1

Hybrid nanocomposite layers Ni/Al2O3/C graphite produced by electrocrystallization method

Bartoszek W., Trzaska M.

Archives of Metallurgy and Materials

|

2019

|

Vol. 64, iss. 1

167--173

EN

The paper presents the results of studies of hybrid composite layers Ni/Al2O3/Cgraphite produced by the electrodeposition method. Three variants of hybrid composite layers were prepared in electrolyte solutions with the same amounts of each dispersion phases which were equal to 0.25; 0.50 and 0.75 g/dm3. The structure of Ni/Al2O3/Cgraphite layers as well as the Al2O3 and graphite powders, which were used as dispersion phases was investigated. The results of morphology and surface topography of produced layers are presented. The modulus of elasticity and microhardness of the material of produced layers were determined by DSI method. Tribological and corrosion resistance tests of produced layers were carried out. Realized studies have shown that the material of the produced layers is characterized by a nanocrystalline structure. Incorporation of dispersion phases into the nickiel matrix increases the degree of surface development of layers. Ni/Al2O3/Cgraphite layers are characterized by high hardness and abrasion resistance by friction, furthermore, they provide good corrosion protection for the substrate material.

2

Corrosion properties of Ni/Al2O3/Cgraphite hybrid composite layers

Bartoszek W., Cieślak G., Skroban K., Mazurek A., Trzaska M.

Ochrona przed Korozją

|

2018

|

nr 2

36--39

EN

The paper presents the results of studies of composite layers with nickel matrix and dispersed phase in the form of: alumina oxide (Al2O3) and graphite (Cgraphite) produced by electrodeposition on steel substrate. Three variants of composite layers were produced: Ni/Al2O3, Ni/Cgraphite, Ni/Al2O3/Cgraphite and for comparison purpose a nickel layer was also produced. Alumina oxide and graphite powders were used as dispersion phases. The dispersed phases were characterized by scanning electron microscopy (SEM) and Raman spectroscopy for graphite powder. The results of investigations of the structures of the produced layers with SEM, EDS, and results of Vickers hardness measurements as well as results of corrosion tests using electrochemical potentiodynamic method are presented. Damage characteristics after corrosion studies were obtained using a light microscope.

PL

W pracy przedstawiono wyniki badań warstw kompozytowych z niklową osnową oraz wbudowanymi w nią cząstkami faz dyspersyjnych w postaci: tlenku glinu (Al2O3) oraz grafitu (C grafit) wytwarzanych w procesie elektroosadzania na podłożu stalowym. Wytworzono trzy warianty powłok kompozytowych: Ni/Al2O3, Ni/C grafit, kompozytową warstwę hybrydową Ni/Al2O3/C grafit oraz w celach porównawczych warstwę niklową. Jako fazy dyspersyjne stosowano proszki Al2O3 oraz grafitu rozproszone w kąpieli Wattsa. Charakterystykę faz dyspersyjnych realizowano za pomocą skaningowej mikroskopii elektronowej (SEM) oraz spektroskopii Ramana dla proszku grafitu. Przedstawiono wyniki badań struktury oraz składu chemicznego wytworzonych warstw za pomocą SEM z przystawką EDS, wyniki pomiarów twardości metodą Vickersa, a także wyniki badań korozyjnych za pomocą elektrochemicznej metody potencjodynamicznej. Charakterystykę zniszczeń po badaniach korozyjnych dokonano za pomocą mikroskopu świetlnego.

3

Wpływ grubości warstw Ni-P osadzanych na stopie aluminium AW-7075 na ich adhezję i właściwości mechaniczne

Czapczyk K., Legutko S., Siwak P., Grochalski K., Mazurek A.

Inżynieria Powierzchni

|

2018

|

nr 1

18--26

PL

W artykule przedstawiono wyniki badań mechanicznych warstw Ni-P osadzonych metodą redukcji chemicznej na stopie aluminium AW-7075. Zbadano wpływ grubości warstw na twardość i mikrotwardość Vickersa, którą określono metodą DSI, oraz adhezję do podłoża metodą zarysowania. Przedstawiono morfologię za pomocą mikroskopii świetlnej oraz topografię badanych warstw przy użyciu profilometru metodą stykową. Zastosowano różne grubości w celu określenia ich wpływu na adhezję do stopu AW-7075. Wyniki badań pozwoliły stwierdzić, że warstwy Ni-P o większej grubości odznaczają się większymi wartościami twardości oraz modułu Younga niż cieńsze warstwy Ni-P, a także wykazują lepszą adhezję do stopu AW-7075.

EN

The article presents the results of mechanical tests of Ni-P layers deposited by the chemical reduction method on the AW-7075 aluminum alloy. The effect of layer thickness on hardness and microhardness of Vickers, which was determined by the DSI method, and their adhesion to the substrate by scratch method were investigated. The morphology was obtained using light microscopy and the topography of the examined layers using a contact profilometer. Different thicknesses were used to determine their effect on adhesion of the leyers to AW-7075 alloy. The results allowed to state that Ni-P layers of higher thickness are characterized by higher hardness and Young's modulus values than thinner Ni-P layers, and also show better adhesion to the AW-7075 alloy.

4

Nakładanie warstw niklowych na modele do odlewania precyzyjnego

Jesiotr M., Tarnowski M., Kucharska B., Myszka D., Wierzchoń T.

Prace Instytutu Odlewnictwa

|

2013

|

T. 53, z. 3

45--51

PL

W artykule przedstawiono sposób modyfikacji powierzchni form ceramicznych na granicy rozdziału model wytapiany - ceramika poprzez zastosowanie warstwy niklowej na jednorazowym modelu wykonanym z określonego rodzaju polimeru, np. polimetakrylanu metylu (PMMA), a następnie nałożenie na tak przygotowany model warstw formy ceramicznej. Kolejne fazy zakładają usunięcie modelu ze skorupy ceramicznej, tak aby metaliczna warstwa pozostała wewnątrz formy. Do przygotowanej w ten sposób formy, po procesie wyżarzania, możliwe będzie wlanie ciekłego metalu o określonej temperaturze topnienia, np. stopu aluminium. W ten sposób można będzie uzyskać wysokiej jakości powierzchnię odlewu, o określonej chropowatości i braku wad powierzchniowych. Hipotezą badawczą postawioną w artykule jest takie zaprojektowanie metalicznej powłoki w formie ceramicznej, aby uzyskać jej lepszą zwilżalność ciekłym metalem niż przy zastosowaniu konwencjonalnych technik odlewania precyzyjnego.

EN

The article presents a method of modification of ceramic mould surface on the boundary between lost-wax model - ceramics by using a layer of nickel on a disposable model made of a specified type of polymer e.g. polymethyl methacrylate (PMMA) and then applying the layers of a ceramic mould to such a model. Successive phases consist in removing the model from the ceramic shell so that the metallic layer remains in the mould. After annealing it will be possible to pour liquid metal of a specific melting point e.g. aluminium alloy, to a mould prepared in this way. This way it is possible to obtain a high quality casting surface, of certain roughness and lack of surface defects. The research hypothesis stated in the article is to design a metallic coating in a ceramic form to get better wettability with molten metal than when using conventional techniques of precision casting.

5

Studies of the structure and properties of Ni-P and Ni-P/Si3N4 surface layers deposited on aluminum by the electroless method

Trzaska M.

Journal of Achievements in Materials and Manufacturing Engineering

|

2010

|

Vol. 43, nr 1

269--275

EN

Purpose: The paper presents the results of studies on the structure and properties of the nickel Ni-P surface layers and composite Ni-P/Si3N4 surface layers deposited on the surfaces of aluminum 1200 (A2) and its 7075 (PA9) alloy by the electroless method. Design/methodology/approach: The aluminum substrate, the sample surfaces were treated by: degreasing, etching and zincking. The composite layers were produced from a disperse Si3N4 ceramic phase with an amorphous structure and nanometric size grains. Findings: The structure of the ceramic disperse phase Si3N4 and the layer materials was determined. The topography and morphology of the layers were examined. The content of the Si3N4 phase in the layer material was determined. The microhardness of the Ni-P and Ni-P/Si3N4 layers and of the substrate material was examined. The adhesion of the nickel phosphorus and composite layers to the aluminum substrate was determined. The results of studies of the corrosion resistance of the layers are presented. The anodic polarization characteristics, corrosion current densities and corrosion potentials were determined. The results of measurements of the impedance characteristics and the counterpart results obtained by modeling with the use of equivalent electrical circuits are presented. Both the nickel Ni-P and composite Ni-P/Si3N4 layers ensure excellent properties of the aluminum products. Practical implications: A good quality of final the nickel Ni-P surface layers and composite Ni-P/Si3N4 surface layers on the surfaces of aluminum are obtained. The surface layers are characterized by high hardness, frictional wear resistance and ensure excellent protection of the aluminum substrate against corrosion. Originality/value: The produced nickel and composite surface layers have show high hardness as well as very good resistances not only to corrosion but also to mechanical wear.

6

Ocena przyczyn dekohezji wybranych laminatów warstwowych na podstawie kryterium strukturalnego

Dąbrowski H.

Kompozyty

|

2006

|

R. 6, nr 4

71-74

PL

Opierając się na strukturalnym kryterium wytężenia, dokonano analizy przyczyn dekohezji laminatów warstwowych o wzmocnieniu krzyżowym [š30], [š45] oraz [0/90]. Ponieważ model strukturalny stosowany do analizy uwzględnia w opisie wytężenia laminatów wytrzymałość włókien osnowy i warstwy granicznej, wiec wytrzymałości tych elementów oraz ich zmiany zostały uwzględnione w rozważanych laminatach. Rozpatrzono modele laminatów, w których osnowa i warstwa graniczna wykazywały różne wartości wytrzymałości. Korzystając z modelu strukturalnego, oceniono naprężenia krytyczne powodujące wytężenie jednego z elementów struktury. Ocenę te przeprowadzono dla dróg obciążania zawartych w przedziale 0-360° na płaszczyźnie [sigma]x - [sigma]y. Przyjęto, że osiągnięcie jednego ze stanów krytycznych przez włókna, osnowę lub warstwę graniczną [1] jest równoznaczne z osiągnięciem stanu krytycznego przez laminat. Na podstawie obliczonych wartości naprężeń krytycznych sporządzono wykresy krzywych granicznych we współrzędnych [sigma]x - [sigma]y. Na wykresach tych zaznaczono również obszary, w których zawarte drogi obciążania powodują dekohezję danego elementu struktury. Stwierdzono, że przyczyna dekohezji zależy nie tylko od struktury laminatu, wytrzymałości jego elementów, ale także od drogi obciążania. Oceniono wpływ struktury (kierunków ułożenia warstw) oraz wytrzymałości wymienionych elementów struktury na przyczyny dekohezji badanych laminatów. Wyniki zilustrowano na wykresach.

EN

Phenomenological criterions, which are applied for estimation of the uniaxial strengthened layers oriented, require of strength tests of the layers. It makes difficult to use the laminates design and optimization processes of their structure elements. Additional defect of these applied criterions, which are used in method of elimination of layers is lack of information, which of them are the weakest elements and then undergo the decohesion process as the first links. It makes impossible to elaborate the method of the laminate strength properties improving the weakest element of its structure. It should be done during laminate structure design when structure elements are selected (fibers, warp and then- chemical treatment). The causes of fracture were identified in cross-reinforced (š30, š45, 0/90) ply laminates using a structural criterion. The model takes account of all the three material elements: fibres, matrix and phase interface, so strength characteristics and then- changes for all the three constituents were used in the analysis. Laminates with differing strengths of the matrix and the interface were considered. The structural model yielded critical stresses for each element. The analysis involved loading paths from the 0-360° range at the [sigma]x - [sigma]y plane. It was assumed that attaining a critical condition by the fibres, the matrix or the interface is equivalent to attaining the critical condition by the whole laminate. The computed critical stresses served as a basis for determining plots of limit curves in the [sigma]x- [sigma]y coordinates. In the plots the areas are marked that contain those loading paths which are responsible for damaging a particular structural element. It was found therefore that fracture in laminates is affected not only by their structure and strength of individual structural elements, but also by a loading path applied. Example plots show how the ply configuration and strength of individual structural elements determine types of fracture.

7

Influence of sintering temperature on decohesion of Al-(Al2O3)p composite modified with nickel.

Olszówka-Myalska A.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 5

683-686

EN

Aluminium matrix composite reinforced with alumina particles coated with nickel was investigated. Nickel layer of thickness less than 1 micrometer was deposited by chemical method on Al2O3 particles with 500 mesh granulation. Hot pressing in Degussa press was used to obtain composite materials. The decohesion of composite material depending on sintering temperature was analysed by SEM methods. Different mechanisms of composite decohesion were identified. The role of reactive bonding was analysed.

PL

Badano kompozyt z osnową aluminiową i cząstkami tlenku aluminium o granulacji 500 mesh pokrytymi metodą chemiczną warstwą niklu o grubości mniejszej od 1 mikrometra. Materiał otrzymano w wyniku prasowania na gorąco w prasie Degussa mieszaniny proszków. Metodami SEM analizowano wpływ temperatury spiekania na mechanizm dekohezji kompozytu. Stwierdzono występowanie różnych mechanizmów dekohezji oraz wpływ, powstałego na granicy cząstka-osnowa, połączenia reaktywnego.