Investigation of the Electromagnetic Shielding Effectiveness of Needle Punched Nonwoven Fabrics Produced from Stainless Steel and Carbon Fibres

Ozen M. S., Usta I., Yuksek M., Sancak E., Soin N.

Fibres & Textiles in Eastern Europe

2018

Vol. 26, no. 1 (127)

94--100

The electromagnetic shielding effectiveness (EMSE) of needle punched, nonwoven fabrics produced using staple stainless steel and carbon fibres was investigated. Utilising carding and large scale industrial type needle punching machines, webs of staple stainless steel and carbon fibres were produced, which were subsequently bonded on the needle punching machine at approximately 132 punches/cm2 and 13.5 mm needle penetration depth. The effect of varying the carbon fibre content was studied by varying the blend ratio of stainless steel and carbon fibres between 5-20%. EMSE measurements of as-produced needle punched nonwoven fabrics were carried out using the coaxial transmission line method (ASTM D4935-10) in the frequency range of 15-3000 MHz. Within the range, the EMSE values were enhanced from 22.3 dB (95/5, stainless steel/carbon) to 44.7 dB (80/20, stainless steel/carbon), which was attributed to the enhanced conductivity of the fabrics. In fact, the surface resistivity of the samples decreased from 5.80E + 3 Ω to 2.43E + 2 Ω, enhanced for 95:5 and 80:20 stainless steel/carbon blends.

Zbadano efektywność ekranowania elektromagnetycznego (EMSE) igłowanych włóknin wykonanych z wykorzystaniem stali nierdzewnej i włókien węglowych. Wytworzono włókniny ze stali nierdzewnej i włókien węglowych, które spajano na maszynie do igłowania przy około 132 uderzeniach / cm2 i głębokości penetracji 13,5 mm. Zbadano wpływ zmiany zawartości włókien węglowych poprzez zmianę stosunku mieszanki stali nierdzewnej i włókien węglowych w zakresie 5-20%. Pomiary EMSE wytwarzanych w ten sposób igłowanych włóknin wykonano metodą współosiowej linii transmisyjnej (ASTM D4935-10) w zakresie częstotliwości 15-3000 MHz. Stwierdzono, że wartości EMSE zostały zwiększone z 22,3 dB (95/5, stal nierdzewna / węgiel) do 44,7 dB (80/20, stal nierdzewna / węgiel), co zostało przypisane zwiększonej przewodności wyrobów.

Inter-/Intra-Laminar Reinforced Hybrid Fibre Composites by Needle Punching and Thermal Bonding: Evaluation of Mechanical and Static Puncture Properties

Li T.-T., Wang R., Lou C.-W., Pan Y.-J., Hsieh C.-T., Lin J.-H.

Fibres & Textiles in Eastern Europe

2016

Vol. 24, no. 4 (118)

84--91

This study comparatively presents the static puncture property of different structures of intra-/inter-laminar reinforced hybrid composites via needle punching and thermal bonding techniques. The tensile and bursting properties of two composites with inter-laminar reinforcement by needle-punching and inter-and-intra- laminar reinforcement by both needle punching and using Kevlar fibres were also evaluated comparatively. The significance of process parameters including the low-melting PET fibre content, take-up speed of the punching machine, the plied orientation between the nonwoven and fabric and thermal bonding on the static puncture resistance was firstly investigated to seek out the significant parameters. The effects of significant processing parameters on static puncture and mechanical properties were explored afterwards. The research result shows that the plied orientation, low-melting PET content and thermal bonding affect the static puncture resistance most significantly. The maximum tensile strength and bursting strength occurred when hybrid composites after thermal bonding were composed of parallel-plied nonwovens and 90°-orientated glass fabric, as well as 70 wt% low-melting PET fibres. Recycled Kevlar fibre reinforcement dissipates additional static puncture resistance, and makes the static puncture resistance higher, as well as the tensile and bursting strengths for resultant hybrid fibre composites. Employing recycled Kevlar fibres is economical for the fabrication of hybrid composites. Diversified economical hybrid composites will be applied as a wall interlayer or garment interlining in the future.

Przedstawiono porównawcze omówienie statycznej wytrzymałości na przebicie różnych hybrydowych kompozytowych wzmocnionych struktur laminarnych. Badano wytrzymałość na rozciąganie i przerwanie różnych wariantów kompozytów zarówno igłowanych jak i łączonych termicznie, w tym takich, w których stosowano do wzmocnienia włókna Kevlar. Badano istotność wpływu różnych parametrów na statyczną wytrzymałość na przebicie. Stwierdzono znaczny wpływ orientacji igłowania i zawartości niskotopliwego PET.