Test methods of concrete resistance to chloride ingress

Zych T.

Czasopismo Techniczne. Budownictwo

2014

R. 111, z. 6-B

117--139

The experimental methods for determination of concrete resistance to chlorides – both the chloride permeability test methods (NT Build 492 NordTest – Non-S teady State Migration Test, AASHTO T 277-ASTM C 1202 Test) and the methods for testing concrete resistance to surface scaling due to cyclic freezing and thawing in the presence of NaCl solution (deicing salts, saline sea water, etc.) (e.g. Slab Test according to CEN/TS 12390-9, based on the Borås method according to Swedish Standard SS 13 72 44) are presented in the paper. The Rapid Chloride Test – the method used "in situ" to determine the chloride ion content in concrete is also described.

W artykule przedstawiono doświadczalne metody określenia odporności betonu na działanie chlorków – metody badania przepuszczalności chlorków (NT Build 492 NortTest – Test migracji chlorków przy nieustalonym przepływie, AASHTO T 277-ASTM C 1202 Test) oraz metody badania odporności betonu na powierzchniowe łuszczenie spowodowane cyklicznym zamrażaniem i odmrażaniem w obecności roztworu NaCl (soli odladzających, słonej wody morskiej itd.) (np. Slab Test według normy CEN/TS 12390-9, wzorowany na metodzie Borås według szwedzkiej normy SS 13 72 44). Opisano również Rapid Chloride Test – metodę "in situ" badania zawartości jonów chlorkowych w betonie.

Air void system parameters and frost resistance of air-entrained concrete containing calcareous fly ash

Dąbrowski M., Glinicki M. A.

Roads and Bridges - Drogi i Mosty

2013

Vol. 12, no. 1

41-55

The paper presents results of the investigation of the air void characteristics and the resistance to cyclic freezing and thawing of air-entrained concrete containing calcareous fly ash. The frost resistance was tested also under the presence of de-icing salts to check the resistance to frost-salt scaling and without de-icing salts. The range of investigation included air entrained concrete mixes with the specified water-binder ratio of w/b=0.45 with addition of calcareous fly ash or made using blended cements with calcareous fly ash (W), and also siliceous fly ash (V) and ground granulated blast-furnace slag (S). The coarse aggregates used were crushed granodiorite and crushed limestone. The air-void system parameters were determined by microscopic image analysis and the effect of addition of calcareous fly ash was assessed. The effect of concrete age and presence of fly ash W on the strength and freeze-thaw resistance was also studied. The tests have shown that the use of calcareous fly ash as one of the main constituents of blended cements does not affect the frost salt scaling resistance nor the resistance to internal frost damage provided that the air void system is adequate.

Przedstawiono wyniki badań charakterystyki porów oraz odporności na cykliczne zmrażanie i rozmrażanie betonów napowietrzonych z popiołem lotnym wapiennym. Badania mrozoodporności przeprowadzono w obecności środków odladzających (odporność na powierzchniowe łuszczenie) oraz bez środków odladzających. Zakres badań obejmował betony napowietrzone o w/b=0, 45 z dodatkiem popiołu lotnego wapiennego Oraz betony z cementów wieloskładnikowych, zawierających Popiół lotny wapienny (W), a także popiół lotny krzemionkowy (V) i granulowany żużel wielkopiecowy (S). Zastosowano dwa rodzaje kruszyw do betonu: grys granodiorytowy i grys wapienny. Określono charakterystykę porów powietrznych w betonie metodą Mikroskopowej analizy obrazu i przeanalizowano efekty stosowania popiołów lotnych wapiennych. Przeanalizowano także wpływ wieku betonu i obecności popiołu lotnego W na wytrzymałość i mrozoodporność betonu. Z badań wynika, ?e zastosowanie popiołu lotnego wapiennego jako składnika głównego cementów wieloskładnikowych nie pogarsza odporności betonu na powierzchniowe łuszczenie w obecności soli odladzających, jak i mrozoodporności wewnętrznej, pod warunkiem właściwego napowietrzenia betonu.