The influence of the temperature of plastic deformation on the structure and mechanical properties of copper alloys CuCo2Be and CuCo1Ni1Be

Ozgowicz W., Grzegorczyk B.

Archives of Materials Science and Engineering

2009

Vol. 39, nr 1

5-12

Purpose: The aim of the paper is to determine the influence of temperature of plastic deformation on the structure and mechanical properties of copper alloy of the CuCo2Be and CuCo1Ni1Be during a tensile test applied on electrodes to welders. Design/methodology/approach: The tensile test of the investigated copper alloys was realized in the temperature range of 20-800°C with a strain rate of 1.2⋅10-3s-1 on the universal testing machine. Metallographic observations of the structure were carried out on a light microscope and the fractographic investigation of fracture on an electron scanning microscope. Findings: The mechanical properties of alloys as well as the range of occurrence of the Portevin - Le Chatelier (PLC) phenomenon was determined on the basis of F-ΔL curves formed by tensile tests; however the character of fracture during the break of the samples was defined on the basis of fractographic investigations. Research limitations/implications: Practical implications: In result of tensile tests of copper alloys it has been found that the PLC effect occurs in both alloys in the temperature range of 150-350°C. However, the ductility minimum temperature of the alloys equals about 500°C. At the temperature of stretching of about 450°C the investigated copper alloys show maximum strength values. Originality/value: The type of "teething" on the load - displacement curves was defined, according to the classification received in literature. The dependence εkr = f(t) was marked too.