Evaluation of TiN Coating Properties Deposited on HS6-5-2C Steel

Kowalczyk Joanna

Tribologia

2020

nr 3

23--31

The article presents selected properties of TiN coating on HS6-5-2C steel by Physical Vapour Deposition (PVD). The coating thickness was measured with a Calotest, and its hardness was measured with a nanohardness tester. Tribological parameters were determined, namely, the coefficient of friction and linear wear on the TRB3 tester operating in a ball-on-disk sliding friction pair. The disc was made of HS6-5-2C steel with a TiN coating and the ball of 100Cr6 steel without coating and with a-C:H coating, with Al2O3. The tests were performed under technically dry friction conditions. The coating structure observations were made using a scanning microscope, and the analysis of the geometric structure of samples, before and after tribological tests, were performed with an optical profile measurement gauge. The test results showed that the lowest linear wear was obtained for friction pairs with an Al2O3 ball and a steel ball with a-C:H coating applied.

W artykule przedstawiono wybrane właściwości powłoki TiN osadzonej na stali HS6-5-2C techniką fizycznego osadzania z fazy gazowej PVD. Zmierzono grubość powłoki przy użyciu Calotestera oraz jej twardość za pomocą nanotwardościomierza. Określono parametry tribologiczne, a mianowicie współczynnik tarcia i zużycie liniowe na testerze TRB3 pracującym w skojarzeniu trącym kula–tarcza w ruchu ślizgowym. Tarcza wykonana była ze stali HS6-5-2C z powłoką TiN, a kula ze stali 100Cr6 bez i z naniesioną powłoką a-C:H, z Al2O3. Badania wykonano w warunkach tarcia technicznie suchego. Obserwacje struktury powłoki zrealizowano przy użyciu mikroskopu skaningowego, a analizę struktury geometrycznej powierzchni próbek przed i po testach tribologicznych wykonano profilometrem optycznym. Wyniki badań wskazały, że najmniejsze zużycie liniowe uzyskano dla par trących z kulą wykonaną z Al2O3 oraz stalową z naniesioną powłoką a-C:H.

Examination of Selected Thermal Properties of Basalt Composites

Miśkiewicz Pamela, Frydrych Iwona, Makówka Marcin

Fibres & Textiles in Eastern Europe

2020

Vol. 28, no. 2 (140)

103--109

A composite based on basalt fabric was produced because of its good thermal and mechanical properties. As a result of the reactive magnetron sputtering technique, a layer of aluminium and zirconium (IV) oxide 200 nm thick was deposited on Mylar film, which was adhered to the surface of the basalt fabric using a special adhesive glue and silicone. The variants of composites prepared were subjected to contact resistance tests at a contact temperature of 100 °C and 250 °C, as well as to resistance to thermal radiation tests. The tests carried out on the composites obtained showed an improvement of tested parameters.

W pracy wytworzono kompozyt na bazie tkaniny bazaltowej ze względu na jej dobre właściwości termiczne i mechaniczne. W wyniku zastosowania techniki reaktywnego rozpylania magnetronowego na folii Mylar osadzono warstwę aluminium i tlenku cyrkonu o grubości 200 nanometrów, którą przyklejono na powierzchnię tkaniny bazaltowej poprzez zastosowywanie kleju oraz silikonu. Przygotowane warianty kompozytów poddano badaniom odporności na ciepło kontaktowe dla temperatury kontaktu 100 °C i 250 °C oraz odporności na promieniowanie cieplne. Przeprowadzone na kompozytach badania wykazały poprawę badanych parametrów.