Zastosowanie metody PAW do napawania odlewów precyzyjnych

Łyczkowska Katarzyna

Stal, Metale & Nowe Technologie

|

2021

|

nr 7-8

76--79

PL

W pracy zostały przedstawione wyniki badań metalograficznych napoin wykonanych metodą PAW na stopie Inconel 713C. Dokonano analizy makroi mikrostruktury napoiny, strefy wpływu ciepła oraz materiału rodzimego. Analizy strukturalne z obszarów napoin wykazują, że badany materiał należy zaliczyć do trudno spawanych. W każdej napoinie ujawnione zostały pęknięcia w strefie wpływu ciepła oraz na linii wtopienia, gdzie kryształy napoiny krystalizowały na nadtopionych ziarnach.

EN

The paper presents the results of metallugraphic tests of padding welds made with the PAW method on the Inconel 713C alloy. An analysis of the macro- and microstructure of the padding weld, the heat-affected zone and the parent material is carried out. Structural analyses of the padding weld areas demonstrate that the tested material should be classified as difficult to weld. Cracks in the heat-affected zone and on the fusion line, where the padding weld crystals crystallised on the melted grains, were revealed in each padding weld.

2

Laserowa modyfikacja struktury i właściwości wybranych gatunków stali

Popławski M., Piasecki A., Marchewka M.

Inżynieria Materiałowa

|

2013

|

Vol. 34, nr 6

798--801

PL

W pracy przedstawiono wyniki badań nad wpływem parametrów pracy lasera Star Weld Select na mikrostrukturę trzech wybranych stali. Do badań użyto stal węglową 1.0037, stal narzędziową stopową 1.2343 oraz stal austenityczną 1.4301. Zróżnicowanie składu chemicznego badanych materiałów miało istotny wpływ na zmiany mikrostruktury uzyskane pod wpływem działania lasera. Dokonano miejscowego przetopienia oraz wykonano napoiny na powierzchni próbek. Stwierdzono, że gęstość mocy lasera i gatunek obrabianego materiału podłoża ma wpływ na możliwe do uzyskania utwardzenie materiału podłoża, jak i twardość uzyskanej napoiny. Zastosowanie mniejszej gęstości mocy i większej średnicy drutu do napawania skutkuje uzyskaniem mniejszej twardości oraz większej grubości wytworzonej strefy przetopu. Napoiny wytworzone na stali austenitycznej i niskowęglowej konstrukcyjnej charakteryzują się podobnym poziomem twardości. Natomiast wykonanie miejscowego przetopienia stali austenitycznej nie wpłynęło na zmianę jej twardości, niezależnie do warunków pracy lasera. Na podstawie mikroanalizy składu chemicznego metodą EDS stwierdzono, że zastosowanie mniejszej gęstości mocy wpływa na ujednorodnienie składu chemicznego w miejscu przejścia napoiny do materiału rdzenia.

EN

The study shows the results of research on the influence of working parameters of the Star Weld Select laser on the microstructure of three selected steels. Carbon steel 1.0037, alloy tool steel 1.2343 and austenitic steel 1.4301 were used in the experiment. The diversification of composition of researched materials had a significant influence on the change of microstructure obtained as a result of laser action. Local remelting as well as padding welds were applied on the surface of the samples. It was observed that the power density value as well as the type of the base material being worked on, have an influence on the obtained hardening of the base material and the hardness of the obtained padding weld. The application of lower power density and bigger diameter of padding weld wire results in obtaining lower hardness and bigger thickness of the produced remelting zone. Padding welds produced on the austenitic and low-carbon constructional steel are characterized by similar level of hardness. Local remelting of austenitic steel, however, did not influence the hardness, regardless of the laser working conditions. On the basis of the microanalysis of chemical composition with EDS method, it was found out that the application of lower power density increases the homogeneity of chemical composition in the area of transition of the padding weld into the base material.

3

Badania odporności na ścieranie warstw napawanych i stali narzędziowych na matryce kuźnicze

Turek J., Okoński S., Piekoszewski W.

Obróbka Plastyczna Metali

|

2012

|

T. 23, nr 1

39-44

PL

W artykule przedstawiono wyniki badań odporności na zuSycie ścierne stali narzędziowych do pracy na gorąco X37CrMoV5-1 i 55NiCrMoV7 i warstw napawanych materiałami UTOP-38, F-812 i F-818. Badania wykonano na urządzeniu T11 produkcji ITE Radom w temperaturze 250 oC. Najlepsze wyniki uzyskano dla stali X37CrMoV5-1 i 55NiCrMoV7 oraz dla materiału F-818.

EN

The article features an analysis of the resistance to abrasive wear of X37CrMoV5-1 and 55NiCrMoV7 hot-work tool steels and of padding welds overlaid with UTOP-38, F-812 and F-818 materials. The analysis was conducted at the temperature of 250 oC on the T11 testing machine produced by ITE Radom. The best outcome was achieved for X37CrMov5-1 and 55NiCrMoV7 steels and for F-818

4

Optymalizacja doboru napoin w ujęciu materiałoznawczym

Napiórkowski J., Pękalski G., Sachadel U.

Zeszyty Naukowe. Elektryka / Politechnika Opolska

|

2002

|

Vol. 280, z. 51

519-524

PL

W wielu urządzeniach energetycznych nezbędną cechą jest wysoka odporność na zużywanie ścierne. Często w takich przypadkach wykorzystuje się napawanie elektrodami o złożonym składzie chemicznym. W pracy przedstawiono wyniki badań dotyczące siedmiu z kilkudziesięciu rodzajów elektrod, które poddano badaniom metalograficznym. Wyniki tych badań uzupełniono o laboratoryjne próby odporności na zużywanie ścierne. Zaproponowano sposób oceny wybranychcech napoin prowadzący do optymalizacji ich trwałości eksploatacyjnej.

EN

Essential feature of many devices is a high abrasive resistance. To achieve such an feature, it is necessary to use a pad welding equipped with electrodes of complex chemical constitution. The work present results of research concerning seven selected electrodes which were put to metallographic tests. Moreover, there were carried out laboratory tests of abrasion resistance. The paper consists also a suggested assessment of padding weld's qualities, enabling an optimization of their operating durability.