Some aspects of continuous casting of low carbon microalloyed steels with niobium and titanium

Derda W., Wiedermann J.

Archives of Metallurgy and Materials

|

2012

|

Vol. 57, iss. 1

303-310

EN

An analysis of the causes of transverse corner and surface crack formation during continuous casting of low carbon niobium and titanium-containing steel into square billets is presented in this paper. Using X - ray analysis method, the chemical composition of non- metallic phases inside corner cracks was determined. The temperature ranges of the occurrence of nitrides and carbonitrides of Nb, Ti and Al were established using FactSage 6.2., a commercial computer program. The need for the precise selection of cooling conditions during casting of billets both in the mould and in spray cooling regions was pointed out with the aim of obtaining the optimum surface, and particularly corner temperature of the billet before its entrance to the straightening stand.

PL

W referacie przedstawiono na podstawie badań w warunkach przemysłowych, analizę przyczyn powstawania pęknięć na powierzchni i na narożach wlewków ciągłych o przekroju kwadratowym, odlewanych ze stali niskowęglowych z zawartością niobu i tytanu. Przy użyciu metody mikroanalizy rentgenowskiej dokonano oceny składu chemicznego faz niemetalicznych występujących wewnątrz pęknięć. Z wykorzystaniem programu komputerowego FactSage 6.2 wyznaczono zakresy temperatury występowania azotków i węglikoazotków Nb, Ti, Al. Wskazano na konieczność precyzyjnego doboru warunków chłodzenia odlewanych stali w krystalizatorze oraz w strefie chłodzenia natryskowego celem uzyskania optymalnej temperatury wlewka ciągłego w szczególności na narożach przed operacją jego prostowania w klatce walców ciągnąco - prostujących.

2

Wpływ parametrów odlewania na strukturę pierwotną i jakość wlewków ze stopu Ti-48Al-2Nb-2Cr

Chrapoński J., Mikuszewski T.

Inżynieria Materiałowa

|

2003

|

R. XXIV, nr 6

667-670

PL

W pracy przedstawiono wpływ temperatury odlewania oraz temperatury i materiału form odlewniczych na strukturę pierwotną i jakość wlewków ze stopu Ti-48Al-2Nb-2Cr. W badaniach wykorzystano formy metalowe, grafitowe i ceramiczne. Odlewanie prowadzono do form o temperaturze 293 i 773 K. Jakość wlewków oceniono określając rodzaj, wielkość, kształt i rozmieszczenie defektów skurczowych. Określono również rodzaj i zasięg stref krystalicznych. Metodami metalografii ilościowej określono wielkość ziarna wlewków. W wyniku przeprowadzonych badań stwierdzono, że przy odpowiednim doborze parametrów opracowana technologia wytapiania i odlewania umożliwia uzyskanie wlewków o jednorodnej strukturze, złożonej z drobnych ziaren równoosiowych. Prawidłowy dobór parametrów odlewania pozwala również na ograniczenie we wlewkach wielkości i głębokości zalegania defektów skurczowych, co wydatnie zwiększa uzysk metalu.

EN

The effect of casting temperature as well as temperature of moulds on primary structure and quality of ingots made of Ti-48Al-2Nb-2Cr alloy has been presented. The moulds made of metal, graphite and ceramic have been used. Casting was carried out into cold moulds (293 K) and heated to 773 K. The ingots quality was evaluated by examination of type, size, shape and distribution of shrinkage defects. The type and area of different crystal zones was also examined. The grain size of ingots was established by quantitative metallography methods. It was concluded that at appropriate selection of parameters the presented technology ensured obtaining ingots with homogeneous, equiaxed fine grains structure. The proper selection of cast parameters enables limitation of size and location depth of shrinkage defects, which considerably increases the metal's yield.

3

Ciągłe odlewanie stali szynowych w Hucie Katowice

Kasprowicz J., Liszka S., Kuna J., Oleksiak R.

Hutnik, Wiadomości Hutnicze

|

2003

|

Vol. 70, nr 8-9

319--327

PL

W artykule przedstawiono wybrane elementy procesu przygotowania i odlewania stali szynowych decydujące o jakości i własnościach szyn podczas ich eksploatacji w torze. Zidentyfikowano problemy technologiczne i jakościowe, jakie mogą wystąpić w procesie ciągłego odlewania stali szynowych oraz zaprezentowano sposoby przeciwdziałania negatywnym zjawiskom. Podkreślono znaczenie, jakie dla gotowego wyrobu mają: właściwa makrostruktura wlewka ciągłego (pozbawiona defektów wewnętrznych typu pęknięcia, pęcherze i nadmierna segregacja pierwiastków) oraz stosowanie odpowiednio dobranych parametrów odlewania stali szynowych w krystalizatorze i strefie wtórnego chłodzenia (temperatura odlewania, typ zasypki izolująco-smarującej, ułożenie i stan rolek prowadzących pasmo, stan techniczny chłodnicy wtórnej). W artykule określono również wymagania, jakie muszą spełnić współcześnie produkowane szyny i których dotrzymanie jest warunkiem koniecznym dla obecności firmy na rynkach szynowych.

EN

Selected elements of liquid rail steel preparation and casting influencing quality and properties of rails during their exploitation are presented in this paper. Some technological and quality problems which may occur during continuous casting as well as means of counteraction were identified. Attention was drawn to such elements influencing the final product as: proper con cast ingot macrostructure (without internal defects of cracks type, pinholes, pulls and elements segregation), parameters in a mould and in a zone of secondary cooling (casting temperature, type of mould powder, position and wear of guiding rolls, technical condition of secondary cooler). Some requirements for contemporary produced rails which are necessary to be fulfilled if a company wants to be present in rail markets are also described.