Wyniki wyszukiwania - BazTech

1

Mechanical and anticorrosion efficiency of organic coatings with polyaniline phosphate and polypyrrole phosphate modified pigments

Kalendová Andrėa, Kohl Miroslav

Ochrona przed Korozją

|

2020

|

nr 9

278--289

EN

This paper describes the results of a study of the anticorrosion efficiency of composite materials prepared by precipitating conductive polymer salts on the surface of synthesized pigment particles. Specifically, composite pigments with polyaniline phosphate and polypyrrole phosphate were prepared. The novelty consists in testing the anticorrosive properties of composite pigments based on tungsten and molybdate, which have been surface treated with salt conductive polymers. Strontium, zinc and ferric molybdates and tungstates were synthesized and described and then coated with the conductive polymer salts. Twelve composite material samples were prepared and described and paints containing them as pigments were formulated. A solvent-type epoxy-ester resin served as the binder. The volume concentrations of the composite materials in the paint were 1%, 5%, 10% and 15%. The paints were applied to steel panels and the anticorrosion efficiency of the composite pigments was measured in dependence on the conductive polymer salt type and pigment volume concentration. Paint samples containing a commercial zinc phosphate pigment were prepared as reference materials. The physico-mechanical properties of the paints were also measured: the paint films exhibited an outstanding mechanical resistance. The steel panels coated with the paints were subjected to accelerated cyclic corrosion tests, the results point to a very good anticorrosion efficiency of the organic coatings containing the composite particles examined.

PL

W pracy omówiono wyniki badań skuteczności antykorozyjnej materiałów kompozytowych wytworzonych przez wytrącanie soli polimerów przewodzących na powierzchni zsyntetyzowanych cząstek pigmentu. Sporządzono pigmenty kompozytowe z fosforanem polianiliny i fosforanem polipirolu. Nowość polega na przebadaniu antykorozyjnych właściwości pigmentów kompozytowych na bazie wolframu i molibdenianu, które zostały poddane obróbce powierzchniowej solami polimerów przewodzących. Zsyntetyzowano molibdeniany i wolframiany strontu, cynku i żelaza, scharakteryzowano je, a następnie pokryto solami polimerów przewodzących. Sporządzono i scharakteryzowano dwanaście próbek materiałów kompozytowych i opracowano receptury farb zawierających je jako pigmenty. Jako spoiwo zastosowano rozpuszczalnikową żywicę epoksyestrową. Stężenia objętościowe materiałów kompozytowych w farbie wynosiły 1%, 5%, 10% i 15%. Farby nałożono na płytki stalowe i badano skuteczność antykorozyjną pigmentów kompozytowych w zależności od rodzaju soli polimeru przewodzącego i stężenia objętościowego pigmentu. Jako próbki odniesienia sporządzono farby zawierające handlowy fosforan cynku. Stalowe płytki pokryte farbami poddano przyspieszonym cyklicznym badaniom korozyjnym – wyniki wskazują na bardzo dobrą skuteczność antykorozyjną powłok organicznych zawierających badane pigmenty kompozytowe. Przebadano również właściwości fizyko-mechaniczne powłok i stwierdzono, że powłoki wykazywały wyjątkową odporność mechaniczną.

2

Bezchromowe powłoki konwersyjne na cynkowych podłożach stopowych - badania rozpoznawcze

Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2009

|

nr 4-5

174-176

PL

Otrzymano warstwy konwersyjne z roztworów soli molibdenu Na2MoO4 z dodatkiem cytrynianu sodu jako czynnika kompleksującego. Jako podłoża użyto stali węglowej St3s z elektrolitycznie osadzoną powłoką cynkowo-niklową. Badano wpływ pH oraz temperatury kąpieli na przebieg procesu i właściwości osadzonych powłok. Jako punkt odniesienia dla właściwości powstałych warstw użyto próbek chromianowanych. Badania polaryzacyjne wykazały, że wzrost temperatury kąpieli powoduje zmniejszenie odporności korozyjnej powłok w środowisku 0,5 M NaCl (wzrost prądów korozyjnych, spadek oporu polaryzacyjnego). Najlepsze warstwy zawierające molibden uzyskano w temperaturze 25 i 40°C. Powłoki są jednorodne i pozbawione spękań.

EN

Molybdate conversion layers have been obtained on the Zn-Ni alloy electrogalvanised steel from a solution containing sodium molybdate(VI) and sodium citrate, acidifi ed with phosphoric acid. The layers were deposited at different bath temperatures and different pH values. Chromated samples were used as the reference in order to compare the corrosion resistance properties. The increasing bath's temperature causes decreasing corrosion resistance (bigger corrosion curents, smaller polarization resistance) in 0,5 M NaCl environment. The best molybdate layers were obtained in temperature 25-40°C. These layers are homogeneous and free of cracks.

3

Warstwy molibdenianowe na powłokach stopowych Zn-Ni jako alternatywa warstw chromianowych

Winiarski J., Szczygieł B.

Ochrona przed Korozją

|

2008

|

nr 4-5

124-126

PL

Na podłożu ze stali węglowej St3s z elektrolityczną powłoką cynkowoniklową otrzymano warstwy konwersyjne z roztworów zawierających molibdenian sodu. Parametrami zmiennymi w procesie osadzania warstw konwersyjnych były: rodzaj kwasu nieorganicznego użytego do zakwaszania kąpieli, pH roztworu, temperatura kąpieli i czas zanurzania. Dla oceny właściwości korozyjnych stosowano porównawczo próbki chromianowane. Wykazano, że wzrost temperatury kąpieli do osadzania warstw molbdenianowych powoduje zmniejszenie odporności korozyjnej powłok w środowisku Na2SO4 (większe prądy korozyjne, mniejszy opór polaryzacji). Najlepsze, jednorodne i pozbawione spękań, warstwy zawierające molibden uzyskano w temperaturze 20°C.

EN

Molybdate conversion layers have been obtained on the Zn-Ni alloy electrogalvanised steel from a solution containing sodium molybdate (VI) acidified with phosphoric acid or nitric acid. The layers were deposited at different bath temperatures and different kind of inorganic acids. Chromated samples were used as the reference in order to compare the corrosion resistance properties. Increasing bath's temperature decreases corrosion resistance (bigger corrosion curents, smaller polarisation resistance) in Na2SO4 environment. The best molybdate layers were obtained in temperature T = 23°C. These layers are homogeneous and free of cracks.

4

Influence of corrosion inhibitors on the electrochemical behavior of adi in aqueous environments: local and macro-scopic approaches

Krawiec H.

Advances in Materials Science

|

2007

|

Vol. 7, nr 2(12)

210-215

EN

The corrosion behavior of austempered ductile iron (ADI) in acidic environment bas been investigated at the microscaleby means of the electrochemical microcell technique, surface analysis methods and at the macroscale using the classical electrochemical techniques. Local electrochemical investigations have revealed that the matrix (ausferrite), far from spheres, under-goes anodic dissolution in IM NaClO4, pH=3 solution. The classical electrochemical measurements have exhibited that the corrosion inhibitors like molybdate binder the anodic dissolution of alloys. Surface observations combined with the local electrochemical analysis have shown that the corrosion of ADI first occurs in the close vicinity of same graphite spheres and then around oxide inclusions. The surface observations (SEM) with inhibitors have shown that the surface layer consists of iron oxide, molybdenum oxide is formed. These mixture of oxides binder the anodic dissolution of ADI.