Morphology and selected properties of cellulose acetate membranes for environmental applications

Maryudi Maryudi, Hakika Dhias Cahya, Amillia Amillia

Polimery

|

2024

|

Vol. 69, nr 5

292--299

EN

Microporous membranes were obtained by dry-wet phase inversion from a solution of cellulose acetate (CA) in acetone (13, 14 and 15 wt%). Polyethylene glycol was used as a blowing agent. The structure and mechanical properties were examined. FT-IR spectra show that the addition of polyethylene glycol improves the thermodynamics of the solution and increases the hydrophilicity of the membrane. The SEM method confirmed the microporous structure of membranes with an asymmetric structure and various pore sizes and porosities. Higher CA concentration resulted in better tensile properties.

PL

Mikroporowate membrany otrzymano metodą inwersji fazy sucho-mokrej z roztworu octanu celulozy (CA) w acetonie (13, 14 i 15% mas.). Jako środek porotwórczy zastosowano glikol polietylenowy. Zbadano strukturę i właściwości mechaniczne. Widma FT-IR pokazują, że dodatek glikolu polietylenowego poprawia termodynamikę roztworu i zwiększa hydrofilowość membrany. Metodą SEM potwierdzono m ikroporowatą strukturę membran o asymetrycznej budowie i różnej wielkości porów oraz porowatości. Większe stężenie CA skutkowało lepszymi właściwościami mechanicznymi przy rozciąganiu.

2

Influence of the addition of chitin nanocrystals on the characteristics of cellulose acetate films

Ravikumar Preethi, Sagadevan Suresh

Polimery

|

2021

|

T. 66, nr 2

98--104

EN

The present study deals with chitin nanocrystal (CHNC)-reinforced cellulose acetate (CA) films formed by the solvent casting method that makes use of poly(ethylene glycol) (PEG) as a plasticizing agent. Three different films containing various mass ratios of CHNCs (0.5, 1, and 2 wt %) in CA were investigated for hydrophilicity, mechanical properties, soil degradation, strength, water solubility, light transmittance, and antifungal activity. From the FT-IR analysis, no detectable shifts to the cellulose acetate bands with the loading of small amounts of CHNCs were observed. However, the light transmittance capacity of CA films decreased due to chitin addition. The chitosan incorporation enhanced the hydrophilic character of CA films, and also, the mechanical properties of the lower percentage of CHNCs in CA, like Young’s modulus, had a slight positive effect, while the tensile strength and elongation at breaks – had a negative influence. Finally, an increasing trend of antifungal activity with that of increased CHNC content was observed, i.e., the 2 wt % CHNCs containing CA film showed an inhibition rate (FGI) of 35%, 1 wt % CHNCs had a 15% inhibition rate, which is higher than that of 0.5 wt % CHNCs and pure CA, thereby indicating the potential role of CHNCs-reinforced CA films for packaging applications.

PL

Metodą odlewania rozpuszczalnikowego otrzymano biodegradowalne folie z octanu celulozy (CA) z dodatkiem 0,5; 1 i 2% mas. nanokrystalicznej chityny (CHNC) i poli(glikolu etylenowego) jako plastyfikatora. Zbadano hydrofilowość, właściwości mechaniczne, zdolność do degradacji w glebie, rozpuszczalność w wodzie, przepuszczalność światła i aktywność przeciwgrzybiczną folii. Przy niewielkiej zawartości CHNC nie stwierdzono przesunięcia pasm charakterystycznych w widmach FT-IR. Modyfikowane folie CA charakteryzowały się mniejszą przepuszczalnością światła i większą hydrofilowością (mniejsza wartość kąta zwilżania). Dodatek 0,5% mas. CHNC w niewielkim stopniu zwiększał moduł Younga oraz zmniejszał wytrzymałość na rozciąganie i wydłużenie przy zerwaniu. Stwierdzono korzystny wpływ CHNC na stopień hamowania wzrostu grzybów (wskaźnik FGI). Przy zawartości 1% mas. CHNC wskaźnik ten wynosił 15%, a przy zawartości 2% mas. 35% i był wyższy niż dla octanu celulozy (FGI = 7,5%). Wzmocnione CHNC folie CA mogą znaleźć zastosowanie w przemyśle opakowaniowym.

3

Improving the Water-Repellent and Antifungal Properties of Electrospun Cellulose Acetate Materials by Decoration with ZnO Nanoparticles

Nachev Nasko, Spasova Mariya, Manolova Nevena, Rashkov Iliya, Naydenov Mladen

Fibres & Textiles in Eastern Europe

|

2021

|

Vol. 29, no. 3 (147)

40--45

EN

Suitable conditions for the preparation of nano- and microstructured materials from cellulose acetate and cellulose acetate/ZnO from solutions/suspensions in aceton/water by electrospinning/electrospraying were found. The materials obtained were characterised by scanning electron microscopy (SEM), X-ray diffraction analysis (XRD) and contact angle measurements. The antifungal activity of the materials obtained against Phaeomoniella chlamydospora, which is one of the main species causing diseases in grapevines, was studied as well. It was found that electrospinning of CA solutions with a concentration of 10 wt% reproducibly resulted in the preparation of defect-free fibres with a mean fibre diameter of ~780 nm. The incorporation of ZnO nanoparticles resulted in the fabrication of hybrid materials with superhydrophobic properties (contact angle 152°). The materials decorated with ZnO possessed antifungal activity against P. chlamydospora. Thus, the fibrous materials of cellulose acetate decorated with ZnO particles obtained can be suitable candidates to find potential application in agriculture for plant protection.

PL

W pracy wskazano odpowiednie warunki do otrzymywania materiałów nano- i mikrostrukturalnych z octanu celulozy i octanu celulozy/ZnO z roztworów/zawiesin w acetonie/wodzie metodą elektroprzędzenia/elektrorozpylania. Uzyskane materiały scharakteryzowano za pomocą skaningowej mikroskopii elektronowej (SEM), dokonano analizy dyfrakcji rentgenowskiej (XRD) oraz pomiarów kąta zwilżania. Zbadano również działanie przeciwgrzybiczne uzyskanych materiałów przeciwko Phaeomoniella chlamydospora, który jest jednym z głównych gatunków wywołujących choroby winorośli. Stwierdzono, że podczas elektroprzędzenia z roztworów CA o stężeniu 10% wag. w sposób powtarzalny otrzymywano włókna wolne od defektów o średniej średnicy ~ 780 nm. Wprowadzenie nanocząstek ZnO zaowocowało wytworzeniem materiałów hybrydowych o właściwościach superhydrofobowych (kąt zwilżania 152°). Materiały z dodatkiem ZnO wykazywały działanie przeciwgrzybiczne przeciwko P. chlamydospora. Stwierdzono, że otrzymane materiały mogą być stosowane w rolnictwie do ochrony roślin.

4

Antifungal Microcapsules of Ethyl Cellulose by Solvent Evaporation and Their Application to Cotton Fabric

Erkan G., Sarıışık M.

Fibres & Textiles in Eastern Europe

|

2015

|

Vol. 23, no. 6 (114)

125--130

EN

In this study two antifungal pharmaceutical agents, terbinafine and ketoconazole, were microencapsulated by solvent evaporation. Two types of ethyl cellulose with different viscosity values were used. Microcapsules were evaluated by X-ray diffractometry, DSC, FTIR and SEM analysis. Although the characteristic peaks of ketoconazole appeared in the X-ray diffractometry, those of terbinafine disappeared. The same results were observed for DSC analysis. The melting point of ketoconazole existed, while that of terbinafine was not observed. The microcapsules had a spherical shape, however the particle size varied between 5 and 120 μm. The microcapsules were applied to 100% cotton fabric. The washing of fabrics was performed in various washing cycles, and afterwards antifungal tests were performed. The fabrics had antifungal properties against Trichophyton rubrum, which causes mycoses, up to 5 washing cycles.

PL

Zastosowano dwa antygrzybiczne farmaceutyki, terbinafinę i ketokonazol, wprowadzano do mikrokapsułek uzyskanych przez odparowanie rozpuszczalnika. Zastosowano dwa typy etylocelulozy o różnej lepkości. Mikrokapsułki badano za pomocą dyfrakcji rentgenowskiej, DSC, FTIR i SEM. Podczas gdy charakterystyczne piki ketokonazolu były widoczne w badaniach rozproszenia rentgenowskiego, piki terbinafiny nie były widoczne. Te same wyniki zaobserwowano przy zastosowaniu analizy DSC, punkt topnienia ketokonazolu był widoczny podczas gdy punktu topnienia terbinafiny nie można było zaobserwować. Kształty mikrokapsułek były sferyczne o różnych rozmiarach od 5 do 120 µm. Mikrokapsułki zastosowano do impregnacji 100% tkanin bawełnianych. Tkaniny prano stosując różne cykle pralnicze, a następnie przeprowadzano testy antygrzybiczne obrabianych tkanin. Testy wykazały antygrzybiczne właściwości przeciwko Trichophyton rubrum, powodujących grzybice, nawet do pięciu cykli pralniczych.

5

Próby wytwarzania pochodnych celulozy z modyfikowanych radiacyjnie mas celulozowych

Iller E., Kukiełka A., Mikołajczyk W., Stupińska H., Starostka P

Przegląd Papierniczy

|

2002

|

R. 58, nr 10

619--626

PL

Badano w warunkach laboratoryjnych wytwarzanie karboksymetylocelulozy (KMC), karbaminianu i octanu celulozy z masy celulozowej modyfikowanej strumieniem elektronów. W badaniach użyto masy celulozowej do przerobu chemicznego Alicell i sosnowej masy papierniczej, w których zdeponowano dawki energii w przedziale 0-15 kGy. Napromieniowanie strumieniem elektronów masy celulozowej Alicell wpłynęło pozytywnie na zawartość azotu i rozpuszczalność karbaminianu celulozy, a także na stopień acetylacji octanu celulozy. W przypadku otrzymywania KCM stwierdzono wpływ wstępnej obróbki radiacyjnej na spadek lepkości tej pochodnej, nie uzyskano jednak wzrostu stopnia podstawienia grup hydroksylowych ani wydajności produktu. Uzyskano natomiast interesujące wyniki otrzymywania karboksymetylocelulozy z masy celulozowej papierniczej, szczególnie w przypadku stosowania wysokostężeniowej merceryzacji.

EN

The labolatory trials of preparation of carboxymethylcellulose(CMC), carbomate(CC) and cellulose acetate from the cellulose pulps modified by electron-beam treatment has been carried out. In the tests, as a raw material, the Alicell and the paper grade pine pulps after irradation of electron beam with dose 10 and 15 kGy have been used. The electron beam treatment positively Influanced on physico-chemical properties of those pulps. Prepared the CC from electron beam modified of Alicell pulps possessed a high contens of nitrogen and characterized by exellent solubility. In the case of preparation the CMC it was found that the preliminary irradation of pulps effected on the reduction of the viscosity in this derivative but did not observe any increase in the degree of substitution of the hydroxyl groups as well as the product yield. Quite interesting results were obtained for preparation of the carboxyme- thylcellulose from the paper grade pulp, especially when high consistency mercerization had been applied.

6

Preparation and properties of cellulose acetate-coal heterogeneous reverse osmosis membranes.

Gashi S. T., Daci N. M., Selimi T. J., Berisha S.

Environment Protection Engineering

|

2000

|

Vol. 26, nr 4

29-37

EN

The heterogeneous asymmetric reverse osmosis membranes made from a blend of cellulose acetate and powdered coal prepared from two different composition of casting solvent solutions have been studied. Blends of cellulose acetate-coal of the following proportions by weight (1:1), (1:1.25) and (1:1.5) are tested with the first solvent mixture (acetone-dioxane), and the composition of cellulose acetate-coal in ratio (1:1.5) with three different types of coal and the second solvent (acetone) is also verified under the same casting solution, temperature, solvent evaporation time and gelation medium. The difference in performances caused by changes of solvents as well as by various amounts and types of coal are presented. At 86-90% level of solute separation and feed flow conditions corresponding to a mass transfer coefficient of 45×10-4 cm/s the productivities of the membranes are 49.89-30.99 g/(h/cm2) at 17×105 Pa using 6.86 mol/dm3 of NaCl in the feed. The reverse osmosis separation of other 10 inorganic salt solutions under the same conditions as in permeability tests have also been tested. The scanning electron micrographs of membranes with overaged reverse osmosis characteristics are given.

PL

Badano heterogeniczne, asymetryczne membrany do odwróconej osmozy, które wykonano z mieszanki octanu celulozy ze sproszkowanym węglem przygotowanej z dwu różnych mieszanin roztworów rozpuszczalnika służących do odlewania membrany. Testowano mieszaniny octanu celulozy z węglem aktywnym (w proporcji 1:1, 1:1,25 i 1:1,15), do których dodawano acetonu z dioksanem, a następnie mieszaninę octanu celulozy z trzema różnymi odmianami węgla (w stosunku 1:1,5), do której dodawano acetonu. W obu przypadkach zachowano ten sam skład roztworu do wylewania, taką samą temperaturę, ten sam czas parowania i rozpuszczalnika i to samo medium żelujące. Pokazano, że różnice w wydajności membran zależą od rodzaju rozpuszczalnika oraz ilości i rodzaju dodanego węgla. Gdy rozdzielenie substancji rozpuszczonych wynosiło 86-90%, a warunki przepływu cieczy przez membranę odpowiadały współczynnikowi przenikania masy 45x10-4 cm/s, wtedy sprawność membran wynosiła 49,89-30,99 gh-1 cm-2 pod ciśnieniem 17x10 5 Pa dla roztworu NaCl o stężeniu 6,86 mx dm-3. Testowano także w tych samych warunkach separację w wyniku odwróconej osmozy 10 innych roztworów soli nieorganicznych. Zaprezentowano zdjęcia membran wykonane za pomocą mikroskopu skaningowego.