The Problem of Material Fracture Prediction in Cross Rolling Processes

Pater Zbigniew, Tomczak Janusz, Bulzak Tomasz, Zniszczyński Andrzej

Advances in Science and Technology. Research Journal

|

2018

|

Vol. 12, no 4

184--189

EN

The paper deals with the problem of material fracture prediction in metal forming processes. It was found that the application of well-established solutions for ductile fracture prediction to the modelling of cross rolling processes leads to serious errors. These errors result from the fact that the limit value of the damage function determined via uniaxial tensile and compression tests is too low. Therefore, it is necessary to devise a new test in which the state of stress is similar to that in a cross wedge rolling process characterized by the occurrence of alternating compressive and tensile stresses.

2

Preliminary analysis of a rotary compression test

Pater Zbigniew, Walczuk Patrycja, Lis Konrad, Wójcik Łukasz

Advances in Science and Technology. Research Journal

|

2018

|

Vol. 12, no 2

77--82

EN

The paper addresses the problem of material fracture in cross rolling processes. A new test based on rotary compression for determining limit values of the damage function after the Cockroft-Latham criterion is proposed. A FEM analysis is performed to determine the stress and strain states in a workpiece subjected to this test. The numerical results demonstrate that the axial region of the workpiece is characterized by the presence of alternating tensile and compressive stresses conducive to fracture. The distribution of the Cockroft-Latham integral in the axial region of the workpiece is determined.

3

Symulacja i interpretacja próby SICO

Trębacz L., Kuziak R., Pietrzyk M.

Prace Naukowe Politechniki Warszawskiej. Mechanika

|

2005

|

z. 207

91--96

PL

Opracowanie ilościowego kryterium pękania materiałów w procesach plastycznej przeróbki metali ma duże znaczenie dla modelowania tych procesów w zastosowaniu do specjalnych materiałów, charakteryzujących się małą plastycznością. Znane kryteria opierające się na obliczeniach historii naprężenia i odkształcenia, dają dobre wyniki jakościowe, ale dokładność ilościowa jest często niewystarczająca. Jest to zwykle związane z trudnościami w wyznaczeniu współczynników materiałowych w kryterium pękania. Problem opracowania bardziej ogólnego kryterium, dającego dobre wyniki jakościowe, jest nadal otwarty. Próba SICO jest powszechnie stosowana do wyznaczania podatności materiałów do pękania. Ze względu na duże niejednorodności temperatury, naprężeń i odkształceń w tej próbie, jej ilościowa interpretacja stwarza duże trudności. Jednym z celów niniejszej pracy jest modelowanie numeryczne próby SICO i wykorzystanie wyników symulacji, obejmujących obliczenia pól odkształceń, naprężeń i temperatur, do wyznaczenia parametrów materiałowych w kryterium pękania. Opracowanie metodyki fizycznej symulacji próby SICO jest drugim celem pracy. Próby zrealizowano na symulatorze Gleeble 3800 dla stali z różną zawartością miedzi. Wyniki prób wykorzystano do identyfikacji kryteriów pękania. W wyniku przeprowadzonych badań możliwe było ilościowe wyznaczenie zależności między parametrami materiałowymi w kryterium pękania a zawartością miedzi w stali.

EN

Formulation of quantitative fracture criterion for materials subjected to plastic working is essential for modeling of these processes for special materials, which are characterized by low plasticity. Criteria based on computing of stress and strain history are commonly used. They give relatively good qualitatively results but quantitative accuracy is often insufficient. It is generally due to difficulties with determination of material coefficient in fracture criteria. Problem of formulation more general criterion, which give qualitatively good results, is still open. SICO test is commonly used to determine tendency of materials to fracture. Due to in homogeneities of temperature, stress and strain fields in the test, quantitative interpretation produce certain problems. Goals of this work follow from this facts. The first is numerical simulation of the SICO. Results of this simulation (stress, strain and temperature fields) are used to determined materials parameters in fracture criterion. Physical simulation of the SICO test is the second goal of the work. Tests were performed on Gleeble 3800 for steels with different contents of copper. Results of these tests are used to identification fracture criterion. Suggestion of the relationship between material parameters in fracture criterion and copper contents in steel was possible.

4

Częściowe zamknięcie szczeliny międzyfazowej spowodowane termicznymi deformacjami

Matczyński M., Martyniak R., Honczar K., Nagalka S.

Zeszyty Naukowe Politechniki Świętokrzyskiej. Mechanika

|

2003

|

Z. 78

315-324

PL

W pracy rozważa się dwuskładnikowy kompozyt z prostoliniową międzyfazową szczeliną. Składniki kompozytu różnią się własnościami termicznymi, zaś ich własności mechaniczne są jednakowe. Powierzchnie szczeliny są termicznie izolowane. Szczelina pod wpływem obciążenia termicznego zamyka się na pewnym odcinku w jej środkowej części. Wykorzystując metodę potencjałów zespolonych rozwiązanie kontaktowego zagadnienia szczeliny sprowadzono do rozwiązania silnie osobliwych równań całkowych. Analizowana jest długość odcinka kontaktu, rozwarcie szczeliny w jej pozostałej części, ciśnienie kontaktowe brzegów szczeliny oraz współczynniki intensywności naprężenia w jej wierzchołkach.

EN

The bimaterial is weakened by the straight interface crack. The components of the bimaterial are of the same mechanical properties but differ in thermal properties. The crack surfaces are thermally insulated. It is assumed that due to the thermal load the crack is closed along of certain segment, which is located in the central part of the crack. Making use of the method of complex potentials, the solution of the problem is reduced to the solution of singular integral equations. The length of the contact segment, opening of the remaining part of the crack, contact pressure and stress intensity factors at the crack tips are discussed.