PL
 |
EN
Preferencje help
Polish version English version Język
Widoczny [Schowaj] Abstrakt
Liczba wyników

Znaleziono wyników: 6

Liczba wyników na stronie
first rewind previous Strona / 1 next fast forward last
Wyniki wyszukiwania
Wyszukiwano:
w słowach kluczowych:  pneumokulkowanie
help Sortuj według:

help Ogranicz wyniki do:
first rewind previous Strona / 1 next fast forward last
1
Content available Relationship between 3D surface roughness parameters and load capacity of adhesive joints after shot peening
Zielecki Władysław, Świrad Sławomir, Ozga Ewelina
Technologia i Automatyzacja Montażu
|
2023
|
nr 3
35--43
EN
The aim of the article was to investigate whether roughness parameters in a 3D system can be used to assess the load capacity of adhesive lap joints strengthened in the shot peening process. The analyzes were carried out for single-lap adhesive joints made of EN AW-2024-T3 aluminum alloy, whose overlaps were shot peened for 60 to 180 s using balls with a diameter of 0.5 to 1.5 mm with a compressed air pressure of 0.3 to 0.5 MPa. As a result of the regression and correlation analysis, it was found that within the adopted range of input parameters variability, the load capacity of adhesive joints subjected to shot peening is most closely related to the roughness parameter Sdr. It has been shown that increasing the value of the Sdr parameter contributes to increasing the load capacity of adhesive joints. A mathematical model describing the impact of treatment time, balls diameter and compressed air pressure on the value of the Sdr parameter was also built. The model was built in accordance with the the Hartley's PS/DS-P:Ha3 plan methodology. The obtained results allow to conclude that the Sdr parameter can be used to predict the load capacity of adhesive joints after shot peening and thus to assess the strengthening treatment (within the assumed range of input parameters variability). Additionaly, the simplicity and low cost of roughness measurements justify the use of this method in industrial purposes.
PL
Celem artykułu było zbadanie, czy parametry chropowatości w układzie 3D mogą być stosowane do oceny nośności zakładkowych połączeń klejowych, umacnianych w procesie pneumokulkowania. Analizy przeprowadzono dla połączeń klejowych jednozakładkowych ze stopu aluminium EN AW-2024-T3, których zakadki pneumokulkowano w czasie od 60 do 180 s, kulkami o średnicy od 0,5 do 1,5 mm z ciśnieniem wynoszącym od 0,3 do 0,5 MPa. W wyniku przeprowadzonej analizy regresji i korelacji stwierdzono, że w przyjętym zakresie zmienności parametrów wejściowych, nośność połączeń klejowych poddanych pneumokulkowaniu jest najsilniej związana z parametrem chropowatości Sdr. Wykazano, że zwiększanie wartości parametru Sdr, przyczynia się do zwiększania nośności połączeń klejowych. Zbudowano również model matematyczny, opisujący wpływ czasu obróbki, średnicy kulek i ciśnienia sprężonowego powietrza na wartość parametru Sdr. Model zbudowano zgodnie z metodyką planu Hartleya PS/DS-P:Ha3. Uzyskane wyniki pozwalają na stwierdenie, że parameter Sdr może być wykorzystywany do przewidywania nośności połączeń klejowych po pneumokulkowaniu, a tym samym do oceny obróbki umacniającej (w przyjętym zakresie zmienności parametrów wejściowych), a prostota i niskie koszty pomiarów chropowatości przemawiają za słusznością użycia tej metody w celach przemysłowych.
2
Content available The influence of shot peening on the stress state in the adhesive layer and the load capacity of adhesive joints
Zielecki Władysław, Godzimirski Jan, Ozga Ewelina
Technologia i Automatyzacja Montażu
|
2022
|
nr 2
32--40
EN
The aim of the article was to determine the influence of shot peening of the outer surface of the overlap on the stress state in the adhesive layer and the load capacity of single lap adhesive joints made of EN AW-2024-T3 aluminum alloy. Experimental investigations and numerical simulations were carried out. According to the results of experimental analyses, shot peening with balls with a diameter of 1 mm for 120 s with a compressed air pressure of 0.5 MPa increased the load capacity of the adhesive joints by 33%. Numerical simulations have shown that shot peening, by deforming the joined elements, reduces the stress perpendicular to the surface of the adhesive layer which results in a reduction of equivalent (von Misses) stress and an increase in strength of adhesive joints.
PL
Celem artykułu było określenie wpływu pneumokulkowania zewnętrznej powierzchni zakładki na stan naprężeń w spoinie klejowej oraz nośność połączeń klejowych jednozakładkowych wykonanych ze stopu aluminium EN AW-2024-T3. W ramach badań przeprowadzono doświadczenia eksperymentalne i obliczenia numeryczne. Zgodnie z wynikami doświadczeń eksperymentalnych, pneumokulkowanie połączeń klejowych kulkami o średnicy 1 mm w czasie 120 s z ciśnieniem sprężonego powietrza wynoszącym 0,5 MPa przyczyniło się do wzrostu nośności połączeń klejowych o 33%. Obliczenia numeryczne wykazały, że pneumokulkowanie, poprzez odkształcenie klejonych elementów, zmniejsza naprężenia prostopadłe do powierzchni spoiny klejowej, co skutkuje zmniejszeniem jej wytężenia (naprężenień zredukowanych) i wzrostem wytrzymałości połączeń klejowych.
3
Content available Relationship between surface roughness and load capacity of adhesive joints made of aluminum alloy 2024-T3 after shot peening
Zielecki Władysław, Ozga Ewelina
Technologia i Automatyzacja Montażu
|
2022
|
nr 4
34--45
EN
The aim of the work was to investigate the influence of selected shot peening parameters on the load capacity of adhesive joints and on the surface roughness of samples made of aluminum alloy 2024-T3. The research was also aimed at verifying whether it is possible to assess the load capacity of adhesive joints on the basis of the surface roughness parameters after shot peening. The treatment variants were developed according to the matrix of the Hartley's PS/DS-P:Ha3 plan. Shot peening time varied from 60 to 180 s, ball diameter from 0.5 to 1.5 mm and compressed air pressure from 0.3 to 0.5 MPa. As a result of the analysis of the correlation between the load capacity of connections and the surface roughness, it can be concluded that the greatest relationship exists between the load capacity and the Rku parameter. The regression analysis shows that the load capacity of the connections should increase along with the increase of the Rku parameter. The study also showed that the Rku parameter is also most strongly associated with the deflection of the Almen strips. The Almen strip deflection increases with the increase of the Rku parameter. The regression equation describing the influence of shot peening parameters on the value of the Rku parameter indicates that the value of the Rku parameter increases with the increase of the treatment time and the decrease of the ball diameter and the compressed air pressure.
PL
Celem pracy było zbadanie wpływu wybranych parametrów pneumokulkowania na nośność połączeń klejowych oraz chropowatość powierzchni próbek ze stopu aluminium 2024-T3. Badania miały również na celu sprawdzenie, czy możliwa jest ocena nośności połączeń klejowych na podstawie parametrów chropowatości powierzchni po pneumokulkowaniu. Warianty pneumokulkowania opracowano zgodnie z matrycą planu Hartleya PS/DS-P:Ha3. Czas obróbki zmieniał się w zakresie od 60 do 180 s, średnica kulek od 0,5 do 1,5 mm i ciśnienie sprężonego powietrza od 0,3 do 0,5 MPa. W wyniku analizy korelacji miedzy nośnością połączeń i chropowatością powierzchni można stwierdzić, ze największa zależność występuje pomiędzy nośnością a parametrem Rku. Analiza regresji wskazuje, ze wraz ze zwiększaniem wartości parametru Rku nośność połączeń również powinna wzrastać. W ramach pracy wykazano również, że parametr Rku jest parametrem chropowatości najsilniej związanym ze strzałką ugięcia płytek Almena. Strzałka ugięcia płytek Almena wzrasta wraz ze wzrostem parametru Rku. Równanie regresji opisujące wpływ parametrów pneumokulkowania na wartość parametru Rku wskazuje, że wartość parametru Rku wzrasta wraz ze zwiększaniem czasu kulkowania i zmniejszaniem średnicy kulek i ciśnienia sprężonego powietrza.
4
Content available remote Wskaźniki kontrolne SGP pneumokulkowanych powierzchni elementów ze stopu MgAl8ZnMn
Kudyba U., Korzyńska K.
Zeszyty Naukowe Politechniki Rzeszowskiej. Mechanika
|
2010
|
z. 82 [278]
43-50
PL
Praca stanowi próbę wyłonienia reprezentatywnej grupy wskaźników struktury geometrycznej powierzchni (SGP) obrobionych przez pneumokulkowanie, wystarczającej do pełnej kontroli struktury takich powierzchni. Badania wykonano na próbkach ze stopu MgAl8ZnMn kulowanych na urządzeniu VaporBlast, a analizę wskaźników SGP wykonano na urządzeniu TayScan 150 z oprogramowaniem TalyMap 3D. Obliczono wzajemne korelacje pomiędzy dwudziestoma dwoma wybranymi parametrami, co pozwoliło określić wzajemne ich powiązania i ujawnić istniejące, znaczące korelacje pomiędzy niektórymi z nich. Uznano, że dla kompleksowego scharakteryzowania stanu powierzchni po pneumokulkowaniu wystarczy podać wartości tylko siedmiu parametrów. Są to parametry: Sa, Ssk, Sal, Str, Sp, Ssc oraz STp. Stwierdzono, że pozostałe parametry SGP, jako silnie skorelowane z podanymi, nie muszą być badane po pneumokulkowaniu.
EN
The work is an attempt to identify a representative group of indicators of surface geometric structure (SGS) of the samples finished by pneumatic ball peening (PBP), and being sufficient to fully control of the such surface structures. The tests performed on samples made of an alloy MgAl8ZnMn and peened using VaporBlast device. The analysis of SGS indicators has been performed with TayScan 150 profilometer and TalyMap 3D software. The correlations between twenty-two selected parameters were calculated. It was allowed to determine their mutual relations, and to reveal the existing significant correlations between some of them. It was considered that for a comprehensive characterization of the surface after PBP enough to give the value of only seven parameters. These are the parameters: Sa, Ssk, Sal, Str, Sp, Ssc and STp. It was found that the other parameters of the SGS are strongly correlated with the above mentioned and need not be examined after PBP.
5
Content available remote Wpływ pneumokulkowania na wytrzymałość zmęczeniową elementów z powłokami chromowymi
Dzierwa A.
Zeszyty Naukowe Politechniki Rzeszowskiej. Mechanika
|
2004
|
z. 62 [209]
69--72
PL
W artykule zamieszczono wyniki badań wytrzymałości zmączenieniowej oraz stanu warstwy wierzchniej elementów ze stali 40H pokrytych powłoką chromu galwanicznego o grubości ∼25 µm i obrobionych przez pneumokulkowanie. Stwierdzono, że pneumokulkowanie powłok chromowych może poprawić wytrzymałość zmęczeniową do poziomu zbliżonego, jaki posiadały elementy przed chromowaniem.
EN
The paper presents results of the tests concering fatigue strenght and surface layer condition in relation to specimens made of 40 H steel (coating thickness about 25 µm) and finished by pneumatic ball peening. It has been found that the pneumatic ball peening of chromium coats can improve level of fatigue strenght, in relation to the elements possessed as results of chromium electroplating.
6
Content available remote Wpływ pneumokulkowania na wybrane właściwości stopu MgAl8ZnMn
Żarski T.
Zeszyty Naukowe Politechniki Rzeszowskiej. Mechanika
|
2004
|
z. 62 [209]
427--432
PL
W artykule przedstawiono wyniki badań wstępnych, przeprowadzonych na stopie magnezu MgAl8ZnMn poddanym pneumokulkowaniu. Zbadano wpływ pneumokulkowania na wytrzymałość na rozciąganie oraz mikrotwardość. Badaniom poddano także powierzchnię stopu przez pomiar chropowatości.
EN
The paper presents results of the tests performed on MgAl8ZnMn alloy after bearing ball peening. Bearing ball peening influence on tensile strength and microhardness were tested. Surface roughness tests were performed too.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.