity have vibrational motions. Furthermore, the baseline of liquid PNIPA was established, too. On the basis of these reference lines of PNIPA, the change of heat capacity at the glass temperature was calculated.
3
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Acopolymer showing two cloud points was obtained by grafting poly(N-isopropylacrylamide) (PNIPAM) onto hydroxypropylcellulose (HPC). The structure of the polymer was verified using 1H NMR, FT-IR, GPC, and elemental analysis. The values of cloud points could be changed by increasing ionic strength and as a result of the interactions with surfactants.
PL
Metodą naszczepienia poli(N-izopropyloakryloamidu) (PNIPAM) na hydroksypropylocelulozie (HPC) otrzymano kopolimer wykazujący dwa punkty zmętnienia. Strukturę polimeru potwierdzono wykorzystując badania metodami 1H NMR, FT-IR, GPC oraz analizy elementarnej. Wartości temperatury w punktach zmętnienia ulegały zmianie w wyniku siły jonowej oraz w wyniku oddziaływań z surfaktantami.
4
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Scientists have made many attempts to develop smart textiles by grafting the copolymerisation of environment-responsive polymers (ERP) onto the surface of fabrics. Among the ERPs used for this purpose, poly(N-isopropyl acrylamide) (PNIPAAm) has attracted considerable attention due to its well-defined lower critical solution temperature (LCST) in an aqueous medium of temperature about 32-34°C, which is close to body temperature. This article summarises recent advances in the application of PNIPAAm and its copolymer hydrogels to temperature-sensitive hygroscopic fabrics, environment-sensitive deodorant fibres and stimuli-sensitive nutrient delivery fabrics. Another temperature sensitive poly(2-ethoxyethyl vinyl ether)/poly(hydroxyethyl vinyl ether) copolymer (EOVE200-HOVE40) is also briefly introduced, with regard to its application in thermally-controlled Vitamin E release.
PL
Naukowcy przeprowadzili wiele prób dla opracowania inteligentnych tekstyliów poprzez kopolimeryzację na powierzchni materiałów polimerów wrażliwych na warunki otoczenia. Z pośród tego rodzaju polimerów na szczególną uwagę zasługuje poli(N-izopropylo- akryloamid) ze względu na jego dokładnie zdefiniowaną dolną krytyczną temperaturę roztworu (LCST) dla wodnych roztworów, która wynosi około 32-34 oC, a więc jest bliska temperaturze ciała człowieka. W artykule podsumowano ostatnie osiągnięcia nad zastosowaniem poli(N-izopropylo-akryloamidu) i jego kopolimerów w postaci hydrożeli do higroskopijnych tkanin i dzianin wrażliwych na temperaturę, włókien zapachowych czułych na oddziaływanie otoczenia oraz materiałów stymulujących szybkość uwalniania odżywek. Skrótowo opisano również inny związek wrażliwy na temperaturę, a mianowicie kopolimer poli(2-etoksyetylo-winylo eteru) i poli(hydroksy-etylo-winylo eteru) (EOVE200-HOVE40), stosowany przy termicznie sterowanym uwalnianiu witaminy E.