An experiment leading to obtaining the mathematical model of the mean equivalent stress (MES) of magnesium alloy AZ31 was realized in the laboratory rolling mill. Neglecting of the speed term in the resulting model of MES was possible by a relatively narrow range of applied strain rates, and also by the fact that a close relationship between height strain and strain rate exists. The paper also presents the obtained data, related to the dependencies between deformation process parameters, inhomogeneity and grain size after dynamic recrystallization for the specimens subjected to hot rolling. A significant influence of the deformation temperature on the grain size after recrystallization was identified, while observing lower sensitivity of this parameter to an increased rolling speed.
PL
Na walcarce laboratoryjnej przeprowadzono badania w celu wyznaczenia matematycznego modelu średniego naprężenia uplastyczniającego dla stopu magnezu AZ31. Pominięcie parametru prędkości w opisanym modelu było możliwe dzięki relatywnie wąskiemu zakresowi zadawanych prędkości odkształcenia, a także dzięki istnieniu ścisłego związku pomiędzy wartością odkształcenia, a prędkością odkształcenia. Artykuł przedstawia również wyniki związane z zależnościami pomiędzy parametrami procesu odkształcenia a niejednorodnością oraz wielkością ziarna po dynamicznej rekrystalizacji dla próbek poddanych walcowaniu na gorąco. Stwierdzono istotny wpływ temperatury odkształcenia na wielkość ziarna po rekrystalizacji oraz mniejszą wrażliwość tego parametru na wzrost prędkości walcowania.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.