Rheological properties of paste for self-compacting concrete with admixtures

Liu He, Duan Guangchao, Zhang Jingyi, Yang Yanhai

Archives of Civil Engineering

2022

Vol. 68, nr 3

585--599

The paste content in the self-compacting concrete is about 40% in unit volume. The rheological properties of paste directly determine the properties of self-compacting concrete. In this paper, the effect of silica fume (2, 3, 4, and 5%), limestone powder (5, 10 and 15%), and the viscosity modified admixture (2, 3, 4, 5, 6, and 7%) on the rheological properties were investigated. The effect of admixtures on shear thickening response was discussed based on the modified Bingham model. The results indicate that yield stress and plastic viscosity increased with increased silica fume and viscosity modified admixture replacement. The paste’s yield stress increases and then decreases with limestone powder replacement. The critical shear stress and minimum plastic viscosity are improved by silica fume and viscosity modifying admixture. The critical shear stress first increases and decreases as the limestone powder replacement increases. A reduction in the shear thickening response of paste was observed with silica fume and viscosity modified admixture replacement increase.

Influence of the 0.01at.% Ti addition on Zn Single crystals hardening in the (0001)<11-20> system

Mikułowski B., Boczkal G.

Archives of Metallurgy and Materials

2004

Vol. 49, iss. 1

37-42

Zn and ZnTi0.0l at.% single crystals were deformed in a compression test in the (0001)<11-20> system up to a gamma= 0.2 range at temperatures 77K, 150K, 293K, 373K, 473K. Two deforming rates were used; 10-4 S-1 and 10-3 s-1. On the base of obtained compression curves of the critical resolved shear stress CRSS, the hardening coefficient within the range of easy slip and activation volume V* were determined. A substantial impact of small additions of Ti (0.01at%) on the process of crystals strengthening was established. The CRSS value single crystals of pure Zn was changing within a range of 0.46MPa at 77K to 0.27MPa at 473K, wheras for ZnTi0.0l at.% it amounted respectively 1.96MPa i 0.87MPa. The hardening coefficient was changing respectively from 11.1 MPa to 0.97 MPa for Zn, and from 80.4 MPa to 7.2 MPa for ZnTi0.0l at.%. The activation volume V* was rising monotonically with temperature inside a range of 12.7 to 46 × 10-20 cm3 for ZnTi0.0l at.% and 2.1 to 9.8 × 1020 cm3 for Zn.

Monokryształy Zn oraz ZnTi0.01at% odkształcano w próbie ściskania w systemie (0001)<11-20> do zakresu gamma=0.2 w temperaturach 77K, 150K, 293K, 373K, 473K. Stosowano dwie prędkości odkształcenia; 10 do -4 s do-1 oraz 10 do -3 oraz 10 do -3 s do -1. Na podstawie uzyskanych krzywych ściskania wyznaczano krytyczne napreżenie ścinające KNS, współczynnik umocnienia w zakresie łatwego poslizgu oraz objetość aktywowaną. Stwierdzono silny wpływ niewielkich ilości dodatku Ti na proces umocnienia monokryształów Zn. Wielkość KNS dla monokryształów czystego Zn zmieniała się od 0.46 Mpa w 77K do 0.27b MPa w 473K, natomiast dla monokryształów ZnTi0.01at.% wynosiła 1.96 MPa i 0.87 MPa. Wspołczynnik umocnienia zmieniał się odpowiednio 11.1 MPa do 0.97 MPa dla Zn oraz 80.4 MPa do 7.2 MPa dla ZnTi0.01at.%. Objetość aktywowana wazrastał monotonicznie wraz z temperaturą w zakresie 12.7 do 46x10 do -20 cm sześc. dla ZnTi0.01at.% oraz 2.1 do 9.8x10 do -20 cm sześć. dla Zn.