1

Isothermal treatment of nitrided layers formed on steels

Nawrocki P., Szawłowski J.

Inżynieria Powierzchni

|

2018

|

nr 4

34--41

EN

This work was aimed at investigating the formation of nitrided layers during the isothermal transformation (austempering) and at describing the formed nitrided layer properties. The tested steels were characterized by a different content of carbon and alloying elements. In the case ofthe isothermal transformation, 4 variants of heat treatment parameters of nitrided layers were applied. The heat treatment differed in the austenitizing temperature (750°C-860°C) and the isothermal transformation temperature (390°C-420°C). The microstructure and the mechanical properties (hardness) of the nitrided layers formed after the heat treatment processes were determined. After the nitriding process, during 30 hours in the nitriding atmosphere consisting only of ammonia, the high nitrogen saturation in the surface zone of the layers was obtained. The nitrided layers, after the heat treatment processes, were characterized by the diversified thickness, as evidenced by the hardness distributions at their cross-sections.

PL

Niniejsza praca miała na celu zbadanie kształtowania się warstw azotowanych podczas przemiany izotermicznej oraz opis właściwości powstałej warstwy azotowanej. Badane stale charakteryzowały się różną zawartością węgla oraz zawartością pierwiastków stopowych. W przypadku przemiany izotermicznej zastosowano 4 warianty parametrów obróbki cieplnej warstw azotowanych. Obróbka cieplna różniła się temperaturą austenityzowania (750°C-860°C) i temperaturą przemiany izotermicznej (390°C-420°C). Określono mikrostrukturę oraz właściwości mechaniczne (twardość) powstałych warstw azotowanych po procesach obróbki cieplnej. Po procesie azotowania, w czasie 30 h w atmosferze azotującej, składającej się tylko z amoniaku, uzyskano wysokie nasycenie azotem w powierzchniowej strefie warstw. Warstwy azotowane, po procesach obróbki cieplnej, charakteryzowały się zróżnicowaną grubością, o czym świadczą rozkłady twardości na ich przekrojach.

2

Mikrostruktura warstwy azotowanej jarzeniowo na stopie Inconel 600

Borowski T., Płociński T., Kurzydłowski K. J., Wierzchoń T.

Inżynieria Materiałowa

|

2011

|

Vol. 32, nr 4

348-351

PL

Stopy niklu typu Inconel 600 stosowane obecnie w przemyśle lotniczym, chemicznym i energetycznym charakteryzują się dobrą plastycznością oraz odpornością na utlenianie w wysokiej temperaturze. Jednakże stopy te wykazują małą odporność na zużycie przez tarcie, co można eliminować przez zastosowanie obróbek powierzchniowych. Proces azotowania jarzeniowego umożliwia wytworzenie warstw dyfuzyjnych gwarantujących kilkakrotny wzrost twardości, a także poprawę odporności korozyjnej. Wytworzone warstwy charakteryzują się złożoną budową i wymagają szczegółowej analizy mikrostruktury, co stanowi przedmiot pracy. W artykule omówiono wyniki badań mikrostruktury, składu chemicznego i fazowego warstw wytworzonych w procesie azotowania jarzeniowego na stopie Inconel 600. Proces ten umożliwia wytworzenie dyfuzyjnych warstw austenitu azotowego z wydzieleniami azotku chromu (CrN) i tworzącymi się na powierzchni austenitu azotowego azotkami typu (Cr, Fe, Ni)N, które zapewniają dobrą odporność korozyjną i odporność na zużycie przez tarcie.

EN

Nickel alloys of Inconel 600 type that are currently applied in aircraft, chemical and power industries are characterized by good plasticity and oxidation resistance at high temperature. However, these alloys have low frictional wear resistance which may be eliminated by the application of surface treatment processes. Glow discharge assisted nitriding enables to produce diffusive layers that guarantee several times increase of hardness and improvement of corrosion resistance. The layers produced with the use of this method are characterized by complex structure and thus their microstructure needs to be analysed in detail which was taken up in this study. The paper describes the results of the examinations of microstructure, chemical and phase composition of layers produced on Inconel 600 alloy in the process of glow discharge assisted nitriding. This process enables to produce diffusive layers of nitrogen austenite with chromium nitride (CrN) precipitates and nitrides of (Cr, Fe, Ni)N type created on the surface of nitrogen austenite. These nitrides ensure good corrosion resistance and frictional wear resistance.

3

Zastosowanie MFM do opisu struktury warstw azotowanych jarzeniowo na stali Fe27Ni2TiAlMoNb

Borowski T., Jeleńkowski J., Wierzchoń T.

Inżynieria Materiałowa

|

2010

|

Vol. 31, nr 1

23-26

PL

W artykule scharakteryzowano właściwości magnetyczne i stabilność austenitu, martenzytu atermicznego i odkształceniowego stali Fe27Ni2TiAlMoNb a także austenitu azotowego (fazy S o rożnych stałych sieciowych), który tworzy się w czasie azotowania jarzeniowego poniżej temperatury As. Morfologi i analizę składników strukturalnych, tworzących się w procesie azotowania jarzeniowego, opisano, stosując mikroskop sił magnetycznych MFM, a do określenia składu fazowego wytworzonych warstw azotowanych zastosowano dyfraktometr rentgenowski.

EN

The paper analyzes the magnetic properties and stability of austenite, athermal martensite, and deformation martensite that form in Fe27Ni2TiAlMoNb steel subjected to glow discharge assisted nitriding, and also of nitrogen austenite (S phase with various lattice constants) which occurs when the nitriding process is conducted below the temperature As. The analysis of these structural components and their morphology was performed using a magnetic force microscope (MFM), whereas the phase composition of the nitrided layers produced on this steel was determined by X-ray diffraction.

4

Odporność korozyjna stali Ni27Ti2AlMoNb poddanej przemianie termicznej i odkształceniowej austenitu oraz azotowaniu jarzeniowemu

Borowski T., Brojanowska A., Kamiński J., Jeleńkowski J., Wierzchoń T.

Ochrona przed Korozją

|

2009

|

nr 4-5

193-197

PL

Stal wysokostopową Ni27Ti2AlMoNb o strukturze niestabilnego mechanicznie austenitu typu TRIP poddano nagniataniu ślizgowemu, co umożliwiło wytworzenie warstwy martenzytu odkształceniowego oraz przemianie atermicznej w ciekłym azocie w celu wytworzenia struktury martenzytycznoaustenitycznej o cechach struktury duplex. Stal o strukturze austenitycznej, duplexowej i z wytworzoną warstwą martenzytu poddano azotowaniu jarzeniowemu w temperaturze 450oC, co pozwoliło uzyskać warstwy o zróżnicowanej grubości i odporności korozyjnej. W badaniach struktury zastosowano elektronowy mikroskop skaningowy z detektorem elektronów wstecznie rozproszonych (BSE). W celu określenia odporności korozyjnej przeprowadzono badania potencjodynamiczne i impedancyjne. Wykazały one istotny wpływ zastosowanych technologii na odporność korozyjną.

EN

The high-alloy Ni27Ti2AlMoNb steel with a structure of mechanically instable austenite of the TRIP type was subjected to sliding burnishing, which resulted in the formation of deformation martensite, and to an athermal transformation in liquid nitrogen which gave a martensitic-austenitic structure with the features of a duplex structure. The untreated sample, the sample composed of austenite with a martensite zone, and the duplex martensite-austenite sample were subjected to glow discharge assisted nitriding at a temperature of 450oC. The nitriding yielded layers of various thicknesses and various corrosion resistances depending on the kind of the sample. The structure of the steel samples was examined in a scanning electron microscope equipped with a back-scattered electron detector (BSE). The corrosion resistance was determined using the potentiodynamic and impedance methods. The examinations have shown that all the treatments affect signifi cantly the corrosion resistance of the steel.