Research of factors influencing the quality of imprints lamination

Havenko Svitlana, Dovhanych Anna

Przegląd Papierniczy

|

2021

|

R. 77, nr 11

614--617

EN

Factors influencing the quality of offset imprints lamination are described. The influence of the morphological structure of the imprints surface on the quality of lamination with polypropylene films has been established. It is proved that the roughness of the imprint surface significantly affects the strength of lamination: the smoother the surface, the weaker is the bonding with the imprint. To objectively assess the adhesive interaction of the adhesive with the paper and the polymer film during lamination, the hardening factor of the “imprint-film” system was introduced. It is confirmed that with increasing lamination temperature the amount of twists of laminates increases, and with increasing speed of lamination the twist of laminates decreases. As a result of optimization, the three-dimensional model which confirms interrelation of mode (temperature and speed) and technological (weight, imprint’s surface structure) factors influencing quality of lamination is constructed.

PL

Omówiono czynniki wpływające na jakość laminowania nadruku offsetowego. Stwierdzono wpływ budowy morfologicznej powierzchni nadruków na jakość laminowania foliami polipropylenowymi. Udowodniono, że chropowatość powierzchni nadruku znacząco wpływa na wytrzymałość laminowania: im gładsza powierzchnia odbitku, tym słabsze wiązanie powstałe podczas laminowania. Wprowadzono współczynnik wzmocnienia systemu „nadruk-folia” do obiektywnej oceny przyczepności nadruku do folii polimerowej podczas laminowania. Potwierdzono, że wraz ze wzrostem temperatury laminowania zwiększa się skręcenie laminatów, a wraz ze wzrostem prędkości – maleje. W wyniku optymalizacji powstaje trójwymiarowy model, który potwierdza wpływ czynników technologicznych (temperatury i prędkości laminowania, masy, struktury powierzchni odbitek) na jakość laminowania.

2

Struktura i właściwości materiałów hybrydowych gips - polimer - woda

Mucha Maria, Mucha Jarosław

Materiały Budowlane

|

2021

|

nr 10

35--37

PL

Badania prezentowane w artykule miały na celu określenie wpływu polimerów rozpuszczalnych w wodzie na właściwości gipsu. Zestalanie gipsu obejmuje uwodnienie i krystalizację oraz utworzenie filmu polimerowego w porach materiału. Te procesy są badane różnymi metodami, takimi jak pomiary zestalania, właściwości mechaniczne, mikroskopia elektronowa, różnicowa kalorymetria skaningowa i inne. Dodatki polimerowe działają przede wszystkim jako opóźniacze procesu zestalania gipsu, powodując zmianę właściwości mechanicznych w wyniku modyfikacji jego struktury morfologicznej. Mechanizm wzrostu kryształów gipsu podczas uwodnienia półwodnego siarczanu wapnia jest procesem kontrolowanym przez nukleację (równania Avramiego).

EN

The study presented in this article is focused on the influence of water soluble polymers on gypsum properties. Gypsum setting involves: gypsum hydration – crystallization and formation of polymer film in material pores. The processes are studied by various methods such as setting and mechanical measurements, scanning electron microscopy, differential scanning calorimetry and others. Polymer additives act first of all as a retarder of setting and change mechanical properties of material due to modification of its morphological structure. The mechanism of gypsum crystal grow during hydration of chemihydrate calcium sulfate was predicted to be nucleation control process (Avrami equation was applied).

3

Properties and Structure of Cellulosic Membranes Obtained from Solutions in Ionic Liquids Coagulated in Primary Alcohols

Fryczkowska B., Kowalska M., Biniaś D., Ślusarczyk C., Janicki J., Sarna E., Wyszomirski M.

Autex Research Journal

|

2018

|

Vol. 18, no. 3

232--242

EN

This paper presents the results of studies on the preparation of cellulosic membranes, from a solution in 1-ethyl-3- methylimidazolium acetate (EMIMAc), using the phase inversion method. Initially, the membranes were obtained by coagulation of the polymer film in water and primary alcohols (methanol, ethanol, 1-propanol, 1-butanol, 1-pentanol), 1-hexanol, 1-octanol) resulting in membranes with significantly differing morphologies. Subsequently, composite membranes were produced, with the support layer being a membrane with the largest pores, and the skin layer a membrane with smaller pores. The resulting membranes were tested for physicochemical and transport properties. The morphology of the membrane surfaces and their cross-sections were investigated by using a scanning electron microscope (SEM). The structure of the membranes, on the other hand, was investigated by FTIR spectroscopy and WAXS structural analysis.

4

Application of electrochemical impedance spectroscopy in analysis of SiO2 layer used for implants in bone surgery

Walke W., Hyla A., Marciniak J., Nowińska K.

Engineering of Biomaterials

|

2016

|

Vol. 19, no. 138 spec. iss.

113

5

Właściwości mechaniczne usieciowanego izocyjanianami produktu reakcji modyfikowanego oleju sojowego i żywicy epoksydowej

Czub P., Kasza P.

Polimery

|

2014

|

T. 59, nr 6

466--476

PL

W wyniku epoksydacji oleju sojowego, a następnie otwarcia, w reakcji z glikolem dietylenowym, powstałych pierścieni oksiranowych (schemat A), otrzymano pochodną hydroksylową oleju sojowego (SDEG). Uzyskaną pochodną wykorzystano w procesie stapiania (schemat B) z małocząsteczkową dianową żywicą epoksydową EPR 162, prowadzonym wobec trifenylofosfiny jako katalizatora. Zsyntezowane materiały scharakteryzowano metodami spektroskopii FT-IR (rys. 1) i 1H NMR (rys. 2), oznaczano zawartość wiązań nienasyconych, grup epoksydowych i hydroksylowych oraz średni ciężar cząsteczkowy i stopień polidyspersji (tabela 1 i 2, rys. 3). Hydroksylową pochodną oleju sojowego i produkt stapiania z żywicą epoksydową utwardzano przy użyciu poliizocyjanianów o różnej budowie [wzory (I)—(VI)]: 2,4-diizocyjanianu toluilenu, diizocyjanianu heksametylenu i 4,4'-diizocyjanianu difenylometanu. Zbadano wybrane właściwości mechaniczne (tabela 4) utwardzonych materiałów (tabela 3) oraz ich strukturę morfologiczną — metodą SEM (rys. 4). Stwierdzono, że produkt procesu stapiania po utwardzeniu ma jednorodną strukturę i charakteryzuje się lepszymi właściwościami mechanicznymi niż pochodna hydroksylowa utwardzona takimi samymi środkami sieciującymi. Obie grupy materiałów na bazie modyfikowanego oleju sojowego wykazują właściwości mechaniczne pośrednie między właściwościami żywicy epoksydowej EPR 162 utwardzonej izoforonodiaminą a żywicy EPR 162 utwardzonej bezwodnikiem metylotetrahydroftalowym.

EN

The hydroxyl derivative of soybean oil (SDEG) was obtained as a result of the epoxidation of soybean oil followed by the opening of oxirane rings in the reaction with diethylene glycol (Scheme A). This derivative was used in the process of fusion with bisphenol A-based low-molecular-weight epoxy resin EPR 162 (Scheme B), carried out using triphenylphosphine as a catalyst. The as-synthesized materials were characterized using FT-IR (Fig. 1) and 4H NMR (Fig. 2) spectroscopy and by determining the content of unsaturated bonds, epoxy and hydroxyl groups as well as the number and weight average molecular weights and polydispersity index (Table 1 and 2, Fig. 3). The hydroxyl derivative of soybean oil and the product of the fusion process were crosslinked using polyisocyanates of different structure [Formulae (I)—(VI)]: toluene-2,4-diisocyanate, hexamethylene diisocyanate and 4,4'-methylene diphenyl diisocyanate. The cured materials (Table 3) were characterized for selected mechanical properties (Table 4) and morphological structure using SEM method (Fig. 4). It has been found that the crosslinked product of the fusion process has a homogeneous structure and better mechanical properties than the hydroxyl derivative crosslinked using the same curing agents. Both groups of materials based on the modified soybean oil showed mechanical properties intermediate between those of epoxy resin EPR 162 crosslinked using isophoronediamine and the resin cured with methyltetrahydrophthalic anhydride.

6

Porównanie właściwości różnych rodzajów celulozy przed i po regeneracji z cieczy jonowych

Surma-Ślusarska B., Danielewicz D., Kaleta M.

Przegląd Papierniczy

|

2012

|

R. 68, nr 2

99-103

PL

Zbadano charakterystykę próbek celulozy zregenerowanej z cieczy jonowych i porównawczo celulozy wyjściowej oznaczając ich właściwości termiczne, stopień krystaliczności, stopień polimeryzacji oraz strukturę morfologiczną. Stwierdzono m.in., że celuloza regenerowana, w porównaniu z celulozą wyjściową, charakteryzuje się podobnymi właściwościami termicznymi, natomiast obniżonymi stopniami krystaliczności i polimeryzacji. Celuloza regenerowana odznacza się odmienną, bardziej jednorodną makro- i mikrostrukturą w porównaniu z wyjściową celulozą włóknistą.

EN

We analysed the characteristics of cellulose regenerated from ionic liquids and, comparatively, of original cellulose analysing their thermal properties, degree of crystallinity, degree of polymerisation and morphological structure. We found that the regenerated cellulose, in comparison to original cellulose, had similar thermal properties, but lower degrees of crystallinity and polymerisation. Regenerated cellulose had a different, more homogeneous macro- and microstructure in comparison to original fibrous cellulose.

7

Wpływ typu mięśnia na parametry widma mocy sygnału EMG

Bartuzi P., Roman-Liu D.

Aktualne Problemy Biomechaniki

|

2008

|

z. 2

7--12

PL

Celem pracy było opracowanie wskaźników, opartych na widmie mocy sygnału elektromiograficznego (EMG), obrazujących budowę morfologiczną mięśnia. Sygnał EMG został zarejestrowany z mięśni: czworoboczny część zstępująca (trapezius pars descendens-TPD), naramienny część obojczykowa (deltoideus pars clavicularis-DPC), naramienny część barkowa (deltoideus pars acromialis-DPA) oraz zginacz łokciowy nadgarstka (flexor carpi ulnaris-FCU), podczas badań w 6 wariantach obciążenia. W wyniku analizy opracowano parametry widma mocy sygnału EMG, szczególnie wrażliwe na zmiany w strukturze mięśnia.

EN

The aim of this study was to develop coefficients of electromyographic (EMG) signal, which show the morphological properties of muscle. Measurements of EMG signal from muscles: trapezius pars descendens (TPD), deltoideus pars clavicularis (DPC), deltoideus pars acromialis (DPA) and flexor carpi ulnaris (FCU), during research in 6 variants of load were realized. As the result of analysis the parameters based on power spectrum of EMG signal were worked out. Differences between morphological structure of muscle can be described using these parameters.

8

Mieszaniny polimerowe PET/PE-LD i PET/PP z dodatkiem nowego kompatybilizatora

Janik J., Lenart S., Królikowski W., Penczek P.

Polimery

|

2004

|

T. 49, nr 6

432-441

PL

Zbadano właściwości mieszanin polimerowych PET z poliolefinami z udziałem nowego kompatybilizatora do tych układów, w postaci karboksylowanego wosku polietylenowego. Określono wpływ takiego dodatku na statyczne właściwości mechaniczne, termiczne i reologiczne oraz na strukturę mieszanin PET/PE-LD i PET/PP (40 % mas./ 60 % mas.) w porównaniu z analogicznymi cechami odpowiednich mieszanin z udziałem kompatybilizatorów handlowych typu "Kraton" (SEBS-g-MA) i "Polybond" (PP-g-MA). Różniące się składem kształtki mieszanin otrzymywano metodą wytłaczania, a do badań mechanicznych dodatkowo wtryskiwano odpowiednie kształtki (tabela 1). Wprowadzenie funkcjonalizowanego wosku PE do mieszaniny PET/PE-LD poprawia kompleksowo wszystkie oceniane właściwości mechaniczne, czyli wytrzymałość na zginanie i na rozciąganie, wydłużenie przy rozerwaniu, obydwa moduły sprężystości (przy zginaniu i przy rozciąganiu) oraz udarność. Z obserwacji mikroskopowych i na podstawie wyników badań DMTA wywnioskowano, że wosk działa jako dobry kompatybilizator tej mieszaniny, poprawiając wzajemną mieszalność jej składników. Wykazuje on duże powinowactwo zarówno do PE-LD, jak i do PET, tworzy z nimi bowiem układy jednorodne. Wpływ funkcjonalizowanego wosku PE w układzie PET/PP jest mniejszy i porównywalny z działaniem badanych kompatybilizatorów handlowych. Te dwa kompatybilizatory handlowe jako dodatki do mieszanin polimerowych PET/PE-LD i PET/PP na ogół korzystnie wpływają na wybrane właściwości mechaniczne, np. poprawiają udarność i wydłużenie przy zerwaniu, z jednoczesnym zmniejszeniem modułu sprężystości przy rozciąganiu. Obrazy struktur morfologicznych wykazały zbyt małe powinowactwo tych kompatybilizatorów do fazy PET (PP-g-MA i SEBS-g-MA tworzą z PET układy heterofazowe.

EN

Properties of PET blends with polyolefins with an addition of carboxylated polyethylene wax as a new compatibilizer for these systems were investigated. The effects of thes additive on static mechanical properties (Table 2 and 3), thermal properties (Table 4, Fig. 1 and 2) and rheological characteristics (Table 4) as well as on the structures of PET/PE-LD or PET/PP blends (40 wt. %/60 wt. %) were determined in comparison with similar blends with commercial compatibilizers such as Kraton (SEBS-g-MA) or Polybond (PP-g-MA) (Figs. 3-8 and 11). Samples of the blends varying in compositions were obtained by extrusion. Additionally, the fittings investigations suitable for of mechanical properties' were injection molded (Table 1). Addition of functionalized PE wax to PET/PE-LD blends improves simultaneously all the properties investigated, i.e. flexural strength, tensile strength, elongation at break, flexural modulus, tensile modulus and impact strength. It was stated from the microscopic observations and DMTA results that the wax acts as a good compatibilizer of the blends, improving compatibility of the components. Because of its significant affinity for both PE-LD and PET, the wax forms homogeneous systems with the components. The effect of PE wax on PET/PP system is less significant and is similar to those of investigated commercial compatibilizers. These two commercial compatibilizers, acting as additives to the polymeric PET/PE-LD or PET/PP blends, usually influence advantageously the selected mechanical properties, for instance they improve an impact strength and elongation at break with simultaneous decrease in tensile modulus. Images of morphological structures showed too little affinities of these compatibilizers for PET phase (PP-g-MA and SEBS-g-MA form heterogeneous systems with PET, Fig. 9 and 10).

9

Influence of Enzymatic Treatment on the Flax Fibre Morphological Structure, Physico - Chemical Properties and Metrological Parameters of Yarn

Lipp-Symonowicz B., Tańska B., Wołukanis A., Wrzosek H.

Fibres & Textiles in Eastern Europe

|

2004

|

Vol. 12, no. 1 (45)

61--65

EN

The effect of enzymatic treatment with cellulolytic and pectinolytic enzymes on the morphological structure and properties of flax fibre and yarn has been examined. The enzymatic treatment has been introduced as a factor assisting the efficiency of the bleaching process. Attention has principally been concentrated on the application of such bleaching technologies which eliminate the chlorine compounds, and at he same time secure obtaining metrological indices and aesthetic values of yarn and physico-chemical properties of the fibres at the required level.

PL

Zbadano wpływ obróbki enzymatycznej cellulolitycznymi i pektynolitycznymi preparatami enzymatycznymi na budową morfologiczną i właściwości włókien lnu. Obróbka enzymatyczna bytu wprowaczona jako czynnik podwyższający efektywność procesu bielenia. Główną uwagę skoncentrowano na zastosowaniu technologii bielenia z wyeliminowaniem związków chloru, przy założeniu uzyskania wskaźników metrologicznych i walorów estetycznych przędzy oraz właściwości fizyko-chemicznych włókien na wymaganym poziomie.

10

Wpływ składu oraz zjawiska inwersji fazowej w mieszaninach PET/PE-LD i PET/PP na ich właściwości mechaniczne i reologiczne oraz na strukturę morfologiczną

Janik J., Królikowski W.

Polimery

|

2002

|

T. 47, nr 4

250-255

PL

Zbadano wpływ składu (w pełnym zakresie) mieszanin PET/PE-LD i PET/PP na ich statyczne właściwości mechaniczne, właściwości reologiczne oraz na strukturę. Stwierdzono, że wytrzymałość na rozciąganie i zginanie, moduł sprężystości przy rozciąganiu i podczas zginania, wydłużenie względne przy zerwaniu oraz udarność bez karbu metodą Charpy zmieniają się skokowo wraz ze zmianą składu mieszanin. Skok ten następuje po przekroczeniu 40% mas. udziału PET w mieszaninie z PE-LD i 25% mas. w mieszaninie z PP. Lepkość obu typów mieszanin w stanie stopionym maleje - również skokowo - wraz ze wzrostem w nich zawartości PET. Skokowe zmiany właściwości zarówno mechanicznych, jak i Teologicznych omawianych układów są spowodowane występowaniem zjawiska inwersji fazowej, co potwierdzają także obrazy mikroskopowe SEM. W mieszaninach o przeważającym udziale poliolefin (90% mas. PE-LD) przełom matrycy wykazuje charakter ciągliwy i włóknisty, natomiast w przypadku dużej przewagi PET (95% mas.) staje się on kruchy.

EN

The effect of composition (in its full range) of PET/PE-LD and ET/PP mixes on their static mechanical properties, rheological roperties and structure was investigated. It was concluded hat tensile strength (sigma(M)) and flexural strength sigma(fM)), elasticity modulus (E-t) and flexural modulus (E-f), elongation at break (epsilon(B)) and Charpy notched impact trength (a(c)U) (Figs. 1-6) change abruptly with composition f the blends. Abrupt changes have been recorded upon exceeding 0% by weight content of PET in the PE-LD blend and 25% by eight in the PP mix. Melt viscosity of both blends drops - lso abruptly - with increase in PET content (Fig. 7). Abrupt hanges in mechanical and rheological properties of the nvestigated systems are caused by phase inversion, confirmed y SEM microscopic images (Figs. 10 and 11). In blends with ominating polyolefin content (90% by weight PE-LD) factures re ductile and fibrous (Fig. 8), whereas domination of PET 95% by weight) givers brittle fractures (Fig. 9).

11

Morphological structure of polyetherketone membranes for gas separation prepared by phase inversion

Brown P. J., Ying S., Yang J.

Autex Research Journal

|

2002

|

Vol. 2, no. 2

101--108

EN

There has been increasing worldwide interest in the field of technical textile materials. Within this context the use of membranes for industrial separation processes has developed, and they can now compete effectively with conventional processes in terms of energy and capital costs. Membranes for gas separation have developed significantly in the last twenty years; however, there is still a need for high-temperature and chemically resistant membranes that exhibit good selectivity and gas permeability. In spite of the developments in gas separation membranes, only a few types of hollow-fibre membranes are still commercially available. Our study examines the fundamental properties of polyetherketone (PEK, a thermally stable and chemically resistant polymer) membranes prepared using concentrated sulphuric acid (98% H2SO4) as a solvent and dilute sulphuric acid (30%-60% H2SO4) as a non-solvent. Other non-solvents included acetic acid, ethanol, methanol, glycerol, and water. The concentration of the polymer-casting solutions was between 15% and 20%. The membrane structure was examined using SEM, and the gas separation properties were measured using a lab-scale test rig. The results show that formation and control of membrane structure are complicated, and that many preparation parameters affect membrane morphology and performance. Polymer concentration is a particularly important parameter. At each individual polymer concentration, the precipitant plays a crucial role, and has a determining influence on membrane structure. Membranes cast using 30-40% glycerol and 50-60% H2SO4 or 70-90% acetic acid as precipitants possessed sponge-type structures, and as such have an acceptable permeation rate. However, membranes cast into water display finger-like structures even at a low coagulation temperature of 3?C, and also exhibit lower permeation rates. It has also been shown that precipitated structures of PEK membranes are highly dependent upon the heat of mixing of the solvent with non-solvent, and that a reduction in this heat of mixing leads to sponge-like structures that are preferential for gas separation membranes.