Oxidation and creep behaviour of the CVD aluminized Rene 77 nickel-based superalloy

Ziaja W., Poręba M., Sieniawski J.

Inżynieria Materiałowa

2010

Vol. 31, nr 3

602-605

Low activity CVD process and heat treatment parameters were selected for nickel-base Rene 77 superalloy. As a result of the treatment aluminide coating with the depth of 35 ?m was formed. Disk-shaped specimens were cyclically oxidized in air at 982°C for 1000 h. Stress rupture tests were carried out at 982°C at the stress level of 124.0 and 151.7 MPa for the aluminized alloy and reference samples without the aluminide coating. Chemical and phase composition of the surface layer was examined after aluminizing and oxidation tests. It was found that aluminide coating improved oxidation resistance of Rene 77 superalloy without deterioration of its creep resistance at 982°C.

Wytworzono warstwę aluminidkową na nadstopie niklu Rene 77 w niskoaktywnym procesie CVD. Przyjęto schemat procesu aluminiowania w połączeniu z obróbką cieplną stopu. Wykonano badania odporności warstwy na cykliczne utlenianie w temperaturze 982°C w łącznym czasie 1000 h. Prowadzono próby przyspieszonego pełzania w temperaturze 982°C przy naprężeniu 124,0 i 151,7 MPa dla materiału bez warstwy oraz po aluminiowaniu. Wykonano badania składu chemicznego i fazowego warstwy wierzchniej po aluminiowaniu oraz po próbie utleniania cyklicznego. Stwierdzono, że wytworzona warstwa poprawiła odporność na utlenienie materiału podłoża - Rene 77, nie prowadząc do obniżenia odporności na pełzanie w temperaturze 982°C.