Wyniki wyszukiwania - BazTech

1

Bimetal Castings with a Titanium Working Layer

Dulska Agnieszka

Archives of Foundry Engineering

|

2023

|

Vol. 23, iss. 2

21--28

EN

The paper presents the technology of bimetallic castings using the casting method of applying layers directly during the casting process. The bimetallic casting consists of a load-bearing part (typical casting material, i.e. gray cast iron with flake graphite) and a working part (titanium insert). The titanium insert was made by printing using the selective laser melting (SLM) method, and its shape was spatial. The verification of the bimetallic castings was carried out mainly based on metallographic tests, temperature and thickness measurements. Structure examinations containing metallographic microscopic studies with the use of a light microscope (LOM) and a scanning electron microscope (SEM) with microanalysis of the chemical composition (energy dispersive spectroscopy - EDS).The aim of the tests was to select the appropriate geometrical insert parameters for bimetallic castings within the tested range. The correct parameters of both the insert, pouring temperature and the casting modulus affect the diffusion processes and, consequently, the formation of carbides and the creation of bimetallic castings.

2

Rezystancyjne przygrzewanie warstw z użyciem proszku WC-Co

Bartnik Z.

Spajanie Materiałów Konstrukcyjnych

|

2008

|

Nr 2 (2)

14--17

PL

Zużycie powierzchni roboczych współpracujących elementów maszyn wiąże się z obniżeniem ich właściwości użytkowych. Spośród spawalniczych metody nakładania warstw na powierzchnie robocze metoda przegrzewania rezystancyjnego stwarza możliwość uzyskania warstw o szerokim przedziale właściwości. Jednym ze sposobów ich uzyskania jest sterowany dobór materiałów na warstwę w postaci proszków czystych metali, stopowych czy kompozytowych, pozwalający na uzyskanie warstwy o pożądanej twardości i ciągłości metalicznej z podłożem. Ponadto znikoma ilość wydzielanych gazów czy dymów w trakcie procesów przygrzewania warstw czyni tę metodę przychylną środowisku naturalnemu.

3

Model nagrzewania ziaren w procesie rezystancyjnego nakładania warstw

Bartnik Z., Zimniak Z.

Przegląd Spawalnictwa

|

2008

|

R. 80, nr 7

21-24

PL

Przedstawiono symulacje MES procesu nagrzewania warstwy ziaren proszku niklu na podłożu z blachy stalowej, ściskanych dwoma miedzianymi elektrodami. Celem modelowania matematycznego był dobór podstawowych parametrów procesu, dla uzyskania pożądanej warstwy wykazującej ciągłość metaliczną z podłożem. Wyniki symulacji numerycznych porównano z zarejestrowanymi obrazami termowizyjnymi.

EN

The compression of nickel powder subjected to resistance heating on a steel base between two copper electrodes was FEM simulated. The aim of the mathematical modelling of the facing process was to identify the parameters which for the physical properties of the materials used for the facing and the base allow one to obtain a high quality facing continuous with the base. The numerical simulation results are compared with experimental results recorded by the thermovision camera.

4

Cienkie warstwy germanowo-węglowe

Szymanowski H., Gazicki M.

Inżynieria Materiałowa

|

2000

|

R. XXI, nr 3

127-129

PL

W ostatnich latach wzrasta zainteresowanie cienkimi warstwami zawierającymi atomy germanu. Cenne właściwości, jak i łatwość plazmowego procesu nakładania powodują gwałtowny rozwój badań tych materiałów. Prezentowana praca zawiera skrót wyników badań prowadzonych przez naszą grupę w ciągu ostatnich kilku lat. Badania te prowadzone były w dwóch kierunkach: 1 - badania mechanizmu nakładania, wyjaśnienia reakcji chemicznych zachodzących w wyładowaniu, powiązaniu mechanizmu procesu z warunkami jego prowadzenia; 2 - badania struktury cienkich warstw, wyjaśnienie ich budowy chemicznej w zależności od warunków powstawania. Zastosowano nowoczesne techniki badawcze. Spektrometria masowa i emisyjna spektroskopia optyczna jako jedne z nielicznych technik umożliwiły prowadzenie badań w trakcie procesu nakładania. Badania FTIR oraz rezonansu magnetycznego ciała stałego C13 pozwoliły na zbadanie struktury chemicznej otrzymanych warstw.

EN

Optical emission spectroscopy (OES) and quadrupole mass spectrometry (QMS) have been applied to the characterization of RF plasma of organogermanium used for the deposition of a-GexCy:H films. QMS analysis show that under low power input condition, the gas phase consists primarily of monomer molecules and their largest fragments. In contrast, at high power input tetraethylgermanium undergoes nearly complete fragmentation forming atomic germanium, atomic and molecular hydrogen, and a number of hydrocarbon species. A dramatic increase of molecular hydrogen concentration with the increasing RF power is confirmed by OES actinometric measurements. Fourier transform infrared spectroscopy of a series carbon-germanium films are presented. It is shows that IR absorption of the films varies dramatically depending on the RF power. Various C-H bands as well as strong Ge-O absorption are characteristic for samples produced at low power. Films deposited at hogh RF power conditions are characterized by a lack of Ge-O signals, considerable Ge-H absorption and substantial broadening of all bands.