Wettability and surface free energy of a radiation-modified polyethylene film

Żenkiewicz M.

Polimery

|

2005

|

T. 50, nr 5

365-370

EN

Effects of the electron radiation generated by a high-voltage linear accelerator on wettability and surface free energy (SFE) of low-density polyethylene (PE-LD) film were studied. Radiation doses of 25, 50, 100, 250, and 500 kGy were used. Water, glycerol, formamide, diiodomethane, and a-bromonaphthalene were applied as measuring liquids for contact angle measurements. The calculations of SFE were made by Owens-Wendt and van Oss-Chaudhury-Good methods, using the results of measurements of contact angle with various systems of the measuring liquids. Wettability tests were also performed. It was found that the contact angle decreased with the rising radiation dose for all the measuring liquids and the shapes of these dependences were similar. However, significant quantitative differences were observed. The largest changes in the contact angle were detected for the dose range of up to 50 kGy. SFE values when measured by different methods and various measuring liquids differed generally in the whole range of the doses applied. Therefore, the surface free energy cannot be accepted as an absolute measure of the thermodynamic state of the surface layer of radiation-modified PE-LD film. Its values can be compared with one another only when they were determined using the same method and the same measuring or standard liquids.

PL

Przedstawiono wyniki badań wpływu dawki promieniowania elektronowego na zwilżalność i swobodną energię powierzchniową (SFE) folii z polietylenu małej gęstości (PE-LD). Strumień elektronów generowano w wysokonapięciowym akceleratorze liniowym stosując dawki 25, 50, 100, 250 i 500 kGy. Jako ciecz do pomiarów kąta zwilżania zastosowano wodę, glicerynę, formamid, dijodometan i a-bromonaftalen (rys. 1, tabela 4), a do testu zwilżalności - standardowe dwu- i trójskładnikowe mieszaniny metanolu, glikolu etylenowego, formamidu i wody. SFE obliczano metodami Owensa-Wendta i van Ossa-Chaudhury'ego-Gooda (rys. 2-4, tabele 5-8). Stwierdzono, że wraz ze wzrostem dawki promieniowania maleje kąt zwilżania wszystkimi stosowanymi cieczami, przy czym przebiegi krzywych opisujących zmiany tego kąta są podobne w przypadku wszystkich zastosowanych cieczy, aczkolwiek występują między nimi istotne różnice ilościowe. Największy spadek kąta zwilżania zaobserwowano w zakresie dawek do 50 kGy. Natomiast wartości SFE wyznaczone z zastosowaniem różnych układów cieczy rosną monotonicznie wraz ze zwiększaniem dawki promieniowania. Stwierdzono jednak, że wartości te określone odmiennymi metodami różnią się w całym zakresie stosowanych dawek (rys. 4). Dlatego SFE nie może być przyjmowana jako bezwzględna miara stanu termodynamicznego warstwy wierzchniej folii PE-LD modyfikowanej radiacyjnie. Jej wartości mogą być porównywane jedynie wówczas, gdy są obliczane tą samą metodą i gdy podstawę tych obliczeń stanowią kąty zwilżania tymi samymi cieczami pomiarowymi.

2

Wpływ dawki promieniowania elektronowego na zwilżalność i swobodną energię powierzchniową folii poli(tereftalanu etylenu)

Żenkiewicz M.

Polimery

|

2004

|

T. 49, nr 2

94-100

PL

Przedstawiono wyniki badań wpływu dawki promieniowania elektronowego (dawki do 500 kGy) generowanego w liniowym akceleratorze wysokonapięciowym, na kąt zwilżania i swobodną energię powierzchniową folii PET. Jako ciecze pomiarowe zastosowano wodę, glicerynę, formamid, dijodometan i alfa-bromonaftalen oraz ich zestawy dwu- i trójskładnikowe, a obliczenia wykonano metodami Owensa-Wendta i van Ossa-Chaudhury'ego-Gooda, wykorzystując w tym celu wyniki pomiarów kąta zwilżania różnymi zestawami cieczy pomiarowych. Wykonano także testy zwilżalności badanych próbek. Stwierdzono, że przebiegi zmian kąta zwilżania, malejącego wraz ze wzrostem dawki promieniowania, są podobne w przypadku wszystkich zastosowanych cieczy pomiarowych z tym, że występują między nimi istotne różnice ilościowe. Największe zmiany wartości tego kąta zaobserwowano w zakresie dawek do 50 kGy. Wyniki badań swobodnej energii powierzchniowej wykonanych każdą z metod, a także tą samą metodą, ale na podstawie kąta zwilżania cieczami z poszczególnych zestawów pomiarowych, różnią się na ogół w całym zakresie stosowanych dawek. Dlatego swobodna energia powierzchniowa nie może być przyjmowana jako bezwzględna miara stanu termodynamicznego warstwy wierzchniej folii PET modyfikowanej radiacyjnie, a jej wartości można porównywać jedynie wówczas, gdy są one określone tą samą metodą i za pomocą tych samych cieczy pomiarowych lub wzorcowych.

EN

Results of investigation of the effect of electron radiation dose (up to 500 kGy), generated in linear high voltage accelerator, on the contact angle and surface free energy of poly(ethylene terephthalate) (PET) film were presented. Water, glycerin, formamide, diiodomethane, alpha-bromonaphthalene as well as their two- or three-component systems were used as measurement liquids. Calculations were done according to Owens-Wendt's or van Oss-Chaudhury-Good's methods, using the results of contact angle measurements. Tests of wettability of samples investigated have been also done. It was found that the courses of changes of contact angle, decreasing with an increase in radiation dose, were similar for all measurement liquids used although significant quantitative differences appeared (Fig. 1, Table 4). The largest changes of contact angle values were observed for radiation doses up to 50 kGy. Surface free energy results, obtained by each method or on the basis of the contact angle with liquids from particular measurements systems used in the same method, differed in general in the whole range of doses used (Figs. 2-6, Tables 5-8). For this reason surface free energy can not be treated as absolute measure of thermodynamic state of surface layer of radiation modified PET film. Its values can be compared only in the case when they are determined by the same method and with the same measurement liquids (or standard ones) using.

3

Wpływ dawki promieniowania elektronowego na zmiany swobodnej energii powierzchniowej folii polietylenowej

Czupryńska J., Żenkiewicz M.

Prace Naukowe Instytutu Technologii Organicznej i Tworzyw Sztucznych Politechniki Wrocławskiej. Konferencje

|

2003

|

Vol. 52, nr 25

228-231

PL

W niniejszym referacie przedstawiono wpływ dawki promieniowania elektronowego na wartość swobodnej energii powierzchniowej folii polietylenowej. Wartość tej energii obliczano z pomiarów kąta zwilżania różnymi cieczami pomiarowymi. Do obliczenia swobodnej energii powierzchniowej zastosowano metodę Owensa-Wendta i van Ossa-Gooda oraz ustalono ją za pomocą metody cieczy wzorcowych. Wykonano analizę porównawczą wyników uzyskanych za pomocą tych metod.

EN

The influence of the dose of the electron radiation over the free surface energy in polyethylene film has been presented in the following work. The value of this energy has been calculated from contactangle using various measuring liquids. To calculate surface free energy Owens-Wendt's and van Oss-Good's methods were used and it was determined with the help of testing liquids. The comparative analysis of the obtained results with the use of the above mentioned method was made.

4

Investigation of tensile properties and tear resistance of polypropylene film modified by irradiation

Żenkiewicz M.

Polimery

|

2003

|

T. 48, nr 1

66-68

EN

Results of investigation of rupture strength, ultimate elongation, and tear resistance of a flat polypropylene film oriented biaxially and modified with use of the electron radiation are presented. It was found that the rupture strength and ultimate elongation of the sample under study dropped to values several times lower when the radiation dose increased from 25 to 500 kGy. At the same time, tear resistance of the sample decreased very quickly, what disqualifies the film as a wrapping material.

PL

Przedstawiono wyniki badań zależności naprężenia zrywającego, wydłużenia względnego przy zerwaniu oraz wytrzymałości na rozdzieranie płaskiej folii polipropylenowej orientowanej dwukierunkowo (BOPP) i modyfikowanej radia-cyjnie strumieniem przyspieszonych elektronów od dawki promieniowania w przedziale 25-500 kGy. Stwierdzono znaczne pogorszenie wszystkich tych właściwości ze zwiększaniem dawki. Wyjątkowo szybko maleje wytrzymałość na rozdzieranie, co dyskwalifikuje badaną folię jako materiał opakowaniowy.

5

Wpływ wysoko energetycznego promieniowania elektronowego na zmianę właściwości niektórych polimerów

Czupryńska J.

Polimery

|

2002

|

T. 47, nr 1

8-14

PL

Opisano podstawowe reakcje radiacyjne zachodzące w polimerach pod wpływem napromieniania wiązką wysokoenergetycznych elektronów (NWWE). Wskazano na towarzyszące temu procesowi zmiany struktury materiału, przede wszystkim na sieciowanie i degradację. Szczegółowo przeanalizowano mechanizm reakcji chemicznych spowodowanych napromienianiem polietylenu, polipropylenu i poli(tereftalanu etylenu). Uwagę zwrócono zwłaszcza na przemiany radiacyjne, którym ulega warstwa wierzchnia polietylenu. Omówiono również możliwości regulowania właściwości mechanicznych tych polimerów pod wpływem promieniowania elektronowego.

EN

Fundamental radiation reactions induced in polymers by high-energy electron beam radiation are described. Structural modifications like crosslinking and degradation are indicated. The mechanism and the reactions occurring in PE, especially in PE upper layers, and in PP and PET are discussed in more detail. Possible radiation control of mechanical properties of polymers is discussed.

6

Wpływ strumienia wysokoenergetycznych elektronów na zwilżalność folii polietylenowej

Żenkiewicz M., Czupryńska J.

Prace Naukowe Instytutu Technologii Organicznej i Tworzyw Sztucznych Politechniki Wrocławskiej. Konferencje

|

2001

|

Vol. 50, nr 23

97-100

PL

W plietylenie pod wpływem promieniowania elektronowego zachodzą reakcje chemiczne prowadzące do utworzenia ugrupowań polarnych. Zbadano wpływ dawki w zakresie 0-600 kGy na kąt zwilżania folii PE wodą i dijodometanem.

EN

Basic radiation reactions occurring in the surface layer of a LDPE film under the influence of an electron beam are discussed. The results of measurements of the contact angle performed which use of water and diiodomethane are presented. There are observed the variations in the wettability of the LDPE film only in the range of doses up to 250 kGy.