Microstructure characterization of welds in X5CrNiCuNb16-4 steel in overaged condition

Ziewiec A., Zielińska-Lipiec A., Kowalska J., Ziewiec K.

Advances in Materials Science

|

2019

|

Vol. 19, nr 1(59)

57--69

EN

The paper presents the results of the investigation of microstructure of the welded X5CrNiCuNb16-4 (17-4PH) steel after solution treatment and aging at 620°C for different periods. The microstructure and the phase composition of the steel was investigated using light microscopy (LM), scanning electron microscopy (SEM), energy dispersive spectrometry (EDS), transmission electron microscopy (TEM) and the X-ray diffraction (XRD). Hardness was measured for samples aged at different times. Density distributions of Cu precipitates were established. The investigation has shown that the microstructure of the X5CrNiCuNb16-4 steel welds after aging at 620 ° C consists of tempered martensite, fine Cu precipitates and austenite. It was observed that the size of the Cu precipitates increases with increasing the aging time, what affects the decrease of hardness. Simultaneously, the quantity of reversed austenite increases with increase of aging time. It was revealed that enrichment of the austenite in Ni, Cu and C affects the increase of Ms, but this factor does not determine the stability of austenite.

2

Kształtowanie odporności korozyjnej i odporności na zużycie przez tarcie stali martenzytycznej AISI 420F w niskotemperaturowych procesach azotowania jarzeniowego

Borowski T., Brojanowska A., Rudnicki J., Wierzchoń T.

Inżynieria Materiałowa

|

2010

|

Vol. 31, nr 4

889-892

PL

Nierdzewne stale martenzytyczne stosuje się na elementy, od których wymaga się dużej wytrzymałości mechanicznej, wysokiej odporności korozyjnej i odporności na zużycie przez tarcie. Są to m.in. zawory, czopy, łopatki turbin gazowych lub narzędzia do cięcia. W wielu przypadkach właściwości użytkowe tych stali nie są satysfakcjonujące. Przez wykorzystanie niskotemperaturowego azotowania jarzeniowego i dobór temperatury procesu można kształtować właściwości stali, wpływając na wzrost odporności na zużycie przez tarcie i odporności korozyjnej. Procesy azotowania jarzeniowego stali AISI 420F prowadzono w temperaturze 350, 400 i 450°C. Za pomocą skaningowego mikroskopu elektronowego wykonano badania mikrostruktury i morfologii wytworzonych warstw na przekroju poprzecznym. Przeprowadzono analizę składu chemicznego z zastosowaniem spektrometru rentgenowskiego z dyspersją energii oraz składu fazowego za pomocą dyfraktometru rentgenowskiego. Wykonano badania odporności na zużycie przez tarcie metodami "trzy wałeczki-stożek" i "rolka-klocek" oraz odporności korozyjnej metodą spektroskopii impedancyjnej i potencjodynamiczną. Uzyskane wyniki badań wykazują znaczący wpływ temperatury procesu azotowania jarzeniowego na właściwości warstwy powierzchniowej stali AISI 420F.

EN

Martensitic stainless steels are used for elements that must combine high mechanical strength with high corrosion and wear resistance. These are among others valves, pivots, gas turbine blades or cutting tools. In many cases functional properties of these steels are not satisfying. Application of low-temperature glow discharge assisted nitriding and a choice of proper process temperature allows for modifying steel properties improving its wear and corrosion resistance. In this project glow discharge assisted nitriding of AISI 420F steel was carried out at the temperatures of 350, 400 and 450°C. A cross-section analysis of microstructure and morphology of produced layers was made with the use of the scanning electron microscope. Examinations of chemical composition with the use of an energy-dispersive X-ray spectrometer as well as an analysis of phase composition with the use of X-ray diffractometer were made. Investigation of wear resistance with the use of "three rollers-taper" and "block-on-ring" methods as well as examinations of corrosion resistance with the use of impedance spectroscopy and potentiodynamic methods were carried out. The research results show a significant influence of glow discharge assisted nitriding process temperature on AISI 420F steel properties.

3

Ocena właściwości tribologicznych technologicznej warstwy wierzchniej azotowanej prożniowo nierdzewnej stali martenzytycznej utwardzanej wydzieleniowo

Rzepkowski A., Gawroński Z.

Inżynieria Materiałowa

|

2006

|

Vol. 27, nr 5

1200-1203

PL

W pracy przedstawiono, na przykładzie stali 17-4PH, właściwości tribologiczne TWW uzyskiwanej w wyniku azotowania próżniowego na nierdzewnych stalach martenzytycznych utwardzanych wydzieleniowo. Dokonano przeglądu i dyskusji przydatności standardowych prób tarcia oraz uzasadniono wykorzystanie do badań metody „Pin-on-Disk" wg. normy ASTM G99.

EN

For example of 17-4PH steel, tribological properties of precipitated hardening vacuum nitrided surface layer of maraging steels, is presented in this paper. Additionally, review of literature and discussion about standard friction tests was made. Moreover, provided justification of using Pin-on-Disc in conformity with the ASTM G 99 standard was presented.