Influence of steel-polypropylene fibers on fracture parameters of high performance concrete

Smarzewski P., Barnat-Hunek D.

Biuletyn Wojskowej Akademii Technicznej

|

2016

|

Vol. 65, nr 2

67--79

EN

The purpose of this article is to determine the influence of the type of fibers on fracture parameters of high performance concrete (HPC). In this study there were two types of coarse aggregate used: granite and granodiorite with a grain size of about 2/8 mm. Experimental tests were performed on cubic samples, cylinders and notched beams. In the concrete of FRC type, 0.5 and 0.75% of steel fibers and 0.5 and 0.25% of polypropylene fibers respectively, were added. Mean strengths and standard deviations for compression, splitting tensile strength, mean static modulus of elasticity and mean fracture energy were determined. Experimental studies in the 1st fracture model showed that the HPC without the addition of fibers (C), was characterized by brittleness, and fiber concrete (FRC) was more ductile. Fibers were bridging the cracks during loading, delayed hairline cracks and prevented the notched beams from breaking. The shape of the descending curve of the load-deflection depended on the geometry and mechanical properties and the quantity of the fibers used, and in the case of HPC without fiber, on the type of coarse aggregate. In the case of granodiorite aggregate, better mechanical parameters of concrete were observed.

PL

Celem artykułu jest ustalenie wpływu włókien na parametry pękania betonu wysokowartościowego (HPC). W badaniu zastosowano dwa rodzaje kruszywa grubego: granit i granodioryt frakcji 2/8 mm. Badania doświadczalne wykonano na próbkach sześciennych, walcach i belkach z nacięciem. W betonie typu FRC dodano odpowiednio 0,5 i 0,75% włókien stalowych oraz 0,5 and 0,25% włókien polipropylenowych. Ustalono średnie wytrzymałości i odchylenia standardowe przy ściskaniu, rozciąganiu przez rozłupywanie, średnie statyczne moduły sprężystości i średnią energię pękania. Badania doświadczalne I modelu pękania pokazały, że HPC bez włókien (C) charakteryzował się kruchością, a fibrobeton (FRC) był bardziej plastyczny. Włókna mostkowały rysy podczas obcią¬żenia, opóźniały powstawanie rys włoskowatych i zapobiegały łamaniu się naciętych belek. Kształt opadającej krzywej obciążenie - ugięcie zależał od geometrii i mechanicznych właściwości oraz ilości zastosowanych włókien, a w przypadku BWW bez włókien od rodzaju kruszywa grubego. W przypadku kruszywa granodiorytowego obserwowano lepsze parametry mechaniczne betonu.

2

The effect of ball type in fine particles grinding on kinetic breakage parameters

Umucu Y., Deniz V.

Inżynieria Mineralna

|

2015

|

R. 16, nr 1

197--203

EN

In the study, the effect of different grinding media on breakage parameters was investigated. Ceramic and steel balls were used as the grinding media. It was observed that the grinding of ignimbrite obeyed first-order breakage kinetics law in the case of ceramic and steel balls. Breakage rates were higher for steel ones comparing to ceramic balls. Furthermore, it was found that the primary breakage distribution function depends on the feed size (i.e., non-normalized), and depends on the different grinding media. The effect of grinding time on the product particle size distribution has also been investigated.

PL

W niniejszych badaniach sprawdzono wpływ różnych mediumów mielących na parametry pękania. Jako mediumy mielące użyto kule ceramiczne i stalowe. Zaobserwowano, że w przypadku kul ceramicznych i stalowych mielenie ignimbrytu było zgodne z kinetycznym prawem pękania pierwszego rzędu. Wskaźniki pękania w przypadku kul stalowych były wyższe w porównaniu do kul ceramicznych. Ponadto odkryto, że podstawowa funkcja rozkładu pęknięć zależy od rozmiaru zasilenia (tzn. nieznormalizowanego) i od różnego medium rozdrabniającego. Sprawdzono również wpływ czasu rozdrabniania na rozkład rozmiaru cząsteczek.

3

Evaluation of fracture parameters for crack problems in fgm by a meshless method

Sladek J., Sladek V., Zhang C., Tan C.-L.

Journal of Theoretical and Applied Mechanics

|

2006

|

Vol. 44 nr 3

603-636

EN

A meshless method based on the local Petrov-Galerkin approach is proposed for crack analysis in two-dimensional (2D), anisotropic and linear elastic solids with continuously varying material properties. Both quasi-static thermal and transient elastodynamic problems are considered. For time-dependent problems, the Laplace transform technique is utilized. The analyzed domain is divided into small subdomains of circular shapes. A unit step function is used as the test function in the local weak form. It leads to Local Integral Equations (LIE) involving a domain-integral only in the case of transient dynamic problems. The Moving Least Squares (MLS) method is adopted for approximating the physical quantities in the LIE. Efficient numerical methods are presented to compute the fracture parameters, namely, the stress intensity factors and the T-stress, for a crack in Functionally Graded Materials (FGM). The path-independent integral representations for stress intensity factors and T-stresses in continuously non-homogeneous FGM are presented.

PL

Przedstawiono bezsiatkową metodę analizy szczelin opartą na podejściu Petrova-Galerkina dla dwuwymiarowych liniowo-sprężystych i anizotropowych ośrodków o zmieniających się własnościach materiałowych. Rozważono zarówno kwazistatyczne problemy naprężeń cieplnych, jak i zagadnienia elastodynamiki, w których zastosowano aparat transformacji Laplace'a. Badany obszar podzielono na małe podobszary kołowe. Jako funkcję testową w lokalnej, słabej postaci zastosowano jednostkową funkcję schodkową, co prowadzi do lokalnych równań całkowych (LIE). Metodę ruchomych najmniejszych kwadratów (MLS) zastosowano do przybliżenia wielkości fizycznych w LIE. Przedstawiono efektywne metody numeryczne wyznaczania parametrów pękania, a w szczególności współczynników koncentracji naprężeń oraz naprężeń T dla szczelin w materiałach funkcjonalnie gradientowych (FGM). Przedstawiono niezależne od drogi całkowania reprezentacje tych parametrów w materiałach FGM o kontynualnie zmieniającej się niejednorodności.

4

Wybrane aspekty identyfikacji stanu mechanicznego połączeń spajanych

Ranatowski E.

Zeszyty Naukowe. Mechanika / Akademia Techniczno-Rolnicza w Bydgoszczy

|

1999

|

Z. 44 (221)

91-107

PL

W artykule przedstawiono relację: struktura - własności mechaniczne, dla heterogenicznych połączeń spajanych w oparciu o zmodyfikowane rozwiązanie Prandtla. Wykonano ocenę stanu naprężenia [sigma...] dla i, k = x, y w sąsiedztwie powierzchni kontaktowej dla stref o obniżonej i podwyższonej wytrzymałości. Dokonano również oceny parametru S[p], jako fizycznej miary deformacji i wytężenia niejednorodnego złącza oraz parametru K[w], jako skutku oddziaływania więzów mechanicznych. W dalszej kolejności wykorzystano parametr K[w] do oceny parametrów procesu pękania, określając delta[R] = delta[...].

EN

In this paper was presented the relation between structure and mechanical properties of the heterogenous weld joints with used a modified Prandtl solution. An analysis was made of stress sigma[sub ik], i k = x, y at interface for the cases of perpendicular and nonperpendicular orientation of the zones relative to the loda action under tension. Conclusion from stress analysis form a stress state parametr S[sub p] as a physical measure of the deformation and effort of the mismatched weld joint and constraint factor K[sub w]. Futhermore, form some basic for application of the constraint factor K[sub w], to an assessment of the fracture parametr delta[sub R] = delta[...].