Multi-criteria diagnostics of historic buildings with the use of 3D laser scanning (a case study)

Szymczak-Graczyk Anna, Walczak Zbigniew, Ksit Barbara, Szyguła Zdzisław

Bulletin of the Polish Academy of Sciences. Technical Sciences

2022

Vol. 70, nr 2

art. no. e140373

The protection and use of historic buildings is a difficult and costly task. Most often, these objects are under conservatory protection and any interference in their structure requires appropriate consent. On the other hand, conducting construction works on historic buildings carries a high risk of their damage or even destruction. Therefore, proper prior diagnostics is an extremely important factor affecting the scope and manner of works to be conducted. The paper presents the use of 3D scanning to determine the deflection of the ceiling under the Column Hall of the historic Palace, the floor of which showed elasticity, recorded during changing service loads. After identifying the places with the greatest deflections, based on data from 3D laser scanning, test holes were made and wood samples from the ceiling were taken to perform moisture content and mycological tests. An endoscopic inspection camera was inserted into test holes, providing the basis for recognizing the structure of the ceiling, i.e. arrangement of layers as well as dimensions and spacing of ceiling beams. Strength calculations were made with the limit state method resulted in the determination of the maximum permissible service load on the ceiling. The presented course of action in diagnostics of the analysed historic building may be an example of a preliminary procedure to be taken before deciding on changes in the manner of use of historic buildings or the functionalities of their individual parts.

Resistance of polypropylene-wood composites to fungi

Cofta G., Borysiak S., Doczekalska B., Garbarczyk J.

Polimery

2006

T. 51, nr 4

276-279

In the present study, the composites of polypropylene and wood were prepared. The experimental material comprised two most common Polish timber species pine wood (Pinus sylvestris L.) as a softwood species and oak wood (Quercus sp.) as a hardwood species. The size of wood sawdust ranged from 0.5 to 1.0 mm. Two types of lignocellulosic materials were used in the experiments described: wood without any previous chemical treatment and wood after its mercerization (i.e. activated with NaOH). In addition the polypropylene-wood composite containing a block copolymer, i.e. styrene-ethylene-butylene-styrene (SEBS) was also obtained. The objective of this study was to evaluate the resistance of different kinds of polypropylene-wood composites to fungal decay. Weight losses and temporary tensile strength of composite samples after the mycological test were determined.

Metodą wytłaczania i prasowania wytworzono kompozyty izotaktyczne polipropylen-drewno. W badaniach wykorzystano dwa gatunki drewna: sosnowe (Pinus sylvestris L.) i dębowe (Quercus sp.). W pracy stosowano drewno surowe oraz drewno po procesie merceryzacji, tj. po aktywowaniu wodnym roztworem NaOH. Wytworzono również kompozyty polipropylen-drewno z dodatkiem kopolimeru blokowego styren-etylen-butylen-styren (SEBS). Badano odporność uzyskanych kompozytów na rozkład powodowany przez grzyby degradujące tkankę drzewną (Coniophora puteana i Coriolus versicolor). W celu oceny stopnia biorozkładu po upływie 16 tygodni wyznaczano ubytki masy próbek kompozytów oraz badano ich wytrzymałość na rozciąganie. Stwierdzono, że ubytki masy (rys. 1) wszystkich wariantów kompozytów wynosiły poniżej 1,8 %. Uzyskane wartości mieszczą się w granicach błędu pomiaru. Stwierdzono, że wytrzymałość na rozciąganie (rys. 2) jest bardziej dokładnym kryterium biorozkładu. Obniżenie wytrzymałości na rozciąganie od 12 do 20 % stwierdzono w przypadku kompozytów na bazie drewna sosnowego, a niewielkie zmiany (do 5 %) w przypadku kompozytów z drewna dębowego. Natomiast najmniejszą wytrzymałość na zerwanie wykazywały kompozyty z dodatkiem środka kompatibilizującego (SEBS). Badania dowiodły, że możliwa jest biodegradacja drewna w matrycy polipropylenowej, pod warunkiem zapewniania dostępu strzępek grzybni do materiału lignocelulozowego w kompozycie.