Wyniki wyszukiwania - BazTech

1

Use of Used Graphite Electrodes as Metal Matrix Composites Reinforcement

Łągiewka Małgorzata

Archives of Foundry Engineering

|

2024

|

Vol. 24, iss. 1

21--25

EN

The work presents the effect of the addition of graphite from recycled graphite electrodes on the mechanical properties of metal matrix composites (MMC) based on the AlMg10 alloy. A composite based on the AlMg10 alloy reinforced with natural graphite particles was also tested. Further, tests of the mechanical properties of the AlMg10 alloy were performed for comparative purposes. Composites with a particle content of 5, 10 and 15 percent by volume were produced by adding introduction of particles into the liquid matrix while mechanically mixing molten alloy. The composite suspensions were gravitationally cast into metal molds. Samples for the Rm , R 0.2, A and E tests were made from the prepared castings. Photos of the microstructures of the materials were also taken. The research shows that the addition of graphite to the matrix alloy causes minor changes in tensile strength (Rm) and yield strength (R 02), regardless of the type of graphite used. The results of the relative elongation tests showed that the introduction of graphite particles into the matrix alloy had an adverse effect on the elongation values in the case of each of the tested composites. The introduction of graphite particles into the AlMg10 alloy significantly increased the Young’s modulus value, both in the case of composites with flake graphite (natural) and graphite from ground graphite electrodes.

2

Struktura materiałów węglowych stosowanych do nawęglania żeliwa

Dobrzański L. A., Pawlyta M., Kwaśny W., Janerka K.

Karbo

|

2009

|

Nr 2

91-98

PL

Porównano struktury różnych typów nawęglaczy stosowanych w odlewnictwie. Specjalny nacisk położono na scharakteryzowanie stopnia uporządkowania struktury krystalicznej, na różnych poziomach organizacji badanych materiałów. Do badań struktury zastosowano rentgenowską analizę strukturalną, mikroskopię optyczną i wysokorozdzielczą skaningową mikroskopię elektronową. Wykazano, że dwa typy nawęglaczy (grafit naturalny i antracyt) charakteryzują się gładką i zwartą powierzchnią, podczas gdy dwa pozostałe (grafit syntetyczny i koks naftowy) posiadają porowatą, "wirowo-listkową" teksturę. W nanoskali wszystkie próbki są porowate. Na zdjęciach mikroskopowych grafitu naturalnego, grafitu syntetycznego i koksu naftowego zidentyfikowano cienkie, równolegle ułożone płatki lub listki grafitowe. Analizowane materiały różnią się stopniem uporządkowania struktury krystalicznej. Jednostki strukturalne grafitu naturalnego i grafitu syntetycznego są istotnie większe niż antracytu i koksu naftowego.

EN

Comparison has been performed of the structure of different kind of carburizers, commonly applied in foundry. Special emphasis was put on description of the order of crystal structure in nano-scale. Structure of carburizers were examined using X-ray diffraction, light microscopy and high-resolution scanning electron microscopy. It was found that two carburizers samples (natural graphite and anthracite) have smooth and compact surface, while two others (synthetic graphite and petroleum coke) are very porous and have "rotational-layered" structure. At nanoscale all samples are porous. With the exception of anthracite on SEM images thin, parallely arranged layers are visible. Analysed materials are different as regards structural order (determined by X-ray measurements): structural units of graphite samples are significantly larger than petroleum coke and anthracite samples.

3

Morfologia struktury kompozytu stop AK20 - grafit naturalny

Mitko M.

Krzepnięcie Metali i Stopów

|

2000

|

R. 2, nr 42

197--203

PL

W pracy przedstawiono metodykę oraz wyniki badań struktury kompozytu otrzymanego poprzez mieszanie a następnie prasowanie siluminu nadeutektycznego AK20 z cząstkami grafitu naturalnego. Badania struktury kompozytu obejmowały ocenę udziału cząstek grafitu, mikroskopię optyczną oraz mikroskopię skaningową przełomów. Nie stwierdzono występowania warstw przejściowych pomiędzy osnową metalową a cząstkami grafitu. Dobre połączenie adhezyjne uzyskano w wyniku dużej lepkości stopu w stanie ciekło-stałym (przy temperaturze ok. 610ºC) oraz stosowaniu dużych nacisków prasowania (300MPa).

EN

The methodology and results of composite structure were presented in this work. The hypoeutectic aluminium alloy AK20 as a matrix with natural graphite particles was prepared by mixing and squeeze casting in solid-liquid state. The examination of composite structure included: estimation of graphite particles fraction, optical microscopy and scanning microscopy of fractures. No interlayers between composite matrix and graphite patricles were found and adhesive connection has been obtained as result high viscosity of alloy in solidification range (610ºC) and high pressure during pressing (300 MPa).