Subcritical crack growth of alumina matrix ceramics

Szutkowska M., Boniecki M., Pędzich Z., Bućko M.

Inżynieria Materiałowa

2006

Vol. 27, nr 3

658-661

The ”load-relaxation technique” was used for determination of relationship of stress intensity factor versus crack growth velocity. The single-edge-notched specimens (SENB) in three-point bending test were used. The crack length after relaxation ck, stress intensity factor at the moment of crack growth initiation KI0, parameters of the subcritical crack growth n and log A, maximum values of stress intensity factor KImax and work of fracture (WOF) were determined. A study of subcritical crack growth of Al2O3 -10 wt% ZrO2 with 12 mol% CeO2 stabilized ZrO2 nanoparticles ceramics was carried. For comparison the results of subcritical crack growth (SCG) test of Al2O3 -10 wt% ZrO2 with unstabilized ZrO2 were presented as well.

Do wyznaczenia zależności współczynnika intensywności naprężeń KI od prędkości wzrostu pęknięcia zastosowano metodę „obciążeniowo-relaksacyjną”. Zastosowano próbki typu SENB w kształcie belki z karbem. Wyznaczono długość pęknięcia po relaksacji ck współczynnik intensywności naprężeń, przy którym rozpoczyna sie rozwój pęknięć podkrytycznych KI0, wartość maksymalną współczynnika intensywności naprężeń KImax parametry wzrostu pęknięć podkrytycznych n i log A, oraz prace pękania WOF. Badania przeprowadzono dla spieku ceramicznego Al2O3-10% masy ZrO2 z dodatkiem nanocząstek ZrO2 stabilizowanego 12 mol.% CeO2. Dla porównania przedstawiono wyniki uzyskane z badań podkrytycznego wzrostu pęknięć dla spieku ceramicznego Al2O3-10% masy ZrO2 z dodatkiem ZrO2 niestabilizowanego.