The infuence of turning and burnishing on corrosion resistance of laser cladded Fe-Cr-Ni layer from viewpoints of thermodynamics and kinetics

Zhang Peirong, Ji Guosheng, Lv Tao, Hu Shunrui, Wang Bing, Liu Zhanqiang

Archives of Civil and Mechanical Engineering

|

2023

|

Vol. 23, no. 1

art. no. e3, 2023

EN

Laser cladding is commonly used to improve the wear and corrosion resistance of the substrate material. However, mechanical machining is necessary, because the surface irregularities and poor surface roughness after laser cladding. It is urgent to investigate the effect of machining on the corrosion resistance of the laser cladded layers, so as to avoid the reduction of corrosion resistance due to the use of inappropriate cutting parameters. In the present study, the influence of turning-induced surface roughness on the corrosion resistance from the viewpoint of corrosion potential was analyzed first. The corrosion potential is the result of the effect of roughness height parameters and functional parameters. Second, the effect of the machining and subsequent burnishing on the corrosion resistance was analyzed by comparing the corrosion behaviors of the turned and burnished surfaces. The polarization resistance is critically increased by subsequent burnishing. Third, the sensitivity of the machined surface on corrosion resistance was analyzed by EIS method. The strengthening mechanism of machining and subsequent burnishing on the corrosion resistance was determined. On the basis of this research, it is expected to be used to guide the selection of appropriate feed parameter in prior turning to improve the strengthening effect of subsequent burnishing, and then, to improve the surface integrity and corrosion resistance of the laser cladded layer.

2

Microstructure and Properties of Composite Produced by Vacuum Sintering of Vanadis 4 Extra Steel Powder with Tantalum Carbides and Following Heat Treatment

Huang Kuo-Tsung, Chang Shih-Hsien, Chuang Chan-Yu

Archives of Metallurgy and Materials

|

2020

|

Vol. 65, iss. 2

555--563

EN

In this study, different amounts of tantalum carbide (TaC) powders (5, 10 and 15 wt.%) are added to Vanadis 4 Extra steel powders. The composite powders are sintered at 1260, 1280, 1300, 1320, 1340 and 1360°C for 1 h, respectively. The experimental results showed that good mechanical properties (hardness 79.7 HRA, TRS 2246 MPa) were obtained by the addition of 10% TaC sintered at 1320°C for 1 h. Furthermore, the optimal sintered V4ES/TaC (Vanadis 4 Extra steel / TaC) composites after sub-zero treatment possess the highest hardness (80.9 HRA) and transverse rupture strength (TRS) values (2445 MPa), as well as a better polarization resistance (658.99 Ω·cm2). After sub-zero treatment, the VC carbides decompose and re-precipitate refined VC carbides within the grains (VC carbides are formed in steel powder); moreover, the TaC particles are still uniformly distributed around the grain boundaries, which results in dispersion strengthening and precipitation hardening. The results clearly reveal that sub-zero heat treatment effectively improves the microstructure and strengthens the V4ES/TaC composite.

3

Prosta metoda ograniczenia zasięgu polaryzacji w badaniach szybkości korozji zbrojenia w betonie

Jaśniok T., Jaśniok M.

Ochrona przed Korozją

|

2016

|

nr 6

210--213

PL

Przedstawiono założenia autorskiej metody ograniczenia zasięgu rozchodzenia się prądów polaryzacyjnych podczas badań szybkości korozji zbrojenia w betonie. Według założeń metody ograniczenie zasięgu polaryzacji uzyskuje się poprzez nacięcie całej grubości otuliny betonowej, tak aby średnica nacięcia odpowiadała średnicy kołowej przeciwelektrody w głowicy pomiarowej. Pierścieniowe nacięcie wypełnia się izolatorem elektrycznym, który równocześnie skleja lokalnie uszkodzony beton. W celu weryfikacji założeń proponowanej metody przeprowadzono badania elektrochemiczne metodami LPR i EIS w roztworze modelującym ciecz porową betonu. Elektrodą badaną był stalowy pręt ze stali gładkiej, natomiast elektrody pomocnicze wykonano w kształcie kołowej blachy i podłużnej siatki drucianej. Pierścieniowy izolator w cieczy porowej zamodelowano fragmentem rury z tworzywa sztucznego. W podsumowaniu analizowane zjawisko wyjaśniono przybliżonym modelem elektrycznym.

EN

This paper describes the original method of limiting polarization current distribution during the measurements of corrosion rate of reinforcement in concrete. On the basis of assumptions behind this method, the polarization range can be limited by cutting through the concrete cover thickness providing that the cut diameter corresponds to the diameter of a disk electrode in a measuring head. The ring-shaped cut is filled with an insulator which simultaneously fixes locally damaged concrete. Electrochemical measurements by LPR and EIS techniques were used to verify the assumptions of the proposed method in the solution simulating concrete pore solution. A working electrode was a smooth steel bar, and counter electrodes were made of circular metal plate and rectangular wire mesh. A fragment of the plastic pipe simulated the ring-shaped dielectric in the pore solution. In the summary, the approximate electrical model explains the analysed phenomenon.

4

Corrosion monitoring by harmonic analysis in aqueous environments

Orlikowski J., Łubiński S., Żuchowski P.

Ochrona przed Korozją

|

2013

|

nr 3

104--106

EN

This paper presents tests concerning the rate of corrosion in non-alloy steel (type S235JR) in an aqueous environment, with an additive of sodium chloride by means of polarization resistance measurements and harmonic analysis. The tests have been carried out for steel samples exposed to the testing environment for six weeks, in order to obtain a constant rate of corrosion in the function of time. The measurements have aimed at verifying the use of harmonic analysis in automatic corrosion monitoring systems. For this purpose, a typical three-electrode sensor, which is applied to measurements taken by means of automatic corrosion monitoring systems, has been used. In conclusion, the tests have revealed that harmonic analysis can be a measurement method to be applied in the design of corrosion monitoring systems.

PL

W niniejszej pracy wykonano badania szybkości korozji stali niestopowej typu S235JR w środowisku wodnym z dodatkiem chlorku sodu, metodami rezystancji polaryzacyjnej oraz analizy harmonicznej. Badania prowadzono po sześciotygodniowej ekspozycji próbek stali w badanym środowisku w celu osiągnięcia stałej szybkości korozji w funkcji czasu. Pomiary miały na celu sprawdzenie wykorzystania metody analizy harmonicznej w automatycznych systemach monitorowania korozji. W tym celu do badań wykorzystano typowy trójelektrodowy czujnik jaki stosowany jest w przypadku pomiarów automatycznym systemem monitorowania korozji. Badania wykazały, że metoda analiza harmonicznej może być techniką pomiarową, która może być wykorzystana do budowy systemów monitorowania korozji.

5

Wpływ umocnienia odkształceniowego na odporność na korozję elektrochemiczną drutów stosowanych w kardiologii

Przondziono J.

Hutnik, Wiadomości Hutnicze

|

2011

|

Vol. 78, nr 8

663--666

PL

W artykule przedstawiono wyniki badań wpływu odkształcenia w procesie ciągnienia oraz modyfikacji powierzchni na odporność na korozję elektrochemiczną drutów stosowanych na prowadniki kardiologiczne. Ustalono przebieg krzywej umocnienia drutów ze stali nierdzewnej X10CrNi18-8. Podano krzywe obrazujące zależność oporu polaryzacji w funkcji odkształcenia w procesie ciągnienia. Dzięki opracowanym zależnościom będzie można przewidzieć, jakimi właściwościami korozyjnymi będzie charakteryzował się drut o żądanej wytrzymałości ciągniony z zadanym odkształceniem.

EN

The article presents test results of the effect of strain in drawing process and surface modification on electrochemical corrosion resistance of wires used for cardiological guide wires. The course of flow curve for wires made of stainless steel X10CrNi18-8 was determined. Curves showing polarization resistance as the function of strain in drawing process were presented. Thanks to those formulated relations it will be possible to anticipate corrosion characteristics of wire featuring the required strength, drawn with the set strain.

6

Własności korozyjne cienkowarstwowych powłok TiN, CrN, TiCN, otrzymanych metodą łukowo-próżniową

Rogowska R.

Problemy Eksploatacji

|

2006

|

nr 3

181-188

PL

W artykule zaprezentowano odporność korozyjną powłok TiN, CrN, TiCN. Powłoki osadzono metodą łukowo-próżniową na stali SW7M i na węglu szklistym. Badania korozyjne powłok przeprowadzono w 0,8M roztworze NaCl. Wyznaczono potencjał obwodu otwartego, krzywe Tafela i Sterna, szybkość korozji, krzywą polaryzacji potencjodynamicznej i opór polaryzacji. Porównano właściwości korozyjne próbek pokrytych i niepokrytych powłokami. Uzyskane wyniki pokazują, że próbki ze stali SW7M pokryte powłokami posiadają potencjał korozyjny bardziej szlachetny.

EN

The article presents problems of corrosion resistance of TiN, CrN, TiCN coatings. The coatings were deposited on samples of SW7M steel and of the glass-carbon by means of the arc-vacuum method. The corrosion behaviour of TiN, CrN and TiCN coatings was examined in 0.8M NaCl solution. The study was performed using open circuit potential, Tafel and Stern curves, corrosion rate, potentiodynamic polarization curve and polarization resistance. The corrosion behaviour of coated and uncoated samples was compared. The results illustrate that coated specimens TiN, CrN, TiCN possess nobler potentials than the uncoated SW7M steel.

7

Rola wody, EBH i temperatury w preparatyce hybrydowych powłok otrzymywanych za pomocą metody zol-żel.

Głuszek J., Masalski J., Kucharczyk B., Golubski Z.

Inżynieria Materiałowa

|

2002

|

R. XXIII, nr 5

355-358

PL

Za pomocą metody zol-żel wytworzono na stali chirurgicznej typu 316L powłoki nieorganiczno-organiczne wykorzystując tetraetoksysilan (TEOS) i eter bisglicydowy hydrochinonu (EBH). Wielowarstwowe powłoki otrzymywano metodą zanurzeniową z zoli zawierających różne ilości TEOS-u, wody, alkoholu etylowego i EBH. Stosowano dwie różne temperatury wypalania powłok. Dokonano elektrochemicznej oceny właściwości ochronnych powłok w roztworze Ringera za pomocą metody stałoprądowej. W oparciu o chrakterystyki polaryzacyjne dokonano oceny jakości powłok. Posłużono się arbitralnie wybranymi wielkościami i -750mv, E2mi A. Wyłoniono siedem najlepszych powłok i uszeregowano je (ranking) biorąc pod uwagę dodatkowy, trzeci parametr opór polaryzacyjny. W preparatyce zoli najbardziej odpowiednim stosunkiem molowym prekursora TEOS do wody jest stosunek 1:5. Właściwości ochronne powłok wypalanych w temperaturze 300 stopni Celsjusza przewyższają właściwości ochronne powłok wypalanych w temperaturze 250 stopni Celsjusza. Nie można jednoznacznie określić, jaki jest wpływ EBH zawartego w zolu na odporność korozyjną powłok (zbyt mała rozpuszczalność EBH w zolu). Małe zmiany w preparatyce często wywierają nieproporcjonalnie duży wpływ na jakość powłoki.

EN

The inorganic-organic coatings on the surgical 316L stainless steel have been synthesized by sol-gel techniques from TEOS and EBH. The multilayer dip coatings have been prepared from sols with different molar ratios of TEOS, water, ethanol and EBH. Coatings have been heated at two different temperatures. The electrochemical estimation by d.c. (direct connect) measurements of protective coatings in Ringer's solution is reported. Coatings performance has been compared using polarization characteristics. Two arbitrary chosen values were applied: i-750mv and E2mu A. The best seven coatings were selected and ranked with regard to the additional parameter - the polarization resistance. In preparation of sols the most appropriate molar TEOS - water ratio was 1:5. Heat treatment at 300 degrees centigrade lead to more remarkable improvements in corrosion resistance of coatings than that at 250 degrees centigrade. It is impossible to univocally determine the effect of EBH content in sol on corrosion resistance of coatings (poor dissolution of EBH in sol). Small changes in the preparation process can often have disproportionate effect on the quality of coating.

8

Wpływ powłoki TiO2 na parametry korozyjne stali 1H13.

Szałkowska E., Głuszek J., Masalski J.

Inżynieria Materiałowa

|

2000

|

R. XXI, nr 6

453-456

PL

W pracy zbadano odporność korozyjną stali nierdzewnej 1H13 bez powłoki i z powłoką TiO2 w środowisku 0,5M H2SO4 w temp. 20 stopni Celsjusza. Powłokę TiO2 otrzymano metodą sol-gel. Jako prekursor tytanu zastosowano tetraizopropyloortotytanian Ti(C3H7O)4. Pomiary strukturalne wykazały, że powłoka TiO2 posiada strukturę krystaliczną typu rutylu. Na podstawie badań polaryzacyjnych ustalono, że powłoka TiO2 hamuje zarówno procesy katodowe jak i anodowe. Szybkość korozji (wyrażona za pomocą gęstości prądowych) jest około dwa rzędy wielkości mniejsza dla próbek stali 1H13 z powłoką TiO2 niż dla próbek bez pokrycia. Spektroskopowe widma impedancyjne stali niepokrytej, eksponowanej w roztworze przez 10 min, 30 min, 60 min i 240 min odpowiadają elektrycznemu obwodowi zastępczemu Randlesa R(RQ). Widmo uzyskane po 1440 min jest bardziej złożone, może być modelowane za pomocą obwodu R(C[RW(RQ)]). Opór przeniesienia ładunku jest zdecydowanie większy po 1440 min ekspozycji niż po krótkich czasach ekspozycji. Hamowaniu szybkości korozji sprzyjają powstałe na powierzchni produkty korozji. Zachowanie stali z powłoką TiO2 dobrze modeluje elektryczny obwód zastępczy (C[R(RQ)(RQ)]), który adekwatnie opisuje ten układ powłokowy zarówno przy krótkich jak i długich czasach ekspozycji. Środowisko korozyjne wywiera korzystny wpływ na zmianę oporu przeniesienia ładunku. Z wydłużeniem tego czasu opór ten rośnie.

EN

This paper presents the corrosion resistance of uncoated 1H13 steel and TiO2-coated 1H13 steel in 0,5M H2SO4 at 20 degrees centigrade. The TiO2 coating was obtained by sol-gel method. As the precursor tetraisopropyl orthotitanate Ti(C3H7O)4 was used. X-ray diffraction analysis indicated that obtained TiO2 coating was rutile type. Polarization experiments showed that the coating inhibits both cathodic and anodic processes, and that the corrosion rate of steel drops by 100 times, as compared to those of a bare steel surface. The equivalent circuit for modelling the impedance characteristics of uncoated stainless steel exposed to 0,5M H2SO4 (t= 10, 30, 60, 240 min.) is given by a simple Randles circuit R(RQ). The impedance spectrum obtained after 1440 min. is more complex. The R(C[RW(RQ)]) circuit is adequate for this spectrum. The polarization resistance (R2) is considerable higher after 1440 min. than after short time exposure. The corrosion rate is inhibited by corrosion products on steel surface. The electrochemical equivalent circuit (C[R(RQ)(RQ)]) is a suitable model for both short and long exposure of TiO2-coated 1H13 steel. Corrosive medium well affects the change of polarization resistance (R2). The longer is the time of exposure the resistance is higher.