This study reports the findings of an argon (Ar) plasma treatment added to the traditional pad-dry-cure process between dry and cure treatments. This new process is called the "paddry-plasma-cure process". The crosslinking agent was a mixture of dimethyloldihydroxyethyleneurea (DMDHEU) and maleic acid (MA). Results show that Ar plasma treatment can increase the bonded crosslinking agent (i.e., the nitrogen content). The dry crease recovery angle (DCRA), wet crease recovery angle (WCRA), and tensile strength retention (TSR) of the pad-dry-plasma-cure finished fabrics were higher than those of traditional pad-dry-cure finished fabrics at a given nitrogen content. Additionally it was found that the number of crosslinks per anhydroglucose unit (CL/AGU) and the length of crosslinks of pad-dry-plasma-cure-finished fabrics were higher than that of traditional pad-dry-cure finished fabrics at the same resin concentration in the pad bath. DCRA, WCRA and TSR values of pad-dry-plasma-cure-finished fabrics were higher than those of pad-dry-curefinished fabrics at the same CL/AGU value. However, activation energies for the pad-dryplasma-cure process were higher than those for the pad-dry-cure process. The anti-bacterial ability and odour absorption of the pad-dry-plasma-cure and pad-dry-plasma-cure finished fabrics were higher than those for the pad-dry-cure finished fabrics. The surface distribution of crosslinking agents for the pad-dry-plasma-cure process was higher than that of the pad-dry-cure process. Thus the pad-dry-plasma-cure process is excellent for improving the physical properties, bacterial inhibition, and odour absorption of finished cotton fabrics and for decreasing their formaldehyde release.
PL
Artykułu odnosi się do problematyki możliwości i celowości wprowadzenia modyfikacji plazmowej w warunkach niskociśnieniowych i w środowisku argonu do konwencjonalnego procesu wykończenia przeciw mnącego z zastosowaniem reaktywnych żywic termoutwardzalnych. Badano kąt odprężenia na sucho i na mokro, i stwierdzono polepszenie właściwości odporności na zagniecenia w wyniku dodatkowego zastosowania plazmy. Badano również właściwości antybakteryjne i pochłanianie zapachów, które okazały się korzystniejsze dla dodatkowej obróbki plazmowej. W wyniku zmodyfikowanej obróbki uzyskano mniejsze wydzielanie formaldehydu z gotowej tkaniny.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
A complex of fibroin and citric acid was prepared and used for the crease resistant finishing of cotton fabrics, which increased the crease resistance of cotton and avoided fabric yellowing caused by citric acid as a finishing agent for cotton. An orthogonal experiment design and variance analysis were adopted to investigate optimum processing parameters for the multiple quality characteristics of treated cotton fabrics. According to range and variance analyses from the orthogonal experiments, fibroin was the most sensitive factor influencing the whiteness index of the fabrics, and citric acid had a more marked effect on crease recovery. The optimum combination of the processing parameters was 4% fibroin, 20 g/dm3 of citric acid, 5% sodium dihydrogen phosphate, a pH 6 finishing bath and a curing temperature of 130°C.
PL
Przygotowano kompleks fibroiny i kwasu cytrynowego dla przeciwgniotliwego wykańczania tkanin bawełnianych. Celem zastosowania kompleksu było zwiększenie odporności tkanin na gniecenie oraz nie powodowanie żółknięcia występującego przy stosowaniu samego kwasu cytrynowego. Zastosowano ortogonalny system analizy eksperymentu dla określenia optymalnych jakościowych parametrów badanych tkanin. Zgodnie z analizą rang i analizą wariancji stwierdzono, że fibroina jest czynnikiem najbardziej wpływającym na indeks bieli tkanin a kwas cytrynowy ma zwiększony wpływ na odprężenie tkanin. Stwierdzono, że optymalny skład preparacji to 4% fibroiny, 20 g kwasu cytrynowego na cm3 roztworu i 5% dwuwodoro fosforanu sodowego, a warunki końcowej kąpieli to pH 6 i temperatura 130°C.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.