The Influence of Heat Treatment and Chemical Composition on the Structure and Mechanical Properties of Thick-walled Ductile Iron Castings

Trepczyńska-Łent M.

Archives of Foundry Engineering

|

2018

|

Vol. 18, iss. 4

71--76

EN

In this work, the effects of 75 mm thick cast iron, (casting mould YIV) composition (Cu) and heat treatment were investigated on the microstructure and mechanical properties (hardness, elongation, tensile strength, yield strength) of ductile iron castings. As a result of adding Cu, the amount of pearlite is at 80% reduces of amount of ferrite. Normalizing of non-alloy cast iron increases the amount of pearlite to 70%. It also, increases tensile strength (659 MPa) and hardness (248 HB). Studied metallographic crossections were made from the grip sections of the tensile specimens. The structure composition and the characteristics of graphite were determined by computer image analysis. Measurements of graphite of non-alloy cast iron after normalizing and in cooper cast iron indicate the approximate amount of precipitates of graphite and their approximate average diameters. The applied normalizing and the additive alloy (Cu) were established to give comparable mechanical properties and structure of matrix in thick-walled castings.

2

Optymalizacja konstrukcji grubościennego odlewu żeliwnego na przykładzie wlewnicy

Maj M., Piekło J., Pysz S., Stachurski W.

Zeszyty Naukowe Politechniki Poznańskiej. Budowa Maszyn i Zarządzanie Produkcją

|

2004

|

Nr 1

63-72

PL

Wlewnice pełnią funkcję stacjonarnych krystalizotorów, w których akumuluje się ciepło przegrzania i ciepło krystalizacji ciekłego metalu, a także następuje niestacjonarny przepływ ciepła stygnącego wlewka. Ten złożony proces wymiany ciepła, któremu towarzyszy powstawanie szczeliny w wyniku zmian geometrii krzepnącego wlewka i nagrzewanej wlewnicy, stwarza trudności w procesie konstruowania wlewnicy. Bardzo pomocne w zakresie projektowania są aktualne programy komputerowe, które uwzględniają przepływy ciepła w zależności od temperatury i zmian stanu fizycznego materiału. Grubościenne odlewy wlewnic z racji długiego czasu krzepnięcia i stygnięcia mają zróżnicowaną strukturę na przekroju ściany i wzdłuż jej wysokości, co znajduje odzwierciedlenie we właściwściach mechanicznych. Nakłada się na to pole temperatury wynikające z cyklicznego nagrzewania wlewnicy. Skutkiem tych zjawisk jest występowanie pola naprężeń chwilowych i trwałych w całym cyklu cieplnym. Prowadzi to do zmęczenia cieplnego materiału i szybkiego zużycia. Przeprowadzone badania właściwości mechanicznych i symulacja komputerowa pozwoliły na korektę kształtu i grubości ścian wlewnicy prowadzącą do eliminacji pionowych pęknięć.

EN

Ingot moulds play the crystallizer rule, in which overheat and crystallization heat of the liquid metal is accumulated and also the unsteady heat flow of ingot cooling down takes place. This compound process of heat exchange, with crack forming, as the result of geometrical changes of solidified ingot and heated ingot mould, is the source of the difficulties in its design process. Actual computer programs are very helpful in the design ranges. These programs take into account the heat flow in dependence on temperature and physical state changes of material. Thick walled casts of ingot moulds, because of long time of solidification and cooling of those, have the diversified microstructure on wall cross-section as well as along its high. These phenomenons reflect the mechanical properties. The temperature field, resulting from cyclic heating of ingot mould, applies too. Occurring of instantaneous and durable field stresses in the whole heat cycle are the effects of these phenomenons. These facts lead to heat fatigue and quick wear of material. Performed mechanical properties investigations and computer simulation allow shape and thickness correction of ingot mould walls resulting in the elimination of perpendicular cracks.

3

Wytwarzanie grubościennych odlewów ze staliwa Hadfielda

Modrzyński A.

Krzepnięcie Metali i Stopów

|

2000

|

R. 2, nr 43

375--382

PL

W wielu przypadkach odlewy, które powinny być wykonane ze staliwa Hadfielda wykonuje się z materiałów zastępczych (np. L35GSM) o znacznie krótszym okresie eksploatacji. Dla wielu odlewni wykonanie w sposób prawidłowy grubościennych odlewów ze staliwa Hadfielda, o kontrolowanych właściwościach na próbkach przylanych do odlewu, jest bardzo trudne technologicznie. Zakład Odlewnictwa Instytutu Technologii Materiałów PP dla potrzeb jednej z krajowych odlewni opracował technologię produkcji grubościennych odlewów z tego gatunku staliwa, która spełniała bardzo surowe warunki odbioru kontrahenta z Niemiec.

4

Segregacja a pękanie odlewów staliwnych

Suchy J., Mochnacki B., Król S.

Krzepnięcie Metali i Stopów

|

1998

|

nr 36

27--31

PL

Krzepnięcie i krystalizacja grubościennych odlewów ze staliw stopowych CrMo-V a także przemiany fazowe zachodzące w stanie stałym decydują o własnościach użytkowych wyrobów finalnych. Segregacja dendrytyczna oraz tworzenie się pasm twardych węglików wanadu i molibdenu są przyczyną powstawania pęknięć dyskwalifikujących odlew.