Magnetoelastic properties of Fe73.5-xCoxNb3Cu1Si13.5B9 alloys in nanocrystalline state.

Szewczyk R., Kolano-Burian A., Bieńkowski A., Kulik T., Salach J.

Archives of Materials Science

2004

Vol. 25, nr 4

485-491

This paper presents experimental results of the magnetic and magnoelastic properties of the Fe73.5-xCoxNb3Cu1Si13.5B9 (x=20, 40, 50) alloys in the nanocrystalline state. In the magnetoelastic investigation the compressive stress was applied to the ring core perpendicularly to the magnetizing field direction. Significant influence of cobalt addiction on both stress dependence of hysteresis as well as on stress-induced changes of flux density (for constant value of magnetizing field) were observed.

Microstructure and mechanical properties of nanocrystalline Ni3Al.

Pakieła Z., Zieliński W., Korznikov A.V., Kurzydłowski K.J.

Inżynieria Materiałowa

2001

R. XXII, nr 5

698-701

The influence of a grain size and long-range ordering on mechanical properties of the intermetallic compound Ni3Al at room temperature was investigated. It has been found that the maximum values of strength and ductility are observed in the material in a completely disordered nanocrystalline state.

W pracy przedstawiono wyniki badań wpływu wielkości ziarna i uporządkowania dalekiego zasięgu w fazie międzymetalicznej Ni3Al na właściwości mechaniczne. Stwierdzono, że maksymalną wytrzymałość i plastyczność ma materiał nanokrystaliczny, pozbawiony uporządkowania dalekiego zasięgu.