Wyniki wyszukiwania - BazTech

1

Carbon Co-Deposition During Gas Reduction of Water-Atomized Fe-Cr-Mo Powder

Ali B., Choi S. H., Seo S. J., Maeng D. Y., Lee C. G., Kim T. S., Park K. T.

Archives of Metallurgy and Materials

|

2017

|

Vol. 62, iss. 2B

1119--1124

EN

The water atomization of iron powder with a composition of Fe-3Cr-0.5Mo (wt.%) at 1600°C and 150 bar creates an oxide layer, which in this study was reduced using a mixture of methane (CH4) and argon (Ar) gas. The lowest oxygen content was achieved with a 100 cc/min flow rate of CH4, but this also resulted in a co-deposition of carbon due to the cracking of CH4. This carbon can be used directly to create high-quality, sinter hardenable steel, thereby eliminating the need for an additional mixing step prior to sintering. An exponential relationship was found to exist between the CH4 gas flow rate and carbon content of the powder, meaning that its composition can be easily controlled to suit a variety of different applications.

2

Próba zwiększenia własności przeciwzatarciowych Smaru Maszynowego 2

Czupryk W.

Tribologia

|

2012

|

nr 3

35-44

PL

Smar Maszynowy 2 charakteryzuje się zbyt niskimi własnościami przeciwzatarciowymi w zastosowaniu do smarowania łożysk tocznych. Cechę tę potwierdzają dane literaturowe i wyniki badań własnych wykonanych na aparacie czterokulowym. W celu zwiększenia własności przeciwzatarciowych Smaru Maszynowego 2 wprowadzono do jego objętości mieszankę tlenku miedzi i gliceryny z alkoholem etylowym. Badania miały na celu dać odpowiedź na pytanie, czy w warunkach dużych nacisków, zmiennych naprężeń i wysokich krótkotrwałych temperatur w obszarze kontaktu tlenek miedzi będzie redukowany do miedzi metalicznej, która będzie spełniała rolę smaru stałego. Badania wykonano na aparacie czterokulowym w trzech następujących po sobie seriach. Każda z nich trwała 60 sekund. Nacisk był stały i wynosił 1472 N. Po wykonaniu badań obliczono graniczne obciążenie zatarcia G0Z. Stwierdzono znaczny wzrost wskaźnika G0Z dla smarów z wymienionymi wcześniej dodatkami: G0Z dla Smaru Maszynowego 2 wynosił 529 [N/mm2], a dla innych składów dodatków wprowadzonych do smaru zawierał się w przedziale 900–1736 [N/mm2]. W celu potwierdzenia zjawiska redukcji tlenku miedzi do miedzi metalicznej wykonano badania powierzchniowe i wgłębne z użyciem spektrometrii AES. Wyniki analiz potwierdziły występowanie w warstwie powierzchniowej i warstwach głębiej zlokalizowanych miedzi metalicznej. Obecność warstewki metalicznej miedzi na ścieżce kontaktu spełniającej rolę smaru stałego skutkowała zwiększeniem odporności na zatarcie Ft trzy-, a nawet czterokrotnie w stosunku do tego samego wskaźnika dla Smaru Maszynowego 2.

EN

The anti-seizing properties of Machine Grease 2 are too poor to ensure the proper lubrication of rolling bearings. This is confirmed by research publications and the results of the author's tests carried out using the four-ball EP tester. In order to enhance the anti-seizing properties of Machine Grease 2, a mixture of copper oxide, glycerine, and ethyl alcohol was introduced into its volume. The aim of the tests was to find out if, under high pressures, variable stresses and short-duration temperatures in the contact region cause the copper oxide to be reduced to metallic copper functioning as grease. The tests in the four-ball EP tester were carried out in three consecutive series, each lasting 60 seconds. The pressure remained constant and amounted to 1472 N. After the tests, the limit of the seizure load G0Z was calculated. Index G0Z was found to be considerably higher for lubricants containing the above additives, amounting to 529 [N/mm2] and 900–1736 [N/mm2] for Machine Grease 2 and lubricating compositions containing the mixture of copper oxide, glycerine and ethyl alcohol, respectively. Due to the presence a metallic copper film on the contact path, seizure resistance Pt increased three to even four times in comparison with this index for Machine Grease 2.

3

Reduction of cadmium oxide from (CdO+ZnO) mixture

Malinowski C., Małecki S.

Archives of Metallurgy

|

2000

|

Vol. 45, iss. 1

103-113

EN

Reduction of cadmium oxide from (CdO-ZnO) mixture by means of a mixture of gases (CO+CO2) and of carbon in the temperature range 1048-1200 K were investigated. It has been found that the reduction rate of CdO is proportional to the CO content in the mixture of the reducing gases. The effect of temperature and of the composition of the gaseous phase on the reduction rate of CdO and on the zinc content in the gaseous reduction products was determined. The value of the activation energy of this process has also been estimated. In the case of CdO reduction from zinc-cadmium carbonate by means of carbon the conditions were determined which should guarantee obtaining cadmium of Cd-"0" grade or cadmium oxide of ”C” grade.

PL

Przeprowadzono badania redukcji tlenku kadmu z mieszaniny (CdO + ZnO) za pomocą mieszaniny gazów (CO+CO2) oraz węgla w zakresie temperatur 1048-1200 K. Stwierdzono, że szybkość redukcji CdO proporcjonalna jest do zawartości CO w mieszaninie gazów redukcyjnych. Określono wpływ temperatury i składu fazy gazowej na szybkość redukcji CdO oraz na zawartość cynku w gazowych produktach redukcji. Oszacowano także wartość energii aktywacji tego procesu. Przy redukcji CdO z węglanu cynkowo-kadmowego za pomocą węgla określono warunki, które winny zapewnić otrzymanie kadmu w gatunku Cd-.”0" lub tlenku kadmu w gatunku ”C”.

4

The properties of the process of reduction of nitrogen oxides on a carbon sorbent.

Jastrząb K., Szarawara J.

Archiwum Ochrony Środowiska

|

1998

|

Vol. 24, no. 4

59-75

EN

The influence of temperature and the composition of gases on the reduction of nitrogen oxide with ammonia on the Polish sorbent, assigned for the purification of combustion gases has been investigated. These investigations were carried out in a flow system with stationary carbon sorbent layer. The dependence of the reduction degree of nitrogen oxide on the space time of the purified gases with the sorbent layer, as well as on the temperature and concentration of NO, NH3, H2O and O2 has been determined. These relation have been expressed by mean of regression equations. The optimal conditions of the process have been determined, viz temperature and the excess of ammonia. Apart from their cognitive significance, the obtained results may serve the purpose of describing quantitatively the reduction process of nitrogen oxide.

PL

Przebadano wpływ temperatury i składu gazów na przebieg redukcji tlenku azotu amoniakiem na polskim sorbencie węglowym przeznaczonym do oczyszczania spalin. Badania prowadzono w układzie przepływowym z nieruchomym złożem sorbentu węglowego. Wyznaczono zależności stopnia redukcji tlenku azotu od czasu zetknięcia oczyszczonych gazów ze złożem oraz temperatury i stężenia NO, NH3, H2O i O2. Zależności te opisano odpowiednimi równaniami regresji. Ustalono optymalne warunki procesu: temperaturę i nadmiar amoniaku. Otrzymane wyniki oprócz znaczenia poznawczego mogą posłużyć do ilościowego opisu procesu redukcji tlenku azotu.