Authors present a short review of selected natural-origin zeolite materials. This article discusses the structure, classification and ability to modify natural zeolites, along with examples of their potential applications as adsorbents or catalysts.
PL
Autorzy przedstawili krótki przegląd wybranych materiałów zeolitowych pochodzenia naturalnego. W artykule omówiono strukturę, klasyfikację i możliwości modyfikacji naturalnych zeolitów, wraz z przykładami ich potencjalnych zastosowań jako adsorbentów lub katalizatorów.
The removal of Cr(VI) from aqueous solutions was investigated using clinoptilolite and phillipsite-chabazite rich tuffs. These minerals were modified using hexadecyltrimethyl – ammonium bromide (HDTMA-Br) and used for Cr(VI) ions removal. The physicochemical characteristics of zeolitic minerals were revealed by XRD, XRF, BET and FT-IR techniques. The uptake capacities of modified zeolites were compared in batch sorption experiments. To predict the sorption isotherms and to determine the characteristic parameters for process design, three isotherm models the Freundlich, the Langmuir, and the Bilangmuir, were applied to experimental data. The data obtained reveal homogeneous Cr(VI) sorption on one kind of active sites on PC-HDTMA surface and heterogeneous sorption on two kinds of active sites on CL-HDTMA surface.
W artykule zbadano możliwość wykorzystania popiołów lotnych klasy C (otrzymywanych w wyniku spalania węgla brunatnego w kotle pyłowym) i F (otrzymywanych w wyniku spalania węgla kamiennego metodą konwencjonalną) jako substratów do syntezy materiału zeolitowego z grupy filipsytu. W tym celu przeprowadzono szereg syntez hydrotermalnych z wykorzystaniem reagentów takich jak wodorotlenek sodu (NaOH) oraz bromek tetrapropyloamoniowy (TPABr). W wyniku reakcji otrzymano docelowy materiał zeolitowy, zarówno z popiołu klasy C, jak i F. Otrzymane produkty syntezy, jak też popiołowe substraty reakcji, poddano charakterystyce chemicznej i mineralogicznej. Badania wykazały, że popiół lotny powstały z węgla brunatnego i kamiennego może być substratem w reakcjach syntez zeolitu, jakim jest filipsyt. Analiza porównawcza dyfraktogramów rentgenowskich produktów z obu typów popiołów wykazała, że lepszym substratem jest popiół klasy C otrzymywany w wyniku spalania węgla brunatnego w kotle pyłowym (w reakcji syntezy otrzymano lepiej wykształcone formy zeolitowe). W pracy dokonano także analizy literaturowej potencjalnych kierunków zastosowania filipsytu w inżynierii i ochronie środowiska. Na podstawie zweryfikowanych danych stwierdzono, iż dalszym kierunkiem badań będzie analiza możliwości wykorzystania otrzymanych materiałów jako potencjalnych sorbentów amoniaku.
EN
The study examined the possibility of using class C fly ash (obtained as a result of brown coal combustion in a pulverized-fuel boiler) and class F (obtained as a result of conventional coal combustion) as substrates for the synthesis of zeolitic material from the phillipsite group. For this purpose, a series of hydrothermal syntheses were carried out using reagents such as sodium hydroxide (NaOH) and tetrapropylammonium bromide (TPABr). As a result of the reaction, the target zeolite material was obtained from both class C and F fly ash. The obtained synthesis products as well as the ash reaction substrates were subjected to chemical and mineralogical characterization. The studies have shown that fly ash formed from brown coal and hard coal may be a substrate in zeolite synthesis reactions to obtain phillipsite. A comparative analysis of X-ray diffractograms of products from both types of ash showed that class C ash obtained as a result of brown coal combustion in a pulverized-fuel boiler is a better substrate (in the synthesis reaction better-formed zeolites were obtained). The article also includes a literature analysis on the potential applications of phillipsite in engineering and environmental protection. Based on the verified data, it was found that the further direction of the research will be the analysis of the possibilities of using the obtained materials as potential ammonia sorbents.
4
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Polish clay material was used as an initial material for synthesis of the FAU type zeolite Y. For clay pre-synthesis preparation was adopted technique of its thermal activation in the temperature range 600-800°C. The temperature of clay material activation and the crystallization time of reaction mixtures on its basis were selected as the most important factors which strongly determined zeolite-formation process and their influence on zeolite Y synthesis was primary investigated. Performed complex investigations for establishment of qualitative and quantitative parameters of zeolitical probes synthesized in the reaction mixture of molar composition Na2O:Al2O3:SiO2:H2O= 5:1:10:200 and additional amount of NaCl (NaCl/Al2O3=2). Powder XRD analysis applied for phase identification and quantitive analysis, confirm increasing of zeolite Y amount up to 53 and 58% for materials synthesized during 48 hours from reaction systems on basis of clay material burned at 600 and 700°C, respectively. Results of XRD analysis correspond with experimental data of gravimetrical analysis on solid part of reaction mixture (losses of ignition and relative mass grow) and determination of residual Na2O in liquid phase. With help of home-made installation confirmed fine adsorptive properties of obtained zeolite powders for dynamic removal of acetone from air. Established, that adsorption effectivity of tested materials is strongly related with amount of zeolite phase in the investigated powders and reaches maximal values in the range of 100-105 mg/g for probes after 48 hours of crystallization in cases of clay material activation 600 and 700°C.
PL
Celem badań była synteza zeolitu typu Y z naturalnego materiału ilastego pochodzącego z Polski. Prawidłowy przebieg procesu krystalizacji wymagał wstępnej aktywacji termicznej surowego materiału ilastego w temperaturach z zakresu 600-800°C. Ustalono że temperatura aktywacji termicznej materiału wyjściowego oraz czas krystalizacji mieszanin reakcyjnych są najważniejszymi parametrami wpływającymi na przebieg procesu syntezy zeolitu, dlatego skupiono się na optymalizacji tych parametrów. Na podstawie badań wstępnych przyjęto następujący skład molowy mieszanin reakcyjnych Na2O: Al2O3: SiO2: H2O = 5: 1: 10: 200. Wprowadzono dodatkowo NaCl, w takiej ilości że stosunek molowy NaCl/Al2O3 wynosił 2. Przeprowadzono szereg badań w celu wyznaczenia parametrów ilościowych oraz jakościowych zsyntezowanych próbek. Analiza XRD stosowana do identyfikacji faz oraz ich analizy ilościowej, wykazała zawartość zeolitu typu Y w zsyntezowanych próbkach w ilości 53 i 58% odpowiednio dla materiałów aktywowanych w 600 i 700°C, których czas krystalizacji wynosił 48h. Wyniki analizy XRD pokryły się z innymi wykonanymi analizami, tj.: oznaczeniem straty po prażeniu, względnego wzrostu masy produktu oraz stężenia Na2O w roztworze poreakcyjnym. Przy wykorzystaniu specjalnie przygotowanej instalacji laboratoryjnej wyznaczono pojemność adsorpcyjną materiałów względem acetonu. Ustalono, że efektywność adsorpcji jest ściśle związana z ilością fazy zeolitowej w próbkach. Najwyższą pojemności adsorpcyjne wynoszące 100 – 105 mg/g uzyskano dla próbek krystalizowanych przez 48h, których temperatura aktywacji wynosiła 600 i 700°C.
Several minerals from zeolite group have been found in Rębiszów basaltoid deposits: gobbinsite, natrolite, gismondine, garronite, thomsonite and phillipsite. For the first time gobbinsite has been recognized in basaltoids from Lower Silesia. Moreover, a new phase has been distinguished on the basis of some determined parameters (such as calculation of chemical formulae and X-ray diffraction patterns), belonging to zeolite group and occurring together with other zeolites. Origin of the whole assemblage of zeolite minerals can be related to hydrothermal activity of post-magmatic solutions within thermal contraction cracks of congealing basaltoid lava.