Wyniki wyszukiwania - BazTech

1

Structured Analysis of Nanostructured Zinc Oxide (ZnO) Thin Films Deposited by Sol-Gel

Hussin Rosniza, Hanafi F., Rashid R. A., Harun Z., Kamdi Z., Ibrahim S. A., Ainuddin A. R., Rahman W., Leman A. M.

Archives of Metallurgy and Materials

|

2022

|

Vol. 67, iss. 3

1055--1060

EN

In this work, zinc oxide (ZnO) thin films are deposited on glass substrate using the sol-gel spin coating technique. The effect of annealing temperature on structural properties was investigated. The ZnO sol-gel was produced from zinc acetate dehydrate as the starting material with iso-propanol alcohol as the stabilizer. The ratio was controlled, distilled water and diethanolamine as the solvent mixing on a magnetic stirrer for an hour under constant heat of 60°C. The ZnO thin film was deposited using the spin coating technique with the speed of 3000 rpm for 30 minutes before the sample undergoes pre-heat in the oven at the temperature of 100°C for 10 minutes. The sample was annealing in the furnace for an hour at 200°C, 350°C, and 500°C. The X-ray diffraction (XRD) analysis confirms that hexagonal wurtzite structure with zincite and zinc acetate hydroxide hydrate composition. The thin films surface roughness was analyzed using an atomic force microscope (AFM) and scanning electron microscope (SEM) for surface morphology observation.

2

Advances in CZTS thin films and nanostructured

Ali N., Ahmed R., Bakhtiar-Ul-Haq, Shaari A.

Opto-Electronics Review

|

2015

|

Vol. 23, No. 2

137-142

EN

Already published data for the optical band gap (Eg) of thin films and nanostructured copper zinc tin sulphide (CZTS) have been reviewed and combined. The vacuum (physical) and non-vacuum (chemical) processes are focused in the study for band gap comparison. The results are accumulated for thin films and nanostructured in different tables. It is inferred from the review that the nanostructured material has plenty of worth by engineering the band gap for capturing the maximum photons from solar spectrum.

3

Odporność kawitacyjna systemów Z powłokami TiN

Krella Alicja K.

Inżynieria Materiałowa

|

2013

|

Vol. 34, nr 1

19--24

PL

W pracy przedstawiono wyniki badań doświadczalnych erozji kawitacyjnej powłok TiN o zróżnicowanej grubości, osadzonych na różne podłoża (stal X6CrNiTi18-10 i X39Cr1 3) metodą katodowego osadzania łukowego (ARC) PVD. Stal X39Crl3 hartowano, a następnie odpuszczano w 600 i 400°C w celu uzyskania podłoży o zróżnicowanych własnościach mechanicznych. Badania erozyjne przeprowadzono na stanowisku ze szczelinowym wzbudnikiem kawitacji. Celem badań było określenie wpływu podłoża oraz grubości powłok na odporność kawitacyjną całego systemu areolgicznego oraz weryﬁkacja wskaźnika odporności RCAV systemów twarda powłoka-stalowe podłoże na niszczenie kawitacyjne. W pracy wykazano, że osadzenie twardych powłok TiN na stalowych podłożach przyczyniło się do spadku ubytku masy w porównaniu z ubytkami masy powstałymi na stalach bez powłok TiN. Wzrost grubości powłok TiN osłabił pozytywny efekt ich nałożenia. Wyniki badań doświadczalnych pozytywnie zweryﬁkowały wskaźnik RCAV wyrażony wzorem (1) - parametr odporności systemów twarda powłoka-stalowe podłoże na niszczenie kawitacyjne. Uzyskane wyniki świadczą, że wskaźnik RC,V bardzo dobrze określa odporność kawitacyjną systemów twarda TiN powłoka-stalowe podłoże niezależnie od grubości powłoki i własności podłoży.

EN

The results ofcavitation erosion tests ofTiN coatings with various thicknesses deposited on various substrates (X6CrNiTi18-10 and X39Cr13) by means ofthe cathodic arc evaporation (ARC) PVD method are presented. X3 9Crl3 steel was subjected to various thermal treatment in order to obtain substrates ofdifferent properties. The cavitation erosion tests were performed in a cavitation tunnel with a slot cavitator. The purpose of this work is to assess the inﬁuence of the substrate properties and coating thickness on the cavitation erosion resistance of the whole hard coating-steel substrate system and veriﬁcation ofthe cavitation erosion resistance parameter RCAV The depositions ofTiN coatings on a steel substrate have caused improvement of the cavitation erosion resistance (Fig. 1). An increase in the coating thickness reduces the positive effect of TiN coatings deposition. The experimental data positively veriﬁed the resistance parameter, RCAV (Fig. 3). This shows that the RCAV parameter very well describes the cavitation erosion resistance of hard TiN coatings-steel substrate systems regardless of the coating thickness or properties ofthe steel used as substrates.

4

Protective coatings based on Zr-Ti-Si-N their physical and mechanical properties and phase composition

Kirik G., Kozak C., Opielak M.

Przegląd Elektrotechniczny

|

2012

|

R. 88, nr 10a

319-321

EN

Hard and super hard coatings of Zr-Ti-Si-N of from 2.8 to 3.5 um thickness were fabricated using vacuum arc source with (HF) stimulation. Six series of samples with various Zr and Ti content were studied. The samples were annealed in vacuum and in air at 1200oC. It was found that films with a high Zr and Ti content were thermally stable up to 1180 C. At the same time, a thin oxide layer of 180 to 240nm was found in the surfaces, which protected the sample from destruction. A size of grains of a substitution solid solution (Zr, Ti)N varied from (10 – 12)nm to 25nm, but Ti concentration in the solid solution increased. In the process of annealing, hardness of the best series of samples increased from 39.6 š 1.4GPa to 53.6GPa, which seemed to indicate that a spinodal segregation along grain interfaces was finished. Tribotechnical characteristics of coatings were measured for various contents of basic elements Zr, Ti, and Si. The work was funded by the project of NAS of Ukraine “Nanomaterials, Nanotechnologies, Nanosystems”.

PL

Twarde i supertwarde powłoki Zr-Ti-Si-N o grubości od 2,8 do 3,5 um zostały wytworzone wykorzystując próżniowe źrodło łuku ze stymulacj. HF. Przebadano sześć serii próbek o rożnej zawartości Zr oraz Ti. Próbki zostały wygrzane w prożni i w powietrzu w temperaturze 1200 C. Wykazano, że warstwy z wysoką zawartości. Zr oraz Ti były stabilne termicznie do temperatury 1180 C. W tym samym czasie cienka warstwa tlenku o grubości od 180 do 240nm została zidentyfikowana w obrębie powierzchni, które ochraniały próbkę przed zniszczeniem. Rozmiar ziaren substytutu roztworu stałego (Zr, Ti)N zmieniał się od (10 . 12)nm do 25nm, jednakże koncentracja Ti w roztworze stałym wzrastała. W procesie wygrzewania twardość najlepszej serii próbek wzrosła od 39,6 +- 1,4GPa do 53,6GPa, co wydaje się wskazywać, że oddzielanie spinodalne wzdłuż interfejsu ziaren zostało zakończone. Charakterystyki trybo techniczne powłok zostały zmierzone dla różnych zawartości podstawowych pierwiastków Zr, Ti, oraz Si. Badania zostały sfinansowane ze środków ukraińskiego projektu NAS "Nanomateriały, Nanotechnologie, Nanosystemy". (Powłoki ochronne wytworzone w oparciu o Zr-Ti-Si-N . właściwości mechaniczne i skład fazowy).

5

Deformation behavior of 2017 nanostructured aluminium alloy

Wiśniewska-Weinert H., Leshchynsky V., Borowski J., Lewandowska M., Kulczyk M., Pachla W.

Inżynieria Materiałowa

|

2012

|

Vol. 33, nr 6

530--534

EN

The paper contains the results of investigation of nanocrystalline aluminium alloy 2017. The possibility of forming those materials obtained by the method of hydrostatic extrusion, depending on the temperature and deforming velocity has been determined. Hydrostatic extrusion process with cumulative true strain 3.79 applied to 2017 aluminum alloy leads to significant grains size refinement to the nanometric scale. The 2017 aluminium alloy with nanometric structure can be successfully formed 200°C and above. The results obtained indicate that deformation at those parameters does not cause discontinuities. Plastic forming above 200°C causes noticeable grain growth and the determined average grain diameters are in the submicron range, even for compression temperature of 300°C.

PL

Praca zawiera wyniki badań nanokrystalicznego stopu aluminium 2017. Określono możliwość kształtowania tych materiałów otrzymanych metodą wyciskania hydrostatycznego w zależności od temperatury i prędkości odkształcenia. Hydrostatyczne wyciskanie stopu aluminium 2017 z kumulacją umocnienia 3,79 prowadzi do znaczącego rozdrobnienia ziaren do skali nanometrycznej. Stop aluminium 2017 o strukturze nanometrycznej można z powodzeniem kształtować w temperaturze 200°C i wyższej. Otrzymane wyniki wskazują, że odkształcanie przy tych parametrach nie powoduje powstania nieciągłości. Kształtowanie plastyczne w temperaturze wyższej niż 200°C powoduje zauważalny rozrost ziarna, a wyznaczone średnie średnice ziarna są w zakresie submikronowym nawet dla temperatury ściskania 300°C.