Kinetics of oxidation of austenitic cast steels 30Ni-18Cr type with additions of Ti (0.03 and 0.9 wt. %) was studied. Specimens prior to oxidation were annealed at 900°C for 500 and 1000 hours. Continuous thermo-gravimetric measurements of oxidation process over 24 hrs in the air were implemented to determine the oxidation rate. Morphology and chemical composition of oxide layers was determined using X-ray diffractometry, scanning microscopy and EDS microanalysis. It has been shown that Ti additions significantly improve the oxidation resistance of these alloys and change the phase composition of the oxide layer.
PL
W pracy przedstawiono wyniki badań kinetyki utleniania staliwa austenitycznego typu 30Ni-18Cr z dodatkami Ti (0,03 i 0,93% mas.). Materiał do badań przed testem utleniania poddano procesowi wyżarzania w temperaturze 900°C przez 500 i 1000 godz. Pomiary kinetyki utleniania staliwa wykonano w atmosferze powietrza metodą termograwimetryczną ciągłą. Budowę morfologiczną i skład chemiczny warstw tlenkowych badano, wykorzystując metodę dyfrakcji rentgenowskiej, mikroskopii skaningowej oraz mikroanalizy rentgenowskiej. Wykazano, że dodatek tytanu obniża przyrost masy staliwa podczas utleniania i zmienia skład fazowy warstwy utlenionej.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.