Determination of Phase Transformation Temperatures by Dilatometric Test of S960MC Steel

Málek M., Mičian M., Moravec J.

Archives of Foundry Engineering

|

2021

|

Vol. 21, iss. 2

57--64

EN

The phenomenon of “soft zone” is occurring in the heat affected zone (HAZ) of high strength low alloy (HSLA) steels. Therefore, the process of weld metal solidification and phase transformation in HAZ is essential to understand the behaviour of the material, especially in the case where welded joints are debilitating part of the construction. The simulation program SYSWELD is powerful tool to predict solidification and phase transformation of welding joint, what correspond to the mechanical properties of the joints. To achieve relevant results of the simulation, it is necessary to use right mathematic-material model of the investigated material. Dilatometric test is the important methods to gather necessary input values for material database. In this paper is investigated physical and metallurgical properties of S960MC steel. The dilatometric curves were carried out on the laboratory machine dilatometer DIL 805L. In addition to determination of the phase transformation temperatures at eight levels of the cooling rate, the microstructure and hardness of the material are further analysed. The hardness of the samples reflects the achieved microstructure. Depending on the cooling rate, several austenitic transformation products were observed such as pearlite, bainite, martensite and many different ferritic microstructures. The differences between the transformation temperature results using the first derivation method and the three tangent method are up to 2%. The limit cooling rate was set at value 30°C/s. The microstructure consists only of bainite and marten site and the hardness reaches a value of 348HV and higher.

2

Wpływ udziału masowego segmentów na właściwości termiczne termoplastycznych elastomerów eterowo-estrowych

Piesowicz E., Irska I., Rosłaniec Z.

Inżynieria Materiałowa

|

2015

|

Vol. 36, nr 6

552--556

PL

Wzrastające ciągle zainteresowanie konstrukcyjnymi materiałami polimerowymi sprawia, że stawia się im coraz większe wymagania w zakresie ich właściwości użytkowych, m.in. dobre właściwości mechaniczne w niskiej i podwyższonej temperaturze. Warunki takie dobrze spełnia grupa poliestrów, w tym niedawno wyodrębnione kopolimery. Na szczególną uwagę zasługują kopolimery poliestrowe zawierające segmenty poli(tereftalanu butylenu) (PBT), poli(tereftalanu etylenu) (PET) i poliestru kwasu 2,6-naftalano-dikarboksylowego z glikolem etylenowym (PEN). Ich dobre właściwości mechaniczne i termiczne, odporność chemiczna i specyficzne właściwości barierowe sprawiają, że znalazły wiele zastosowań szczególnie w przemyśle opakowaniowym. Ciekawymi właściwościami charakteryzują się blokowe kopolimery estrowo-eterowe. Jeżeli długość bloków i różnice we właściwościach fizycznych między nimi są duże, to kopolimery wykazują wówczas strukturę heterofazową. W wyniku przeprowadzonych syntez otrzymano serię 16 polimerów różniących się udziałem masowym sekwencji PTMO (20, 40, 50 i 60% mas.) oraz proporcją molową sekwencji tereftalanowych do naftalanowych w bloku poliestrowym wynoszącą odpowiednio: 100/0; 60/40; 40/60; 0/100% mol. Wzór ogólny otrzymanych polimerów przedstawia rysunek 3. Materiały scharakteryzowano za pomocą różnicowej kalorymetrii skaningowej DSC. Określono również podstawowe właściwości fizyczne polimerów. Badania wykonane metodą różnicowej kalorymetrii skaningowej umożliwiły określenie wpływu udziału PTMO oraz sekwencji EN i ET na przemiany fazowe zachodzące w strukturze otrzymanych materiałów, tj.: na temperaturę topnienia, krystalizacji i zeszklenia fazy zawierającej sekwencje poliestrowe (twardej) oraz PTMO (miękkiej).

EN

The increasing interest in structural constantly polymeric materials makes it places them higher and higher requirements for their performance, including good mechanical properties at low and elevated temperature. Conditions such good meets a group of polyesters, including relatively recently separated copolymers. Particular attention should be paid copolymers containing polyester segments of poly(butylene terephthalate) (PBT), poly(ethylene terephthalate) (PET) and polyester of 2,6-naphthalene dicarboxylic acid with ethylene glycol (PEN). Their good mechanical and thermal properties, chemical resistance and specific barrier properties makes it found a variety of uses particularly in the packaging industry. Interesting properties of block copolymers are characterized by ester-ether. If the length of the blocks and the physical differences between them are large, the copolymers have the structure of the heterophasic. As a result of the synthesis of 16 to give a series of polymers with different weight fraction sequence PTMO (20, 40, 50 and 60 wt %) and the molar ratio of terephthate to naphthalate sequence in block polyester of: 100/0, 60/40, 40/60, 0/100 mol %, respectively. The general formula of the polymers obtained are shown in Figure 3. The materials were characterized using the method of differential scanning calorimetry DSC. Also determined the basic physical properties of polymers. Tests carried out by differential scanning calorimetry possible to determine the effect of PTMO share sequence and EN and ET on the phase transformations in the structure of the materials obtained, i.e.: melting point, crystallization and glass transition phase containing sequences polyester (rigid) and PTMO (soft).

3

Wpływ szybkości grzania i chłodzenia na temperatury przemian fazowych w stopie magnezu EL 21

Przeliorz R.

Rudy i Metale Nieżelazne

|

2013

|

R. 58, nr 10

570--574

PL

W artykule przedstawiono wyniki badań dotyczące wpływu szybkości grzania i chłodzenia na wartości temperatur przemian fazowych stopu magnezu EL 21. Szczególną uwagę zwrócono na aspekty kalibracji temperatury oraz szybkość grzania i chłodzenia próbki w kontrolowanej atmosferze. Badania prowadzono w kalorymetrze Multi HTC, firmy Setaram. Próbki nagrzewano do temperatury likwidus z kontrolowaną szybkością 2,5, 5, 10, 15, 20 °C/min. Natychmiast po stopieniu próbki chłodzono z identycznymi szybkościami. Równowagowe temperatury przemian fazowych zostały obliczone przez ekstrapolację do zerowej szybkości grzania/chłodzenia. Na krzywych grzania i ochładzania stwierdzono znaczną różnicę pomiędzy wartością temperatury topnienia (przy nagrzewaniu) i krzepnięcia (przy chłodzeniu). Obliczono także ciepło właściwe.

EN

The paper deals with the effects of heating and cooling rate on the values of phase transformation point temperatures of EL 21 magnesium alloy. Particular attention was given to aspects of the measurement including control of the atmosphere, suitable reference materials for temperature calibration, size of the sample and the rate of heating and cooling. Samples taken from alloy were heated with controlled ramp rates 2,5, 5, 10, 15, 20 °C/min and immediately after melting they were cooled with the same controlled ramp rate with the help of calorimeter Setaram Multi HTC. Moreover, the equilibrium transformation temperatures were calculated by extrapolating the measured temperatures to zero heating/cooling rates. It was found out that the effect of the super-cooling on the cooling curves is significant. The specific heat was calculated.

4

Some factors influencing the determination of eutectoid transformation start and finish temperatures in hypoeutectoid steels

Pawłowski B., Bała P., Krawczyk J.

Metallurgy and Foundry Engineering

|

2009

|

Vol. 35, no. 2

121-128

EN

This paper presents problems related to the proper determination of the eutectoid transformation start and finish temperatures in steels during heating. Information from references indicate an essential influence of interlamellar spacing in pearlite on the formation of the dilatation effect related to the eutectoid transformation finish, on dilatometric curves. It was revealed, in this paper, that the appearance of the dilatation effect related to the eutectoid transformation finish in hypoeutectoid steels or its lack in the heating dilatograms depends on the resolution ability of the applied dilatometer.

PL

W artykule przedstawiono problemy związane z prawidłowym określeniem temperatur początku i końca przemiany eutektoidalnej w stalach podczas nagrzewania. Doniesienia literaturowe wskazują na istotny wpływ odległości międzypłytkowej w perlicie na powstawanie efektu dylatacyjnego związanego z zakończeniem przemiany eutektoidalnej na krzywych dylatometrycznych. W niniejszej pracy wykazano, że wystąpienie lub nie na dylatogramie nagrzewania efektu dylatacyjnego od końca przemiany eutektoidalnej w stalach podeutektoidalnych związane jest również ze zdolnością rozdzielczą użytego dylatometru.