Background of branched crack formation in surface zone of continuously-cast Ti-Nb microalloyed steel slab

Bekeč P., Longauerová M., Vojtko M., Milkovič O., Kadlec J., Tréfa G., Grimplini G.

Journal of Achievements in Materials and Manufacturing Engineering

|

2014

|

Vol. 67, nr 2

58--64

EN

Purpose: This work deals with the study of the background to the formation of branched cracks in a continuously-cast slab, at pulling rate 0.43 m.min-1. Design/methodology/approach: Samples were taken from the individual cut-outs for further analyzes. Macroscopic analysis was used to evaluate the surface quality of the analysed slabs using a Leica Wild M3Z macroscope. The microstructure was observed with an OLYMPUS VANOX-T light microscope. For the evaluation of the concentration profile of the selected elements in planes parallel to the slab surface, wavelength dispersive X-ray analysis (WDX) was used with a Camebax-MICROanalyzer. Findings: The results of the work show that branched cracks extended to a depth of 10 mm below the slab surface and occurred mostly below oscillation marks. Cracks were mostly present in the edge parts of the slab, where they were also deeper in comparison with locations in the middle of the slab width. Microstructural analysis confirmed heterogeneity of ferrite grain sizes in the slab surface skin. Wavelength-dispersive X-ray analysis of a sample with a branched crack showed chemical heterogeneity of harmful elements, mainly S and As. Research limitations/implications: Precipitation of microalloying elements in connection with the cementite can lead to higher probability of surface crack formation, as also confirmed in this study. Originality/value: of this work is background of branched crack formation in surface zone of continuously-cast Ti-Nb microalloyed steel slab.

2

Wpływ smarowania na jakość powierzchni wlewków ciągłych

Sorek A., Kania H.

Prace Instytutu Metalurgii Żelaza

|

2013

|

T. 65, nr 1

28-35

PL

Istotnym czynnikiem wpływającym na jakość powierzchni wlewków ciągłych są zjawiska fizyczne, chemiczne i mechaniczne zachodzące w strefie przymeniskowej krystalizatora COS. Do zjawisk tych możemy między innymi zaliczyć "smarowanie" powierzchni wlewka ciągłego w krystalizatorze. Powszechnie stosowaną metodą smarowania powierzchni wlewka jest stosowanie zasypek krystalizatorowych. Zasypki w kontakcie z ciekłą stalą tworzą ciekłą fazę żużlową która jest czynnikiem smarującym. W artykule scharakteryzowano proces smarowania powierzchni wlewka w procesie ciągłego odlewania stali. Przedstawiono wyniki badań przemysłowych wpływu stosowanej zasypki na jakość powierzchni otrzymywanych wlewków ciągłych.

EN

The physical, chemical and mechanical phenomena which take place in the near-meniscus zone of continuous casting mold are the significant factors influencing the quality of CC ingot and especially the quality of its surface. Such phenomena include, but are not limited to, the lubrication of ingot surface in the COS mold. Application of mold powders is the commonly used lubrication method. Mold powders form the liquid slag phase in contact with liquid steel. This slag phase is a lubricant agent. In this article, the lubrication of ingot surface in continuous casting was characterized. The paper presents the results of industrial studies on the influence of powders on surface quality of continuous casting ingots.

3

The influence of the near-meniscus zone in continuous casting mold on the surface quality of the continuous casting ingots

Sorek A., Kudliński Z.

Archives of Metallurgy and Materials

|

2012

|

Vol. 57, iss. 1

371-377

EN

The physical, chemical and mechanical phenomena which take place in the near-meniscus zone of continuous casting mold are the significant factors influencing the quality of CC ingot and especially the quality of its surface. Such phenomena consist of the following processes: lubrication of the ingot surface by the liquid slag-forming phase of mold powder, creation of meniscus, formation of the specific kind of galvanic cell and connected with this cell ions migration of liquid mold powder. Application of the mold powders is the commonly used lubrication method of the surface of CC ingots in mold (in near-meniscus zone). According to the ionic structure theory of the liquid metallurgical slags the following thesis can be formulated: the liquid slag-forming phase of mold powder is the ionic liquid. The ionic liquid occurs between two metals: the copper wall of mold and the steel surface of ingot can create a specific kind of galvanic cell in the upper part of mold (the near-meniscus zone of mold). The paper presents results of industrial research of low-carbon steel continuous casting. The electromotive force of galvanic cell situated in the upper (near-meniscus) part of CC mold was measured. Moreover, the influence of applied powders with different alkalinity on the character of oscillatory marks forming on the ingot surface was considered. The galvanic cell, which is created in the upper part of mold in the near-meniscus zone, can cause the essential change of the chemical composition of electrolyte (liquid phase of mold powder) in the near-electrodes zones. So in the process the condition of lubrication and character of obtained oscillatory mark can also be changed.

PL

Istotnym czynnikiem wpływającym na jakość wlewka ciągłego a zwłaszcza jakość jego powierzchni są zjawiska fizyczne, chemiczne i mechaniczne zachodzące w strefie przymeniskowej krystalizatora COS. Do zjawisk tych należy między innymi zaliczyć: "smarowanie" powierzchni wlewka ciekłą fazą żużlotwórczą zasypki, powstawanie menisku, tworzenie się specyficznego rodzaju ogniwa galwanicznego i związana z nim migracja jonów ciekłej zasypki. Powszechnie stosowaną metodą smarowania powierzchni wlewka ciągłego w krystalizatorze - w strefie przymeniskowej - jest stosowanie zasypek krystalizatorowych. Powołując się na teorię jonowej budowy ciekłych żużli metalurgicznych można postawić tezę że ciekła żużlotwórcza faza zasypki krystalizatorowej jest cieczą jonową. Występując między dwoma metalami - miedzianą ścianką krystalizatora i żelazną (stalową) powierzchnią wlewka może utworzyć szczególny rodzaj ogniwa galwanicznego w górnej części krystalizatora (strefa przymeniskowa krystalizatora). W artykule przedstawiono wyniki badań przemysłowych siły elektromotorycznej ogniwa usytuowanego w górnej (przymeniskowej) części krystalizatora COS podczas ciągłego odlewania stali niskowęglowej. Przedstawiono również wyniki badań przemysłowych wpływu stosowanych zasypek krystalizatorowych, różniących się zasadowością, na charakter znaków oscylacyjnych powstających na powierzchni wlewka ciągłego. Występowanie ogniwa galwanicznego w górnej części krystalizatora w tzw. strefie przymeniskowej może w istotny sposób powodować zmianę składu chemicznego elektrolitu (ciekłej fazy zasypki) w obszarach przyelektrodowych a tym samym warunków smarowania i charakteru otrzymywanych śladów oscylacyjnych.

4

Wpływ zasypki krystalizatorowej na jakość powierzchni wlewków ciągłych

Sorek A., Kudliński Z.

Hutnik, Wiadomości Hutnicze

|

2010

|

Vol. 77, nr 11

631-635

PL

W artykule przedstawiono dotychczasowe poglądy dotyczące przyczyn i mechanizmu powstawania znaków oscylacyjnych na powierzchni wlewków ciągłych oraz wyniki własnych badań przemysłowych wpływu zasypek krystalizatorowych (różniących się składem chemicznym i zasadowością) na charakter śladów oscylacyjnych na powierzchni wlewka ciągłego o przekroju poprzecznym 140×165 mm.

EN

The paper we presents the current views on the mechanism for the formation of oscillation marks on the surface of continuous ingots and the results of industrial investigations of the influence of the mold powders (which differ in chemical composition and basicity) on the nature of oscillation marks on the surface of the continuous ingot of cross-section 140×165 millimeters