Microstructure and oxidation resistance of an aluminide coating on the nickel based superalloy Mar M247 deposited by the CVD aluminizing process

Zielińska M., Zagula-Yavorska M., Sieniawski J., Filip R.

Archives of Metallurgy and Materials

|

2013

|

Vol. 58, iss. 3

697--701

EN

An investigation was conducted to synthesize βNiAl coating on the nickel based superalloy Mar M247 in a chemical vapor deposition process (CVD). The low activity process of aluminizing was carried out for 8 hours at the temperature 1050°C. Surface morphology and cross-section microstructure of the diffusion coating were studied and compared by using an optical microscope, a scanning electron microscope (SEM) equipped with energy dispersive spectroscopy and an X-ray diffractometer. It was found that aluminide coating with the thickness of 37 μm consisted of two layers: an outer one and the inner interdiffusion one. The outer layer consists of single phase βNiAl. The inner one, consisted of βNiAl phase and carbides: MC and M23 C6 types which were originally present in the substrate. Cyclic oxidation test was performed at 1000°C for 1000h in the air atmosphere. The aluminized samples exhibited a small mass increase and the α- Al2 O3 oxide formed during oxidation test had a good adherence to the coating. The decrease of aluminum content in the coating with the prolongation of the oxidation time and the phase transformation of βNiAl to γ’ Ni3 Al and to γNi solid solution were observed. The samples without the coating showed a strong mass decrease in comparison to the coated samples.

XX

Niskoaktywny proces aluminiowania prowadzono w temperaturze 1050°C i w czasie 8 h. Badania mikrostruktury na przekroju oraz powierzchni warstwy dyfuzyjnej prowadzono za pomoca mikroskopu optycznego oraz skaningowego mikroskopu elektronowego wyposażonego w detektor EDS. Skład fazowy określano metodą rentgenowskiej analizy fazowej. Uzyskano warstwę aluminidkową o grubości 37 μm składająca się z dwóch stref: zewnętrznej oraz wewnętrznej (dyfuzyjnej). Strefa zewnętrzna składa się z fazy βNiAl. Natomiast wewnętrzna - z fazy βNiAl oraz węglików typu MC oraz M23C6. Badania cyklicznego utleniania prowadzono w temperaturze 1000°C i w czasie 1000 h w atmosferze powietrza. Podczas utleniania warstwy aluminidkowej powstaje tlenek α-Al2O3 o dobrej przyczepności do warstwy dyfuzyjnej. Zwiększenie czasu utleniania od o do 1000 h powoduje zmniejszenie zawartości aluminium oraz przemianę fazową β-NiAl do γ’-Ni3Al i do stałego roztworu γ-Ni. Materiał bez warstwy aluminidkowej charakteryzuje się większą szybkością utleniania w porównaniu do materiału z warstwą aluminidkową.

2

Application of a quantitative materialography methods for an evaluation of a structure repeatability of turbine blades made of MAR M247 nickel-based superalloy

Szczotok A., Cwajna J., Maliński M.

Inżynieria Materiałowa

|

2008

|

Vol. 29, nr 4

362-366

EN

The results of studies on inhomogeneity of gas and shrinkage pores volume fraction, size and shape (Tab. 1) as well as size and shape of grains (Tab. 3) revealed during macroscopic analysis of experimental low pressure turbine blades of a jet engine made of MAR M247 nickel-based superalloy were characterized in the present work. The procedures of macro- and microstructure evaluation described in the work [1] were applied during the investigations to check if a worked out and improved within the framework of a project [2] technology of the blades precision casting ensured their repeatable macro- and microstructure. The blades placed in a casting mould at a various distance from a sprue (Fig. 1) and blades from various casting moulds poured into with a remelted liquid metal from various rods of the same master heat were evaluated. The repeatability of their macro- and microstructure was checked because it was an elementary condition of their properties repeatability.

PL

W pracy opisano wyniki badań niejednorodności udziału objętościowego, wielkości i kształtu porów gazowych i skurczowych (tab. 1) oraz wielkości i kształtu ziaren pierwotnych (tab. 3) ujawnionych w badaniach makroskopowych łopatek doświadczalnych turbiny niskiego ciśnienia silnika odrzutowego z nadstopu niklu MAR M247. W badaniach wykorzystano procedury opisu makro- i mikrostruktury łopatek opisane w pracy [1] w celu sprawdzenia, czy opracowana i doskonalona w ramach projektu [2] technologia precyzyjnego odlewania łopatek zapewniła powtarzalną ich makro- i mikrostrukturę. Ocenie poddano łopatki rozmieszczone w zestawie odlewniczym w różnej odległości od wlewu głównego (rys. 1) oraz łopatki pobrane z różnych form odlewniczych zalewanych ciekłym metalem przetopionym z różnych prętów tego samego stopu wsadowego. Sprawdzano czy mają one powtarzalną makro-i mikrostrukturę, co stanowi podstawowy warunek powtarzalności ich właściwości.

3

Revealing and evaluation of carbides in MAR M247 Ni based superalloy

Szczotok A.

Inżynieria Materiałowa

|

2007

|

Vol. 28, nr 3-4

468-471

EN

The work presents carbide phases occurring in a structure of MAR M247 Ni based superalloy. The ways of revealing these phases and results of using optical, scanning electron and transmission microscopy as well as X-ray phase analysis for researches are presented (Fig. 1 + 10). The author's attention has been concentrated on the carbides morphology and places of occurrence.

PL

W pracy przedstawiono fazy węglikowe występujące w strukturze nadstopu niklu MAR M247. Przedstawiono sposoby ujawniania tych faz i zaprezentowano wyniki zastosowania do badań mikroskopii optycznej, elektronowej skaningowej i transmisyjnej oraz rentgenowskiej analizy fazowej (rys. 1÷10). Skoncentrowano się na morfologii i miejscach występowania węglików.