Tribological Studies on AlCrFeCuCoNi High Entropy Alloy Surface Coated on Ti-6Al-4V Using Plasma Transferred Arc Technique

Prabu G., Duraiselvam Muthukannan

Archives of Metallurgy and Materials

|

2022

|

Vol. 67, iss. 2

409--420

EN

AlCrFeCuCoNi high entropy particles were alloyed on Ti-6Al-4V surface using Plasma transferred arc (PTA) process. PTA alloyed surfaces were investigated for their phase formation, microhardness improvement and wear behaviour. The various wear mechanism and their corresponding surface roughness were studied. The results revealed that the dual phase of BCC and FCC microstructure along with some intermetallic compounds were grown in the alloyed region through the PTA technique and good metallurgical bonding of the alloyed region with the base material were achieved. The PTA alloyed region exhibited a hardness of 718 HV0.2 which is 2.2 times higher than the hardness of base material. The PTA alloyed samples showed higher wear resistance due to the solid solution strengthening as the HEA has high entropy of mixing that leads to the reduction of free energy of the alloyed region. It exhibited better interconnection of the coated material and superior metallurgical bonding to the base material. Frictional heat produced during the wear test has promoted the formation of FeO, Cr2O3, CuO, NiO and Al2O3 oxide film on the PTA alloyed sample. These oxide films act as a barrier between two mating surfaces and improve the tribo performance of the PTA alloyed sample.

2

Structural investigation of the Plasma Transferred Arc hardfaced glass mold after operation

Skowrońska Beata, Sokołowski Wojciech, Rostamian Reyhaneh

Welding Technology Review

|

2020

|

R. 92, nr 3

55--65

EN

The paper presents the results of research aimed at detecting the causes of premature wear of molds for glass shaping, manifesting the formation of pits in the Plasma Transferred Arc pad-welds in which the working surface of the mold was shaped. The weld microstructure was tested, the chemical composition was determined in the pad-weld’s cross-section, linear and surface chemical distributions were made in the pad-weld’s cross-section, the surface morphology in damaged areas, and the chemical composition of surface inclusions were examined. The too high temperature of formed glass associated with wettability of the glass of the mold was indicated as the primary cause of premature mold wear.

PL

W artykule przedstawiono wyniki badań ukierunkowanych na wykrycie przyczyn przedwczesnego zużycia form do kształtowania szkła, objawiające się powstawaniem wżerów w napoinie plazmowej, w której ukształtowano powierzchnię roboczą formy. Przeprowadzono badania mikrostruktury napoiny, określono skład chemiczny w przekroju napoiny, wykonano liniowe i powierzchniowe rozkłady pierwiastków chemicznych w przekroju napoiny, zbadano morfologię powierzchni w obszarach uszkodzonych, zbadano skład chemiczny wtrąceń na powierzchni. Jako podstawową przyczynę przedwczesnego zużycia form wskazano zbyt wysoką temperaturę formowanego szkła powiązaną ze zwilżalnością szkłem formy.

3

Kompozytowe powłoki napawane plazmowo – charakterystyka i otrzymywanie

Bober M.

Przegląd Spawalnictwa

|

2011

|

R. 83, nr 6

43-47

PL

Na podstawie literatury oraz badań własnych w artykule przedstawiono stan wiedzy na temat kompozytowych powłok otrzymywanych metodą napawania plazmowego. Omówiono ogólną charakterystykę napoin kompozytowych oraz mechanizmy ich umocnienia. Przedstawiono też metody otrzymywania napoin kompozytowych z zastosowaniem łuku plazmowego.

EN

The state of the art of coatings deposited by the plasma transferred arc has been presented basing on the literature study and own research. The characterization and strengthening mechanisms of composite overlay formation has been presented. The methods of composite overlay production by the plasma beam have been discussed.