1
Content available remote An estimation of the high-pressure pipe residual life
Jovicic G., Nikolic R., Zivkovic M., Milovanovic D., Jovicic N., Maksimovic S., Djordjevic J.
Archives of Civil and Mechanical Engineering
|
2013
|
Vol. 13, no. 1
36--44
EN
The paper presents an estimation of the residual life of the power plant high-pressure pipe, which has been in exploitation for years. A crack was noticed in the pipe, thus it was necessary to estimate the pipe material residual life until its eventual failure. The combined methodology for residual life estimation, which consists of experimental and numerical investigations, was developed. The samples were taken directly from the real high pressure pipe and material properties were determined experimentally, both at room and elevated (operational) temperature. The experimental results also served for the verification of the developed numerical methodologies. The FEM and the X-FEM methods were used for the residual life numerical estimation of the high pressure pipe. The stress and strain fields, used for the estimate, were obtained by application of the Paris' law. The final verification of numerical results was realized by comparing the critical crack length to the experimentally obtained value.
2
Wrzenie na poziomym pęku rur gładkich i z powłoką porowatą. Część 1
Krasowski K., Cieśliński T.
Technika Chłodnicza i Klimatyzacyjna
|
2011
|
nr 1
5-16
PL
Artykuł poświęcony problematyce badań doświadczalnych procesu wrzenia wybranych cieczy roboczych na poziomym pęku rur gładkich i rur z powłoką porowatą. W jego części pierwszej na wstępie podane zostały parametry opisujące proces wrzenia na poziomym pęku rur, a następnie autorzy dokonują przeglądu wybranych wyników badań eksperymentalnych wielu autorów, najpierw w odniesieniu do procesu wrzenia na pęku rur gładkich, a następnie rur o powierzchni rozwiniętej i rur pokrytych powłoką porowatą. Końcowa część publikacji poświęcona jest zagadnieniu modelowania wrzenia na interesującym autorów pęku rur. Część druga artykułu zawierać będzie prezentację własnych wyników badań autorów wraz z opracowanymi na ich podstawie korelacjami
EN
Experimental investigations of pool boiling of selected fluids on horizontal bundles of plain tubes and porous coated tubes are described. In the first part of the paper the parameters of pool boiling on horizontal tube bundle are defined and selected published results of boiling tests on bundles of plain, enhanced and porous coated tubes are presented. Models of pool boiling on horizontal tube bundle are discussed. In the second part the original test results and own correlations will be given
3
Content available remote Szybki rozwój pęknięcia rury z polietylenu z wadą zewnętrzną i jej lokalne odkształcenie
Baranowski W., Werner K.
Przetwórstwo Tworzyw
|
2011
|
[R.] 17, nr 3
108-112
PL
W artykule analizowano wpływ wad wzdłużnych (szczelin) na powierzchni rur wykonanych z polietylenu, stosowanych do budowy sieci gazowych i wodociągowych, na możliwość szybkiej propagacji pęknięć oraz na wzrost lokalnego odkształcenia na czole szczeliny. Takie wady mogą powstawać w procesie wytłaczania oraz podczas transportu, składowania i montażu rur. Dla założonych wymiarów szczeliny obliczono współczynnik intensywności naprężenia, który porównano z jego wartością krytyczną dla materiału rury w celu określenia krytycznych wymiarów szczeliny ze względu na pękanie. Określono też wielkość spiętrzenia naprężenia rozciągającego na czole wady i wzrost lokalnego odkształcenia jako wynik pełzania materiału. Wyniki obliczeń przedstawiono na wykresach, na podstawie których można określić bezpieczny stan rury z wadą.
EN
In paper the influence of longitudinal defects (the fissures) on surface of pipes made from polythene, applied to building of gas and water pipelines on possibility rapid cracking as well as on the growth of local strain on forehead the fissure were analyzed. Such defects can to come into being both in extrusion process how and during transportation, storing and the assembly of pipes. It the value of stress intensity factor for received dimensions of fissure was counted and it was compared with his critical value for material of pipe in aim of qualification of critical dimensions fissure with regard on cracking. It the size of piling up the tension stress on fissure forehead was definite also and the growth of local strain as result of material creep. The results of calculations were introduced was on graphs, on basis which we can qualify the safe state of pipe with defect.
4
Analiza przyczyn pękania rur ze stali X20CrMoV121 w procesie gięcia
Niewielski G., Lalik S., Szala J.
Hutnik, Wiadomości Hutnicze
|
2004
|
Vol. 71, nr 4
182-187
PL
W pracy przedstawiono wyniki badań pękniętych rur z wysokostopowej martenzytycznej stali X20CrMoV121 (wg DIN 17175) stosowanej między innymi do produkcji rur na przegrzewacze pary w urządzeniach energetycznych. Stosowanie obróbki cieplnej (normalizowania) z temperatury końca walcowania oraz błedy technologiczne, mogące powstać w trakcie procesu wytwarzania rur, prowadzą czasami do ich pękania w trakcie kształtowania. Stwierdzono, że zasadniczą przyczyną pękania rur w procesie gięcia na zimno jest obecność wad pochodzenia metalurgicznego oraz częściowe podhartowanie powierzchni wewnętrznej rury w procesie normalizowania. Podhartowanie to spowodowane zostało wzbogaceniem stali w procesie ciągnienia w węgiel pochodzący ze smarów zawierających grafit. Wytwarzanie w wysokich temperaturach austenityzowania doprowadziło do dyfuzji węgla w głąb materiału od powierzchni wewnętrznej rur.
EN
In the work are presented test results of cracked pipes of the highly alloyed martensitic X20CrMoV21 steel (to DIN 17175) used, among others for production of pipes for steam superheaters in power industry equipment. Application of heat treatment (normalizing) from the final rolling temperature as well as engineering errors liable to occur during manufacturing process of pipes are sometime causing their cracking during plastic forming operations. It was discovered that the main cause of pipe cracking in cold bending process is the presence of defects having metallurgical origin as well as local prehardening of internal pipe surface during the normalizing process. This prehardening was caused by carbon enrichment of steel during drawing process from lubricants containing graphite. Holding in high austenitizing temperatures caused a diffusion of carbon deep into material from the pipe internal surface.
5
Przyczyny pękania rur ze stali X20CrMoV121 podczas gięcia na zimno
Mazur M., Stankiewicz M.
Inżynieria i Aparatura Chemiczna
|
2003
|
Nr 4
16-19
PL
W artykule przedstawiono wyniki badań mikrostruktury, wytrzymałości na rozciąganie, twardości i charakterów przełomów partii rur stalowych w gatunku X20CrMoV121 wykazujących skłonność do pękania przy gięciu na zimno. Stwierdzono, że przyczyną tego stanu jest pasmowy rozkład węglików przy powierzchni wewnętrznej rur. Pękaniu można przeciwdziałać podnosząc temperaturę gięcia lub wykonując ponowną obróbkę cieplną rur.
EN
Results of investigation on microstructure, tensile strength, hardness and characteristic fractures of X20CrMoV121 steel pipes prone to cracking during cold bending have been presented. It has been stated that carbide banding at the inner pipe surface was responsible for this situation. Cracking can be eliminated by the elevation of bending temperature or repetition of pipe heat treatment.
6
Content available remote Metody badań odporności rur polietylenowych na powolny wzrost pęknięć
Sasimowska I., Sasimowski E.
Przetwórstwo Tworzyw
|
1998
|
nr 5
111-114